CN109456729A - The water-based emulsion and preparation method thereof of fire-resistant isinglass belt silicone adhesive - Google Patents
The water-based emulsion and preparation method thereof of fire-resistant isinglass belt silicone adhesive Download PDFInfo
- Publication number
- CN109456729A CN109456729A CN201811184515.6A CN201811184515A CN109456729A CN 109456729 A CN109456729 A CN 109456729A CN 201811184515 A CN201811184515 A CN 201811184515A CN 109456729 A CN109456729 A CN 109456729A
- Authority
- CN
- China
- Prior art keywords
- water
- fire
- based emulsion
- isinglass belt
- silicone adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The water-based emulsion and preparation method thereof of fire-resistant isinglass belt silicone adhesive of the present invention, belong to organic pressure-sensitive gel technical field, first by MQ silicone resin and 107 glue with amino in toluene solvant, catalyst and KH550 is added, organic solvent toluene is steamed after 125 DEG C of back flow reaction 4h, cools down, add organic silicon solvent substitution toluene solvant, condensation polymer is dissolved, and stabilizer is added, deionized water is eventually adding and emulsifier for mixing is uniform.Products obtained therefrom viscosity of the present invention is small, permeability is preferable, it has no irritating odor, using mica tape prepared by the environment-friendly type fire-resistant isinglass belt silicone adhesive water-based emulsion, surface dry is not adhered, uniformly, it is indefectible, after the recycling removing of organic solvent toluene used in reacting, it can recycle, human and environment will not be endangered.
Description
Technical field
The invention belongs to organic pressure-sensitive gel technical fields, and in particular to a kind of water of fire-resistant isinglass belt silicone adhesive
Property lotion and preparation method thereof.
Background technique
Fire-resistant isinglass belt silicone adhesive is developed based on organic pressure-sensitive gel.Organic pressure-sensitive gel be by
The synthetic product of MQ silicone resin and hydroxy-terminated polysiloxane, it not only have good adhesion strength necessary to pressure sensitive adhesive and
Tack, there are many more unique performances, and the spy less than other pressure-sensitive adhesives is especially shown in terms of low temperature and high temperature
Property.Apply the silicone adhesive on fireproof mica band in addition to having the advantages of common pressure sensitive adhesive, it is also necessary to higher cohesion
Intensity, peel strength, viscosity and solid content and low tack are provided simultaneously with the characteristics of burning does not carbonize, Mica Tape Adhesive master
It to be primary raw material by MQ silicone resin and high-viscosity 107 glue, by the related process such as catalytic polymerization and adjustment raw material proportioning, with suitable
Answer different requirements.In conclusion fire-resistant isinglass belt silicone adhesive is synthesized on the Process ba- sis of organic pressure-sensitive gel
Quick-drying, high adhesion firmness silicone adhesive suitable for mica tape bonding.
Fire-resistant isinglass belt adhesive needs very low viscosity when in use, usually 70-100mpas, and common solvent has
Toluene, dimethylbenzene, dichlorotoleune, petroleum ether, cyclohexanone and its mixture.These solvent type fire-resistant isinglass belt silicone adhesives
Toluene or dimethylbenzene used in agent etc. is all the stronger diluent of toxicity, pollutes environment, can also bring when in use to human body
Injury.For the environmental issue for solving fire-resistant isinglass belt adhesive, Chinese patent CN201310188544.0 discloses a kind of environmental protection
Type high-temperature resistant silicone pressure-sensitive adhesive, component include 30-50 parts of organic silicon rubber, 50-70 parts of MQ organic siliconresin, are catalyzed
0.01-0.1 parts of agent, 60-70 parts of solvent, the solvent is the lipid of low molecular weight, not only transparent but also environment-protecting and non-poisonous, is used
Be all low molecular weight or more low-boiling solvent, it is poor to the dissolubility of organic pressure-sensitive gel, in adhesive tape production after gluing
The non-volatile gradient of solidification process volatilization, the pressure sensitive adhesive tape being made into are easy to produce surface blemish, and transparency is bad, and are easy residue glue.
Chinese patent CN106398636A uses the environmentally friendly solvents such as PMA, DBE, EGDA and acetate butyl, nontoxic to the human body, avoids ring
Border pollution, in addition, arranging in pairs or groups to form high low-boiling solvent combination by PMA, DBE, EGDA and butyl acetate, so as to organosilicon
The dissolubility of pressure sensitive adhesive is more preferable, and in adhesive tape production, gluing post cure processes solvent forms suitable volatilization gradient, manufactured Asia
Sensitive tape surface is more smooth, transparency.Both silicone adhesives above mainly directly use the rouge of low molecular weight
Class or part use the lipid of low molecular weight, to dissolve the silicone adhesive of macromolecule, although environment-protecting and non-poisonous, all
Certain stimulation taste, and it is not easy infiltration and quick-drying rapidly.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of environmental protection, good penetrability, quick-dry type after plastic band, viscosity is small,
The water-based emulsion and preparation method thereof of the fire-resistant isinglass belt silicone adhesive of non-stimulated nature and flavor.
To achieve the goals above, the technical solution adopted by the present invention are as follows:
The water-based emulsion of fire-resistant isinglass belt silicone adhesive of the present invention, the component including following weight fraction: methyl MQ
24 parts of silicone resin, 3-5 parts of 0.00005 part -0.2 part of 36 parts of 107 glue, catalyst, silane coupling agent, stabilizer 3- containing amino
5 parts, 40-60 parts of toluene, 10-20 parts of organic silicon solvent, 20-60 parts of deionized water and 1-5 parts of emulsifier.
The viscosity of 107 glue containing amino is ten thousand mPas of 50-100, and the amino molecule formula contained is as follows:
A=1500-2500, b=5-20, c=1500-2500.
The catalyst is tetramethylammonium hydroxide alkali glue, potassium hydroxide base glue, triethylamine, in diethylamine, ethylenediamine
One or more of combinations.
The organic silicon solvent is hexamethyldisiloxane, three cyclosiloxane, four cyclosiloxane, one in five cyclosiloxane
Kind or several combinations.
The isomerous tridecanol or isomerous tridecanol polyoxyethylene ether.
The silane coupling agent is KH550.
The stabilizer is isopropanol.
The preparation method of the water-based emulsion of fire-resistant isinglass belt silicone adhesive of the present invention, comprising the following steps:
1) MQ silicone resin and 107 glue containing amino are dissolved into respectively in toluene, after dissolution completely, reaction is then added
Continue to be mixed in container；
2) catalyst and silane coupling agent are added into reaction vessel, is warming up to 125 DEG C, back flow reaction 4h, the first steamed
Benzene can be with recycling and reusing；
3) it is cooled to room temperature, organic silicon solvent, stirring and dissolving are added into reaction vessel；
4) stabilizer, emulsifier and deionized water are added into reaction vessel, continues to stir evenly, obtains fire-resistant isinglass belt
The water-based emulsion of silicone adhesive.
Compared with prior art, the invention has the benefit that
(1) it can also be recycled after the organic solvent toluene recycling removing reacted, human and environment will not be endangered；
(2) hexamethyldisiloxane or the permeability of cyclosiloxane DMC are fabulous, and viscosity is small, with 107 glue and MQ silicone resin
Condensation polymer is similar to mix, therefore, obtained environment-friendly type fire-resistant isinglass belt silicone adhesive agent emulsion good penetrability；
(3) water is added, environment-friendly type fire-resistant isinglass belt silicone adhesive is made into water-based emulsion, very environmentally friendly, hydrone
It is smaller, further make lotion permeability good；
(4) the environment-friendly type fire-resistant isinglass belt silicone adhesive water-based emulsion viscosity prepared is small, has no irritating odor；
(5) in use, can be demulsified completely, lotion is very thin very close, and obtained fire-resistant isinglass belt is uniform, indefectible.
(6) it joined Silane coupling agent KH550, in use, 3% BPO is added, dried at 150 DEG C, obtained fire resisting
Mica tape is dry and comfortable, is not adhered.
Specific embodiment
Technical solution of the present invention is further elaborated below with reference to embodiment, but institute's protection scope of the present invention is not limited to
This.
Embodiment 1
The water-based emulsion of fire-resistant isinglass belt silicone adhesive of the present invention, including following components:
Methyl MQ silicone resin 24g；
The 107 glue 36g containing amino；
0.00005 part of tetramethylammonium hydroxide alkali glue；
Silane coupling agent KH550 1.8g；
Isopropanol 1.8g；
Organic solvent toluene 40g；
Organic silicon solvent 15g；
Deionized water 40g；
Isomerous tridecanol 3g.
The preparation method of the water-based emulsion of fire-resistant isinglass belt silicone adhesive of the present invention, comprising the following steps: by methyl
MQ silicone resin and 107 glue containing amino are dissolved into respectively in 20g toluene, after dissolution completely, are then added in flask and are continued to mix
Close stirring；After mixing evenly, KH550 and catalyst is added, is warming up to 125 DEG C, back flow reaction 4h, and steam most of toluene,
The toluene steamed can be with recycling and reusing；It cools at room temperature, 20g organic silicon solvent hexamethyldisiloxane is added, replace first
Benzene solvent is added stabilizer isopropanol, is eventually adding deionized water 40g, emulsifier isomerous tridecanol 3g is stirred evenly, glued
Spend smaller, the preferable environment-friendly type fire-resistant isinglass belt silicone adhesive water-based emulsion of permeability.
Embodiment 2
The water-based emulsion of fire-resistant isinglass belt silicone adhesive of the present invention, including following components:
Methyl MQ silicone resin 24g；
The 107 glue 36g containing amino；
0.2 part of tetramethylammonium hydroxide alkali glue；
Silane coupling agent KH550 1.8g；
Isopropanol 1.8g；
Organic solvent toluene 40g；
Organic silicon solvent DMC 10g；
Deionized water 40g
Isomerous tridecanol polyoxyethylene ether 5g
The preparation method of the water-based emulsion of fire-resistant isinglass belt silicone adhesive of the present invention, comprising the following steps: by methyl
MQ silicone resin and 107 glue containing amino are dissolved into respectively in 20g toluene, after dissolution completely, are then added in flask and are continued to mix
Close stirring.After mixing evenly, KH550 and catalyst is added, is warming up to 125 DEG C, back flow reaction 4h, and steam most of toluene,
The toluene steamed can be with recycling and reusing.It cools at room temperature, 10g organic silicon solvent DMC (three cyclosiloxane, Fourth Ring silicon is added
Oxygen alkane, the mixture of five cyclosiloxane, arbitrary proportion), toluene solvant is replaced, and stabilizer isopropanol is added, is eventually adding
Ionized water 40g, emulsifier isomerous tridecanol polyoxyethylene ether 5g are stirred evenly, and obtain that viscosity is smaller, the preferable ring of permeability
Guarantor's type fire-resistant isinglass belt silicone adhesive water-based emulsion.
Claims (8)
1. a kind of water-based emulsion of fire-resistant isinglass belt silicone adhesive, which is characterized in that the component including following weight fraction:
It is 24 parts of methyl MQ silicone resin, 3-5 parts of 0.00005 part -0.2 part of 36 parts of 107 glue, catalyst, silane coupling agent containing amino, steady
Determine 3-5 parts of agent, 40-60 parts of toluene, 10-20 parts of organic silicon solvent, 20-60 parts of deionized water and 1-5 parts of emulsifier.
2. the water-based emulsion of fire-resistant isinglass belt silicone adhesive according to claim 1, which is characterized in that contain amino
The viscosity of 107 glue be ten thousand mPas of 50-100, the amino molecule formula contained is as follows:
A=1500-2500, b=5-20, c=1500-2500.
3. the water-based emulsion of fire-resistant isinglass belt silicone adhesive according to claim 1, which is characterized in that the catalysis
Agent is tetramethylammonium hydroxide alkali glue, potassium hydroxide base glue, triethylamine, the combination of one or more of diethylamine, ethylenediamine.
4. the water-based emulsion of fire-resistant isinglass belt silicone adhesive according to claim 1, which is characterized in that described organic
Siloxane solvent is hexamethyldisiloxane, three cyclosiloxane, four cyclosiloxane, the combination of one or more of five cyclosiloxane.
5. the water-based emulsion of fire-resistant isinglass belt silicone adhesive according to claim 1, which is characterized in that the isomery
Tridecanol or isomerous tridecanol polyoxyethylene ether.
6. the water-based emulsion of fire-resistant isinglass belt silicone adhesive according to claim 1, which is characterized in that the silane
Coupling agent is KH550.
7. the water-based emulsion of fire-resistant isinglass belt silicone adhesive according to claim 1, which is characterized in that the stabilization
Agent is isopropanol.
8. a kind of preparation method of the water-based emulsion of fire-resistant isinglass belt silicone adhesive as claimed in claim 1,
Characterized by comprising the following steps:
1) MQ silicone resin and 107 glue containing amino are dissolved into respectively in toluene, after dissolution completely, reaction vessel is then added
In continue to be mixed；
2) catalyst and silane coupling agent are added into reaction vessel, is warming up to 125 DEG C, back flow reaction 4h, the toluene steamed can
With recycling and reusing；
3) it is cooled to room temperature, organic silicon solvent, stirring and dissolving are added into reaction vessel；
4) stabilizer, emulsifier and deionized water are added into reaction vessel, continues to stir evenly, it is organic to obtain fire-resistant isinglass belt
The water-based emulsion of silicon adhesive.