GB810491A - Oxidation resistant graphite articles - Google Patents

Oxidation resistant graphite articles

Info

Publication number
GB810491A
GB810491A GB373756A GB373756A GB810491A GB 810491 A GB810491 A GB 810491A GB 373756 A GB373756 A GB 373756A GB 373756 A GB373756 A GB 373756A GB 810491 A GB810491 A GB 810491A
Authority
GB
United Kingdom
Prior art keywords
phosphoric acid
blocks
per cent
colloidal silica
solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB373756A
Inventor
Joseph Charles Fisher Jr
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Union Carbide Corp
Original Assignee
Union Carbide Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Union Carbide Corp filed Critical Union Carbide Corp
Priority to GB373756A priority Critical patent/GB810491A/en
Publication of GB810491A publication Critical patent/GB810491A/en
Expired legal-status Critical Current

Abstract

A graphite article of increased strength and oxidation resistance is produced by impregnation with colloidal silica and phosphoric acid. The article may be first impregnated with an aqueous colloidal silica solution and dried, and then treated with an aqueous phosphoric acid solution and dried, the molar ratio of silica introduced to phosphoric acid introduced preferably being 1 to 0.2-3.7. Alternatively the article may be treated with a single aqueous solution containing colloidal silica and phosphoric acid in a molar ratio of 1 to 0.7-15 and at a pH of less than 6. In the example graphite blocks having a permeability of 70 millidarcys and a flexural strength of 2800 p.s.i. are impregnated with a 30 per cent colloidal silica solution at a pressure of 10 mm. of mercury, 4.8-6.6 per cent of silica being absorbed. The blocks are then dried at 100-150 DEG C. for 16-24 hours. The blocks are then impregnated at atmospheric pressure with 30 per cent phosphoric acid solution, 1-6 per cent of phosphoric acid being absorbed. The blocks are then heated at 150 DEG C. until dry. Two tables specifying oxidation loss and flexural strength, respectively, are given.
GB373756A 1956-02-07 1956-02-07 Oxidation resistant graphite articles Expired GB810491A (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
GB373756A GB810491A (en) 1956-02-07 1956-02-07 Oxidation resistant graphite articles

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
GB373756A GB810491A (en) 1956-02-07 1956-02-07 Oxidation resistant graphite articles

Publications (1)

Publication Number Publication Date
GB810491A true GB810491A (en) 1959-03-18

Family

ID=9764002

Family Applications (1)

Application Number Title Priority Date Filing Date
GB373756A Expired GB810491A (en) 1956-02-07 1956-02-07 Oxidation resistant graphite articles

Country Status (1)

Country Link
GB (1) GB810491A (en)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1997042135A1 (en) * 1996-05-02 1997-11-13 Alliedsignal Inc. Improved oxidation protection for carbon/carbon composites and graphites
US5962135A (en) * 1997-04-09 1999-10-05 Alliedsignal Inc. Carbon/carbon friction material
US6114006A (en) * 1997-10-09 2000-09-05 Alliedsignal Inc. High thermal conductivity carbon/carbon honeycomb structure

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1997042135A1 (en) * 1996-05-02 1997-11-13 Alliedsignal Inc. Improved oxidation protection for carbon/carbon composites and graphites
US5962135A (en) * 1997-04-09 1999-10-05 Alliedsignal Inc. Carbon/carbon friction material
US6114006A (en) * 1997-10-09 2000-09-05 Alliedsignal Inc. High thermal conductivity carbon/carbon honeycomb structure

Similar Documents

Publication Publication Date Title
ES474412A1 (en) Stabilizer for polysaccharides
GB1023134A (en) Improvements in ultra-violet absorbing filters
GB810491A (en) Oxidation resistant graphite articles
GB910302A (en) Myrcene derivatives
GB986503A (en) Stable, storable crystalline potassium sorbate and process for its manufacture
GB1003705A (en) Process for the after-treatment of phosphate coatings
ES8707492A1 (en) Process for producing aryldiazonium salts from nitrogenous gases rich in nitrogen oxide, aqueous solutions of these salts and their use for the preparation of aminoazoaromatic compounds.
GB968421A (en) Process of manufacturing 2,2-dimethyl-1,3-propanediol mono(hydroxypivalate)
GB2019192A (en) Dehydration of organic tissue
GB1491061A (en) Method of treating articles of sintered vitreous silica
GB730686A (en) Process for the manufacture of active carbon and active carbon obtained by this process
GB939905A (en) A process for preparing a penillic acid and salts thereof
GB802251A (en) Improvements in high strength single crystals of iron
GB834324A (en) Improvements in or relating to the preparation of ferrous sulphate suspensions
GB955628A (en) A process for increasing the thermal stability of silicon carbide
GB969356A (en) Dimensional stabilisation of paper
GB960246A (en) Process for the production of 2-nitro-4-fluobenzoic and 4-nitro-2-fluobenzoic acids
GB872286A (en) Production of corundum
SU129667A1 (en) Method for improving composition of carbon-free ferrochrome
GB987836A (en) Sparingly-soluble derivative of the kallikrein-inactivator
GB906109A (en) Process for the manufacture of pivalic acid
GB319854A (en) Improvements in the manufacture and production of magnetic cores of high permeability
GB889402A (en) Treatment of cellulosic fabrics and the fabrics thereby obtained
GB867549A (en) Production of 11-bromo-undecanoic acid
GB1002147A (en) Process for the manufacture of shaped articles of regenerated cellulose from viscose