CN105603639B - Micro nanometer fiber eider down blending cotton and preparation method thereof - Google Patents
Micro nanometer fiber eider down blending cotton and preparation method thereof Download PDFInfo
- Publication number
- CN105603639B CN105603639B CN201610156870.7A CN201610156870A CN105603639B CN 105603639 B CN105603639 B CN 105603639B CN 201610156870 A CN201610156870 A CN 201610156870A CN 105603639 B CN105603639 B CN 105603639B
- Authority
- CN
- China
- Prior art keywords
- eider down
- parts
- melt
- blending cotton
- micro nanometer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Present invention firstly provides a kind of micro nanometer fiber eider down blending cotton, it is made up of the raw material of following parts by weight：15~20 parts of eider down, 8~12 parts of polypropylene nano fiber, 4~6 parts of polyurethane micrometer fibers.The present invention also provides a kind of preparation method of above-mentioned micro nanometer fiber eider down blending cotton, including the step of pretreatment and electrostatic spinning of eider down.Blending cotton pyroconductivity prepared by the present invention has reached 0.029W/mK, and proportion only has 0.028, not only merrily and lightheartedly, moistureproof, waterproof, and can be efficiently long-term prevention acarid parasitism and breeding, the machine washing of repetition, wash or dry-cleaned all without deformation, also do not interfere with its thermal property.In a word blending cotton of the invention and it is low temperature resistant, flexibility is good, adhesive force is strong, intensity is high the advantages that and one, going mouldy for effectively can preventing for a long time damage by worms, also there is corresponding product obvious antibacterial, deodorization to act on, it is and nontoxic, production cost is relatively low, and warmth retention property is strong, has a extensive future.
Description
Technical field
The present invention relates to material blending technology field, particularly a kind of micro nanometer fiber eider down blending cotton.
Background technology
Eider down is to grow the belly in geese and ducks, and lupine-like fine hair, slabbing is feather.Because eider down is a kind of
Animal protein fiber, the tiny stomata for ten million triangle that gathers on eider down nodular fibrous, can shrink with temperature Change
Expansion, produces temperature adjustment function, and absorbable human body distributes the hot gas of flowing, completely cuts off the invasion of cool ambient air.From the inspection of fluffy degree
Analyzed in survey, eider down than the heat insulating materials such as silk, cotton will a high grade, for example 450 degree of minimum standard fluffy
90 duck's downs are also more fluffy than silk and cotton good, so eider down is purely by way of a heat insulating material, its economic value is much high
In other heat insulating materials.Because eider down has the superperformance of this unique soft warming and moisture absorption diverging, eider down is determined
Good healthcare function, eider down are widely used in clothes, wadded a quilt with cotton, the field such as filler of weaving.
The pulled wool of eiderdown raw material is after the programs such as rough segmentation, ash disposal, essence point, packing are passed through, still containing a large amount of bacterial diseases
It the microorganisms such as poison, can't use directly as filler, also to be disinfected again by programs such as cleaning, dryings.Down feathers
Material removes the lipid on surface through over cleaning, eliminates stink, feather recovered pliability, become high resilience, then the place that carries out disinfection
Reason, packed after drying and be used as inserts.During sterilization, also the anti-mite processing of except mite is carried out to eider down, to kill eider down
While the acarid of upper attachment, finished product eider down is also set to be not easy to grow acarid again during use.Existing anti-mite processing side
One of formula is to add anti-mite agent during eider down cleans, so that anti-mite agent is attached on eider down, realizes anti-mite effect.
But eider down is different from cashmere, surface lacks sclay texture, and the surface relative smooth of eider down, the adhesion effect of anti-mite agent is simultaneously
It is bad.In addition, eider down can be such that anti-mite agent is impregnated into fiber also different from fiber textile, fiber textile, then will leaching
Long-term anti-mite effect is realized in the fibrage of stain into fabric, but down products does not have fabrication processes, and anti-mite agent is not
It can go deep into inside down products, it is difficult to realize long-term anti-mite effect.In the prior art, eider down processing is also contained more with soaking agent
The inorganic and organic chemical composition of kind, processing liquid making method is complicated, and certain problem of environmental pollution be present.
In addition to disadvantages described above, used in prior art also there is following defect in eider down：First, in order to ensure warming effect,
Down content is higher in eider down product, so that the use cost of eider down is too high；2nd, intensity is poor, washed to make plumage more
Suede crushes, conglomeration, reduces warmth retention property, influences attractive in appearance；3rd, existing eider down water proofing property is poor, so exploitation was a kind of both environmentally friendly, protects
Warm property the problem of strong high-strength waterproof eider down composite fibre turns into those skilled in the art's urgent need to resolve again.
The content of the invention
For overcome the deficiencies in the prior art, the invention provides a kind of micro nanometer fiber eider down blending cotton and its preparation side
Method, solves the problems such as higher existing eider down product cost, anti-mite property difference.
The technical solution adopted for the present invention to solve the technical problems is：
Present invention firstly provides a kind of micro nanometer fiber eider down blending cotton, it is made up of the raw material of following parts by weight：Eider down 15
~20 parts, 8~12 parts of polypropylene nano fiber, 4~6 parts of polyurethane micrometer fibers.
Preferably, the fibre diameter of the polypropylene nano fiber is 200~600nm, the polyurethane micrometer fibers
Fibre diameter is 0.8~1.2 μm.
Preferably, the polypropylene nano fiber includes the raw material of following parts by weight：30~40 parts of polypropylene, epoxy resin
3~5 parts, 1~1.5 part of acrylic acid, 3~5 parts of methyl methacrylate；The polyurethane micrometer fibers include following parts by weight
Raw material：10~20 parts of non-isocyanate polyurethane, 3~5 parts of epoxy acrylate, 1~1.5 part of titanium dioxide nanoparticle.
Preferably, the polypropylene nano fiber also contains 0.1~0.3 part of magnesium stearate.
The present invention a kind of preparation method of above-mentioned micro nanometer fiber eider down blending cotton is also provided, including carry out in order as
Lower step：
Step [1] takes the appropriate Radix Astragali, radix glycyrrhizae to add water to cook 1~2 hour, filtering, obtains filtrate A and filter residue A, filter residue A is dried
Nanoscale is crushed to by superfine grinding method after dry, obtains a nanometer filter residue powder；Appropriate wormwood, camellia and gingko are smashed to pieces
And soaked 10~12 hours in the water at 40~50 DEG C, filter to get filtrate B, last merging filtrate A, liquor B and nanometer filter residue
Powder, pretreatment fluid is obtained after stirring；
Step [2] puts into eider down in above-mentioned pretreatment fluid, is soaked 10~12 hours under stirring, pull out drying,
Eider down powder is obtained after ultra-fine grinding；
Step [3] adds epoxy resin and acrylic acid, stirring 15 into the polypropylene under the molten condition of corresponding parts by weight
~20min, then adds methyl methacrylate, and a certain amount of eider down powder is added after continuing stirring 10~15 minutes, stirring
30~40 minutes, finally obtain melt A；
Step [4] is by non-isocyanate polyurethane and epoxy acrylate melting mixing, while by a certain amount of eider down powder
End is well mixed with nano titanium dioxide powder, and obtained mixture is added in fused solution and is uniformly mixed, must be melted
Thing B；
Step [5] uses the melt shower nozzle being set up in parallel respectively to the melt A after fusing and melt B while carried out
Shoot out；
Electrostatic generator is provided with before the melt shower nozzle, to cause melt to take electrostatic after shooing out；
Step [6] is rapid by the melt A for shooing out out and melt B respectively by corresponding HTHP air nozzle
Stretching, is received to obtain the polypropylene nano fiber, the polyurethane micrometer fibers mixture that include eider down by reception device, that is, obtained
The micro nanometer fiber eider down blending cotton.
Preferably, the weight ratio between the Radix Astragali, radix glycyrrhizae, wormwood, camellia and gingko is 1: 2.5-3.5：3-6：2-
4:1-3；
Preferably, in the step 3 while methyl methacrylate is added, the stearic acid of corresponding parts by weight is added
Magnesium.
Preferably, high temperature when stretching melt A is 180~250 DEG C, and high pressure is 0.3MPa~0.4MPa；Stretching fusing
High temperature during thing B is 150~180 DEG C, and high pressure is 0.15MPa~0.2Mpa.
The positive effect of the present invention：The present invention obtains the micro-nano of high quality by the melting electrostatic spinning technology of uniqueness
Fibre down blending cotton, because the smooth hydrodynamics effect in the surface of the nanofiber and distinctive specific surface area can make
The loss of air pressur that be contacted with nanofiber is smaller reaches air permeable effect, and the presence of micrometer fibers ensure that blending cotton
Bulk strength, the blending cotton pyroconductivity for preparing of the present invention has reached 0.029W/mK, and proportion only has 0.028, not only merrily and lightheartedly,
Moistureproof, waterproof, and can be efficiently long-term prevention acarid parasitism and breeding, the machine washing repeated, washing or dry-cleaned all without
Deformation, does not interfere with its thermal property yet.In a word blending cotton of the invention and it is low temperature resistant, flexibility is good, adhesive force is strong, intensity is high
The advantages that and one, going mouldy for effectively can preventing for a long time damage by worms, corresponding product also have obvious antibacterial, deodorization act on, and
Nontoxic, production cost is relatively low, and warmth retention property is strong, has a extensive future.
Embodiment
Below to a preferred embodiment of the present invention will be described in detail.
The preferred embodiment of the present invention provides a kind of micro nanometer fiber eider down blending cotton, is made up of the raw material of following parts by weight：
18 parts of eider down, 10 parts of polypropylene nano fiber, 5 parts of polyurethane micrometer fibers.
The fibre diameter of the polypropylene nano fiber is 400~500nm, the fibre diameter of the polyurethane micrometer fibers
For 0.8~1 μm.
The polypropylene nano fiber includes the raw material of following parts by weight：35 parts of polypropylene, 4 parts of epoxy resin, acrylic acid 1
Part, 4 parts of methyl methacrylate；The polyurethane micrometer fibers include the raw material of following parts by weight：Non-isocyanate polyurethane
16 parts, 4 parts of epoxy acrylate, 1.5 parts of titanium dioxide nanoparticle.
The polypropylene nano fiber also contains 0.25 part of magnesium stearate.
The preparation method of above-mentioned micro nanometer fiber eider down blending cotton, including the following steps carried out in order：
Step [1] takes the appropriate Radix Astragali, radix glycyrrhizae to add water to cook 1~2 hour, filtering, obtains filtrate A and filter residue A, filter residue A is dried
Nanoscale is crushed to by superfine grinding method after dry, obtains a nanometer filter residue powder；Appropriate wormwood, camellia and gingko are smashed to pieces
And soaked 10~12 hours in the water at 40~50 DEG C, filter to get filtrate B, last merging filtrate A, liquor B and nanometer filter residue
Powder, pretreatment fluid is obtained after stirring；
Step [2] puts into eider down in above-mentioned pretreatment fluid, is soaked 10~12 hours under stirring, pull out drying,
Eider down powder is obtained after ultra-fine grinding；
Step [3] adds the epoxy resin and 1 parts by weight of 4 parts by weight into the polypropylene under the molten condition of 35 parts by weight
Acrylic acid, stir 15~20min, then add the methyl methacrylate of 4 parts by weight, taken after continuing stirring 10~15 minutes
The polypropylene miser of 10 parts by weight and the eider down powder for adding 12 parts by weight thereto, stir 30~40 minutes, must finally melt
Compound A；
Step [4] is by the non-isocyanate polyurethane of 16 parts by weight and the epoxy acrylate melting mixing of 4 parts by weight, together
When the eider down powder of 6 parts by weight is well mixed with 1.5 parts of nano titanium dioxide powder, obtained mixture is added to 5
It is uniformly mixed in the fused solution of parts by weight, obtains melt B；
Step [5] uses the melt shower nozzle being set up in parallel respectively to the melt A after fusing and melt B while carried out
Shoot out；
Electrostatic generator is provided with before the melt shower nozzle, to cause melt to take electrostatic after shooing out；
Step [6] is rapid by the melt A for shooing out out and melt B respectively by corresponding HTHP air nozzle
Stretching, is received to obtain the polypropylene nano fiber, the polyurethane micrometer fibers mixture that include eider down by reception device, that is, obtained
The micro nanometer fiber eider down blending cotton.
Weight ratio between the Radix Astragali, radix glycyrrhizae, wormwood, camellia and gingko is 1: 2.5-3.5：3-6：2-4:1-3；
In the step 3 while methyl methacrylate is added, the magnesium stearate of 0.25 parts by weight is added.
High temperature when stretching melt A is 220 DEG C, high pressure 0.4MPa；High temperature when stretching melt B is 160 DEG C, high
Press as 0.18Mpa.
Above-described is only the preferred embodiments of the present invention, should be understood that the explanation of above example is simply used
In help understand the present invention method and its core concept, the protection domain being not intended to limit the present invention, it is all the present invention
Any modification for being made within thought and principle, equivalent substitution etc., should be included in the scope of the protection.
Claims (4)
- A kind of 1. preparation method of micro nanometer fiber eider down blending cotton, it is characterised in thatThe micro nanometer fiber eider down blending cotton is made up of the raw material of following parts by weight：15~20 parts of eider down, polypropylene nano are fine 8~12 parts of dimension, 4~6 parts of polyurethane micrometer fibers；The fibre diameter of the polypropylene nano fiber is 200~600nm, and the fibre diameter of the polyurethane micrometer fibers is 0.8~1.2 μm；The polypropylene nano fiber includes the raw material of following parts by weight：30~40 parts of polypropylene, 3~5 parts of epoxy resin, propylene 1~1.5 part of acid, 3~5 parts of methyl methacrylate；The polyurethane micrometer fibers include the raw material of following parts by weight：Non- isocyanide 10~20 parts of acid esters polyurethane, 3~5 parts of epoxy acrylate, 1~1.5 part of titanium dioxide nanoparticle；The preparation method includes the following steps carried out in order：Step [1] takes the appropriate Radix Astragali, radix glycyrrhizae to add water to cook 1~2 hour, filtering, obtains filtrate A and filter residue A, after filter residue A is dried Nanoscale is crushed to by superfine grinding method, obtains a nanometer filter residue powder；By appropriate wormwood, camellia and gingko smash to pieces and Soaked 10~12 hours in water at 40~50 DEG C, filter to get filtrate B, last merging filtrate A, liquor B and nanometer filter residue powder, Pretreatment fluid is obtained after stirring；Step [2] puts into eider down in above-mentioned pretreatment fluid, is soaked 10~12 hours under stirring, pulls drying, ultra-fine out Eider down powder is obtained after crushing；Step [3] adds epoxy resin and acrylic acid into the polypropylene under the molten condition of corresponding parts by weight, and stirring 15~ 20min, methyl methacrylate is then added, a certain amount of eider down powder, stirring 30 are added after continuing stirring 10~15 minutes ~40 minutes, finally obtain melt A；Step [4] by non-isocyanate polyurethane and epoxy acrylate melting mixing, while by a certain amount of eider down powder with Nano titanium dioxide powder is well mixed, and obtained mixture is added in fused solution and is uniformly mixed, and obtains melt B；Step [5] uses the melt shower nozzle being set up in parallel respectively to the melt A after fusing and melt B while sprayed Tell；Electrostatic generator is provided with before the melt shower nozzle, to cause melt to take electrostatic after shooing out；Step [6] is respectively drawn rapidly the melt A for shooing out out and melt B by corresponding HTHP air nozzle Stretch, receive to obtain the polypropylene nano fiber, the polyurethane micrometer fibers mixture that include eider down by reception device, that is, obtain institute State micro nanometer fiber eider down blending cotton.
- A kind of 2. preparation method of micro nanometer fiber eider down blending cotton according to claim 1, it is characterised in that：The Huang Weight ratio between stilbene, radix glycyrrhizae, wormwood, camellia and gingko is 1:2.5-3.5:3-6:2-4:1-3.
- A kind of 3. preparation method of micro nanometer fiber eider down blending cotton according to claim 1, it is characterised in that：It is described poly- Also contain 0.1~0.3 part of magnesium stearate in propylene nanofiber raw material, methyl methacrylate is being added in the step [3] While, add the magnesium stearates of corresponding parts by weight.
- A kind of 4. preparation method of micro nanometer fiber eider down blending cotton according to claim 1, it is characterised in that：Stretching is molten High temperature during compound A is 180~250 DEG C, and high pressure is 0.3MPa~0.4MPa；High temperature when stretching melt B is 150~180 DEG C, high pressure is 0.15MPa~0.2Mpa.