GB563025A - Improvements in and relating to the surface treatment of zinc or cadmium or metals coated therewith - Google Patents

Improvements in and relating to the surface treatment of zinc or cadmium or metals coated therewith

Info

Publication number
GB563025A
GB563025A GB979/43A GB97943A GB563025A GB 563025 A GB563025 A GB 563025A GB 979/43 A GB979/43 A GB 979/43A GB 97943 A GB97943 A GB 97943A GB 563025 A GB563025 A GB 563025A
Authority
GB
United Kingdom
Prior art keywords
zinc
acid
grams
sulphuric
cadmium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB979/43A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ford Motor Co Ltd
Ford Motor Co
Original Assignee
Ford Motor Co Ltd
Ford Motor Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ford Motor Co Ltd, Ford Motor Co filed Critical Ford Motor Co Ltd
Publication of GB563025A publication Critical patent/GB563025A/en
Expired legal-status Critical Current

Abstract

563,025. Electrolysis. FORD MOTOR CO., Ltd. Jan. 19; 1943, No. 979. Convention date, June 2, 1942. Drawings to Specification. [Class 41] [Also in Group II] To produce high lustre durability and a surface capable of being painted on the surface of zinc or cadmium or metal coated therewith, the zinc &c. is immersed, e.g. for a period not exceeding 60 seconds, in a chromic acid bath which includes minute amounts of sulphuric and nitric acids, the ratio of the chromic acid to the combined amounts of the other acids being at least 100 to 1 and the nitric acid being present in an amount in excess of the sulphuric acid. A transparent enamel such as an alkyde resin mixed with a melamine resin and dissolved in petrolein naphtha, may be applied after the zinc &c. has been dipped in the acid. In an example, a bath comprises 120 grams of chromic acid, 0.25-0.50 grams of sulphuric acid and 0.8-1.20 grams of nitric acid all per litre of solution. A zinc coating for treatment as set out above, is electro-deposited from a bath containing 8 ozs. per gallon of zinc cyanide, 4'of sodium cyanide and 7 of caustic soda with anodes formed by remelting scrap die castings.
GB979/43A 1942-06-02 1943-01-19 Improvements in and relating to the surface treatment of zinc or cadmium or metals coated therewith Expired GB563025A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US563025XA 1942-06-02 1942-06-02

Publications (1)

Publication Number Publication Date
GB563025A true GB563025A (en) 1944-07-26

Family

ID=22003505

Family Applications (1)

Application Number Title Priority Date Filing Date
GB979/43A Expired GB563025A (en) 1942-06-02 1943-01-19 Improvements in and relating to the surface treatment of zinc or cadmium or metals coated therewith

Country Status (1)

Country Link
GB (1) GB563025A (en)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE1084103B (en) * 1953-03-13 1960-06-23 Armco Int Corp Process for the production of corrosion-resistant, unpainted and shiny metal zinc or aluminum surfaces

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE1084103B (en) * 1953-03-13 1960-06-23 Armco Int Corp Process for the production of corrosion-resistant, unpainted and shiny metal zinc or aluminum surfaces

Similar Documents

Publication Publication Date Title
US2142564A (en) Process for electrodeposition on aluminum and aluminum alloys
US2559878A (en) Zinc and cadmium passivating bath
GB493485A (en) Process for the electrolytic production of metal coatings on objects with a non-conducting surface
GB394637A (en) Method of producing galvanic deposits on aluminium and its alloys
US2654701A (en) Plating aluminum
GB1451145A (en) Corrosion-resistant metal coatings
GB500113A (en) Improvements in processes for nickel-plating of aluminium and its alloys
GB534471A (en) Improvements in or relating to the production of protective coatings on magnesium and magnesium alloys
US2548419A (en) Method for production of lustrous zinc
GB390110A (en) Improvements in or relating to the production of corrosion-resisting coatings on aluminium or aluminium alloys
GB563025A (en) Improvements in and relating to the surface treatment of zinc or cadmium or metals coated therewith
GB1051665A (en)
GB522571A (en) Electrolytic production of protective coatings on aluminium
GB440608A (en) Process for producing galvanic coatings on aluminium and its alloys
GB593763A (en) Improvements in or relating to processes for covering the surfaces of aluminium or aluminium alloy articles with adherent and protective metallic coatings
GB1186729A (en) Electroplating Chromium onto Continuous Metal Strip
GB718573A (en) Process for the deposition of gold or gold alloys by electroplating and bath for carrying out said process
GB672367A (en) Improvements in or relating to the production of phosphate coatings on metals
GB395390A (en) Improvements in and relating to the electrolytic treatment of aluminium or its alloys
GB421696A (en) Anodic coating of zinc base metals
GB1307452A (en) Aqueous solutions for use in the treatment of base metal substrates
GB535199A (en) Improvements in or relating to the production of transparent oxide coatings on aluminium or aluminium alloys
GB436042A (en) Improvements relating to the electro-deposition of metals
GB514184A (en) Treatment of electro-deposited zinc coatings
US3607683A (en) Brass plating bath and brightener composition therefor