JP2007284432A - Organometallic complex, and light emitting element, light emitting device and electronics using the complex - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide an organometallic complex capable of obtaining red light emission, to provide the complex having high luminous efficiency, and to provide the complex capable of obtaining red light emission and having high luminous efficiency. <P>SOLUTION: There is provided an organometallic complex having a structure represented by general formula (G1) (wherein A is a 6-25C aromatic hydrocarbon group; Z is H, 1-4C alkyl, 1-4C alkoxy or 6-25C aryl; A<SB>r</SB><SP>1</SP>is 6-25C aryl; R<SP>1</SP>is H, 1-4C alkyl or 1-4C alkoxy; and M is a central metal and either one of group 9 or 10 elements). <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

The present invention relates to an organometallic complex. In particular, the present invention relates to an organometallic complex that can convert a triplet excited state into light emission. The present invention also relates to a light-emitting element, a light-emitting device, and an electronic device using the organometallic complex.

An organic compound is excited by absorbing light. By passing through this excited state, various reactions (photochemical reactions) may occur or light emission (luminescence) may occur, and various applications have been made.

As an example of the photochemical reaction, there is a reaction (oxygen addition) of singlet oxygen with an unsaturated organic molecule (for example, see Non-Patent Document 1). Since oxygen molecules have a triplet ground state, singlet oxygen (singlet oxygen) is not generated by direct photoexcitation. However, singlet oxygen is generated in the presence of other triplet excited molecules, which can lead to an oxygen addition reaction. At this time, a compound that can be a triplet excited molecule is called a photosensitizer.

Thus, in order to generate singlet oxygen, a photosensitizer capable of becoming a triplet excited molecule by photoexcitation is necessary. However, since a normal organic compound has a singlet ground state, photoexcitation to the triplet excited state is a forbidden transition, and triplet excited molecules are hardly generated. Therefore, as such a photosensitizer, a compound that easily causes an intersystem crossing from a singlet excited state to a triplet excited state (or a compound that allows a forbidden transition to be directly photoexcited to a triplet excited state). Is required. In other words, such a compound can be used as a photosensitizer and is useful.

Also, such compounds often emit phosphorescence. Phosphorescence is light emission caused by transitions between energies of different multiplicity. In ordinary organic compounds, light emission occurs when returning from a triplet excited state to a singlet ground state (as opposed to singlet). Emission when returning from the excited state to the singlet ground state is called fluorescence). An application field of a compound capable of emitting phosphorescence, that is, a compound capable of converting a triplet excited state into light emission (hereinafter referred to as a phosphorescent compound) includes a light-emitting element using an organic compound as a light-emitting substance.

The structure of this light-emitting element is a simple structure in which a light-emitting layer containing an organic compound, which is a light-emitting substance, is provided between the electrodes. From the characteristics such as thin and light, high-speed response, and direct current low-voltage drive, It attracts attention as a flat panel display element. In addition, a display using this light-emitting element is characterized by excellent contrast and image quality and a wide viewing angle.

The light emitting mechanism of a light emitting element using an organic compound as a light emitting substance is a carrier injection type. That is, by applying a voltage with the light emitting layer sandwiched between the electrodes, electrons and holes injected from the electrodes are recombined and the light emitting substance becomes excited, and emits light when the excited state returns to the ground state. And as a kind of excited state, a singlet excited state (S ^* ) and a triplet excited state (T ^* ) are possible like the case of the optical excitation mentioned above. Further, the statistical generation ratio of the light emitting element is considered to be S ^* : T ^* = 1: 3.

A compound that converts a singlet excited state into light emission (hereinafter referred to as a fluorescent compound) does not emit light (phosphorescence) from the triplet excited state at room temperature, and only emits light (fluorescence) from the singlet excited state. Observed. Therefore, the theoretical limit of the internal quantum efficiency (ratio of photons generated with respect to injected carriers) in a light emitting device using a fluorescent compound is 25% on the basis that S ^* : T ^* = 1: 3. It is said that.

On the other hand, if the phosphorescent compound described above is used, the internal quantum efficiency can theoretically be as high as 75 to 100%. That is, the light emission efficiency is 3 to 4 times that of the fluorescent compound. For these reasons, in order to realize a highly efficient light-emitting element, a light-emitting element using a phosphorescent compound has been actively developed in recent years (see, for example, Non-Patent Document 2). In particular, as a phosphorescent compound, an organometallic complex having iridium or the like as a central metal attracts attention because of its high phosphorescent quantum yield.
Haruo Inoue, 3 others, Basic Chemistry Course Photochemistry I (Maruzen Co., Ltd.), 106-110 Zhang, Guo-Lin, 5 others, Gaoding Xuexiao Huaxue Xuebao (2004), vol. 25, no. 3, 397-400

Since the organometallic complex as disclosed in Non-Patent Document 2 is likely to cause intersystem crossing, it can be expected to be used as a photosensitizer. In addition, since light emission (phosphorescence) from a triplet excited state is likely to occur, a highly efficient light-emitting element is expected when applied to a light-emitting element. However, there are still few types of such organometallic complexes.

In addition, since the organometallic complex disclosed in Non-Patent Document 2 has an emission color of orange, when considering application to a full-color display or the like, the color purity as red is deteriorated, and from the viewpoint of color reproducibility. This is a disadvantageous element. Conversely, when the emission color is in the deep red region, that is, when the emission wavelength is extremely long, it is advantageous from the viewpoint of color reproducibility, but the luminous efficiency (cd / A) is lowered.

In view of the above, an object of the present invention is to provide an organometallic complex capable of obtaining red light emission. Another object is to provide an organometallic complex with high emission efficiency. It is another object of the present invention to provide an organometallic complex capable of obtaining red light emission with high luminous efficiency (unit: cd / A).

  Another object is to provide a light-emitting element with high emission efficiency. It is another object of the present invention to provide a light-emitting element that can emit red light with high luminous efficiency. It is another object to provide a light-emitting device and an electronic device with reduced power consumption.

As a result of intensive studies, the inventors of the present invention can form an organometallic complex by ortho-metalating a pyrazine derivative represented by the following general formula (G0) with respect to a group 9 or group 10 metal ion. I found. Further, the present inventors have found that the organometallic complex easily causes intersystem crossing and can efficiently emit phosphorescence. Furthermore, it discovered that the luminescent color of this organometallic complex exhibited favorable red.

（式中、Ａは炭素数６〜２５の芳香族炭化水素基を表す。また、Ｚは水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基、または炭素数６〜２５のアリール基のいずれかを表す。また、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。）

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms. Z represents hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, or 6 carbon atoms. and an aryl group 25. _{Further, a} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. also, ^{R 1} represents hydrogen or an alkyl group having 1 to 4 carbon atoms, or from 1 to carbon atoms, 4 represents an alkoxy group.)

Therefore, the structure of the present invention is an organometallic complex having a structure represented by the following general formula (G1).

（式中、Ａは炭素数６〜２５の芳香族炭化水素基を表す。また、Ｚは水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基、または炭素数６〜２５のアリール基のいずれかを表す。また、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。）

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms. Z represents hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, or 6 carbon atoms. and an aryl group 25. _{Further, a} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. also, ^{R 1} represents hydrogen or an alkyl group having 1 to 4 carbon atoms, or from 1 to carbon atoms, 4 represents an alkoxy group of 4. M is a central metal and represents a Group 9 element or a Group 10 element.)

In addition, when Z in the above general formula (G0) is an aryl group, the organometallic complex of the present invention has a structure represented by the following general formula (G2). Therefore, another structure of the present invention is an organometallic complex having a structure represented by the following general formula (G2).

（式中、Ａは炭素数６〜２５の芳香族炭化水素基を表す。また、Ａ_ｒ ^１およびＡ_ｒ ^２は炭素数６〜２５のアリール基を表す。また、Ｒ^１は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。）

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms, A _r ¹ and A _r ² represent an aryl group having 6 to 25 carbon atoms, and R ¹ represents hydrogen or carbon. It represents either an alkyl group having 1 to 4 or an alkoxy group having 1 to 4 carbon atoms, and M is a central metal and represents a Group 9 element or a Group 10 element.

In consideration of evaporation of the organometallic complex of the present invention for the purpose of sublimation purification and the like, in order to suppress an increase in evaporation temperature due to an increase in molecular weight, in the above general formula (G2), the aromatic hydrocarbon group A Is preferably a substituted or unsubstituted 1,2-phenylene group. In this case, ease of synthesis, A _r ² represents a substituted or unsubstituted phenyl group is preferable. Therefore, a more preferable structure of the present invention is an organometallic complex having a structure represented by the following general formula (G3).

（式中、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｒ^３〜Ｒ^１１はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基、または炭素数６〜１２のアリール基、またはハロゲン基、またはトリフルオロメチル基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。）

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} represents hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms R ^{3 to} R ¹¹ are each hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, an aryl group having 6 to 12 carbon atoms, a halogen group, or trifluoro (M represents a methyl group, and M represents a central metal and represents a Group 9 element or a Group 10 element.)

A more preferable structure is the case where the aromatic hydrocarbon group A is an unsubstituted phenylene group in the above general formula (G2). In this case, the ease of synthesis, A _r ² represents an unsubstituted phenyl group is preferred. Therefore, a more preferable structure of the present invention is an organometallic complex having a structure represented by the following general formula (G4).

（式中、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。）

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} represents hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms M is a central metal and represents a Group 9 element or a Group 10 element.)

Furthermore, in General Formula (G4), red light emission with high color purity and high luminous efficiency (unit: cd / A) can be obtained by replacing A _r ¹ with a substituted or unsubstituted phenyl group. be able to. Therefore, a more preferable structure of the present invention is an organometallic complex having a structure represented by the following general formula (G5).

（式中、Ｒ^１は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｒ^１２〜Ｒ^１６はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基、または炭素数６〜１２のアリール基、またはハロゲン基、またはトリフルオロメチル基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。）

(In the formula, R ¹ represents either hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms. Also, R ^{12 to} R ¹⁶ are each hydrogen or 1 carbon atom. Represents an alkyl group of ˜4, an alkoxy group of 1 to 4 carbon atoms, an aryl group of 6 to 12 carbon atoms, a halogen group, or a trifluoromethyl group, and M is a central metal, (Represents a Group 9 element or a Group 10 element.)

Note that in General Formula (G5), R ^{12 to} R ¹⁶ are preferably hydrogen, a fluoro group, or a trifluoromethyl group. With such a configuration, red light emission in the vicinity of the red chromaticity (that is, (x, y) = (0.67, 0.33)) defined by NTSC (National Television Standards Committee) is obtained. Can do.

Next, when Z in the above general formula (G0) is hydrogen, an alkyl group, or an alkoxy group, the organometallic complex of the present invention has a structure represented by the following general formula (G6). Therefore, another structure of the present invention is an organometallic complex having a structure represented by the following general formula (G6).

（式中、Ａは炭素数６〜２５の芳香族炭化水素基を表す。また、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１およびＲ^２はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。）

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms. _{Further, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} and ^{R 2} are hydrogen or, It represents either an alkyl group having 1 to 4 carbon atoms or an alkoxy group having 1 to 4 carbon atoms, and M is a central metal and represents a Group 9 element or a Group 10 element.

In consideration of evaporation of the organometallic complex of the present invention for the purpose of sublimation purification and the like, in order to suppress an increase in evaporation temperature due to an increase in molecular weight, in the above general formula (G6), an aromatic hydrocarbon group A Is preferably a substituted or unsubstituted 1,2-phenylene group. Therefore, a more preferable structure of the present invention is an organometallic complex having a structure represented by the following general formula (G7).

（式中、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１およびＲ^２はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｒ^３〜Ｒ^６はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基、または炭素数６〜１２のアリール基、またはハロゲン基、またはトリフルオロメチル基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。）

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} and ^{R 2} is hydrogen or an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, R ^{3 to} R ⁶ each represent hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, an aryl group having 6 to 12 carbon atoms, or a halogen atom Represents either a group or a trifluoromethyl group, and M is a central metal and represents a Group 9 element or a Group 10 element.)

A more preferable structure is the case where the aromatic hydrocarbon group A is an unsubstituted phenylene group in the above general formula (G6). Therefore, a more preferable structure of the present invention is an organometallic complex having a structure represented by the following general formula (G8).

（式中、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１およびＲ^２はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。）

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} and ^{R 2} is hydrogen or an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, M is a central metal and represents a Group 9 element or a Group 10 element.)

Further, in the general formula _(G8), by a substituted or unsubstituted phenyl group _A ^{r 1,} the color purity good, and luminous efficiency (Luminous Efficiency, Unit: cd / A) also obtained a high red light emission be able to. Therefore, a more preferable structure of the present invention is an organometallic complex having a structure represented by the following general formula (G9).

（式中、Ｒ^１およびＲ^２はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｒ^１２〜Ｒ^１６はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基、または炭素数６〜１２のアリール基、またはハロゲン基、またはトリフルオロメチル基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。）

(Wherein R ¹ and R ² each represent hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms. Also, R ^{12 to} R ¹⁶ are each hydrogen. Or an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, an aryl group having 6 to 12 carbon atoms, a halogen group, or a trifluoromethyl group, and M represents (It is a central metal and represents a Group 9 element or a Group 10 element.)

Note that in General Formula (G9), R ^{12 to} R ¹⁶ are preferably hydrogen, a fluoro group, or a trifluoromethyl group. With such a configuration, red light emission in the vicinity of the red chromaticity (that is, (x, y) = (0.67, 0.33)) defined by NTSC (National Television Standards Committee) is obtained. Can do.

In addition, when R ¹ in the pyrazine derivative represented by the above general formula (G0) is hydrogen or a methyl group, the pyrazine derivative has a small steric hindrance, so that it is easy to orthometalate to a metal ion, and the viewpoint of synthesis yield. Is preferable. Therefore, a preferable structure of the present invention is an organometallic complex in which R ¹ is hydrogen or a methyl group in the organometallic complex having the structure represented by the general formulas (G1) to (G9).

（式中、Ａは炭素数６〜２５の芳香族炭化水素基を表す。また、Ｚは水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基、または炭素数６〜２５のアリール基のいずれかを表す。また、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。また、Ｌはモノアニオン性の配位子を表す。また、前記中心金属が第９族元素の時はｎ＝２であり、第１０族元素の時はｎ＝１である。） Here, as the organometallic complex having the structure represented by the above general formula (G1), more specifically, an organometallic complex represented by the following general formula (G10) is preferable because synthesis is easy.

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms. Z represents hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, or 6 carbon atoms. and an aryl group 25. _{Further, a} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. also, ^{R 1} represents hydrogen or an alkyl group having 1 to 4 carbon atoms, or from 1 to carbon atoms, And M represents a central metal, a Group 9 element or a Group 10 element, L represents a monoanionic ligand, and the center. (When the metal is a Group 9 element, n = 2, and when the metal is a Group 10 element, n = 1.)

  As the organometallic complex having the structure represented by the above general formula (G2), more specifically, an organometallic complex represented by the following general formula (G11) is preferable because it can be easily synthesized.

（式中、Ａは炭素数６〜２５の芳香族炭化水素基を表す。また、Ａ_ｒ ^１およびＡ_ｒ ^２はそれぞれ、炭素数６〜２５のアリール基を表す。また、Ｒ^１は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。また、Ｌはモノアニオン性の配位子を表す。また、前記中心金属が第９族元素の時はｎ＝２であり、第１０族元素の時はｎ＝１である。）

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms. A _r ¹ and A _r ² each represents an aryl group having 6 to 25 carbon atoms. R ¹ represents hydrogen, Or an alkyl group having 1 to 4 carbon atoms or an alkoxy group having 1 to 4 carbon atoms, M is a central metal, and represents a Group 9 element or a Group 10 element. Represents a monoanionic ligand, and n = 2 when the central metal is a Group 9 element and n = 1 when the central metal is a Group 10 element.)

  As the organometallic complex having a structure represented by the above general formula (G3), more specifically, an organometallic complex represented by the following general formula (G12) is preferable because synthesis is easy.

（式中、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｒ^３〜Ｒ^１１はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基、または炭素数６〜１２のアリール基、またはハロゲン基、またはトリフルオロメチル基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。また、Ｌはモノアニオン性の配位子を表す。また、前記中心金属が第９族元素の時はｎ＝２であり、第１０族元素の時はｎ＝１である。）

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} represents hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms R ^{3 to} R ¹¹ are each hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, an aryl group having 6 to 12 carbon atoms, a halogen group, or trifluoro M represents a methyl group, M represents a central metal, a Group 9 element or a Group 10 element, L represents a monoanionic ligand, and the central metal represents (In the case of a Group 9 element, n = 2, and in the case of a Group 10 element, n = 1.)

  As the organometallic complex having the structure represented by the above general formula (G4), more specifically, an organometallic complex represented by the following general formula (G13) is preferable because synthesis is easy.

（式中、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。また、Ｌはモノアニオン性の配位子を表す。また、前記中心金属が第９族元素の時はｎ＝２であり、第１０族元素の時はｎ＝１である。）

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} represents hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms M is a central metal and represents a group 9 element or a group 10 element, L represents a monoanionic ligand, and when the central metal is a group 9 element, (n = 2 and n = 1 when a Group 10 element)

  As the organometallic complex having a structure represented by the above general formula (G5), more specifically, an organometallic complex represented by the following general formula (G14) is preferable because synthesis is easy.

（式中、Ｒ^１は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｒ^１２〜Ｒ^１６はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基、または炭素数６〜１２のアリール基、またはハロゲン基、またはトリフルオロメチル基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。また、Ｌはモノアニオン性の配位子を表す。また、前記中心金属が第９族元素の時はｎ＝２であり、第１０族元素の時はｎ＝１である。）

(In the formula, R ¹ represents either hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms. Also, R ^{12 to} R ¹⁶ are each hydrogen or 1 carbon atom. Represents an alkyl group of ˜4, an alkoxy group of 1 to 4 carbon atoms, an aryl group of 6 to 12 carbon atoms, a halogen group, or a trifluoromethyl group, and M is a central metal, Represents a Group 9 element or a Group 10 element, L represents a monoanionic ligand, and when the central metal is a Group 9 element, n = 2; In this case, n = 1.)

Note that in General Formula (G14), R ^{12 to} R ¹⁶ are preferably hydrogen, a fluoro group, or a trifluoromethyl group. With such a configuration, red light emission in the vicinity of the red chromaticity (that is, (x, y) = (0.67, 0.33)) defined by NTSC (National Television Standards Committee) is obtained. Can do.

  As the organometallic complex having a structure represented by the above general formula (G6), more specifically, an organometallic complex represented by the following general formula (G15) is preferable because synthesis is easy.

（式中、Ａは炭素数６〜２５の芳香族炭化水素基を表す。また、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１およびＲ^２はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。また、Ｌはモノアニオン性の配位子を表す。また、前記中心金属が第９族元素の時はｎ＝２であり、第１０族元素の時はｎ＝１である。）

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms. _{Further, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} and ^{R 2} are hydrogen or, It represents either an alkyl group having 1 to 4 carbon atoms or an alkoxy group having 1 to 4 carbon atoms, M is a central metal and represents a Group 9 element or a Group 10 element, and L is Represents a monoanionic ligand, and n = 2 when the central metal is a Group 9 element and n = 1 when the central metal is a Group 10 element.)

  As the organometallic complex having the structure represented by the above general formula (G7), more specifically, an organometallic complex represented by the following general formula (G16) is preferable because it can be easily synthesized.

（式中、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１およびＲ^２はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｒ^３〜Ｒ^６はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基、または炭素数６〜１２のアリール基、またはハロゲン基、またはトリフルオロメチル基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。また、Ｌはモノアニオン性の配位子を表す。また、前記中心金属が第９族元素の時はｎ＝２であり、第１０族元素の時はｎ＝１である。）

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} and ^{R 2} is hydrogen or an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, R ^{3 to} R ⁶ each represent hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, an aryl group having 6 to 12 carbon atoms, or a halogen atom Represents a group or a trifluoromethyl group, M represents a central metal, represents a Group 9 element or a Group 10 element, and L represents a monoanionic ligand. When the central metal is a Group 9 element, n = 2, and when the central metal is a Group 10 element, n = 1.)

  As the organometallic complex having a structure represented by the above general formula (G8), more specifically, an organometallic complex represented by the following general formula (G17) is preferable because synthesis is easy.

（式中、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１およびＲ^２はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。また、Ｌはモノアニオン性の配位子を表す。また、前記中心金属が第９族元素の時はｎ＝２であり、第１０族元素の時はｎ＝１である。）

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} and ^{R 2} is hydrogen or an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, M represents a central metal and represents a Group 9 element or a Group 10 element, L represents a monoanionic ligand, and the central metal represents a 9th element. (When a group element, n = 2, and when a group 10 element, n = 1.)

  As the organometallic complex having the structure represented by the above general formula (G9), more specifically, an organometallic complex represented by the following general formula (G18) is preferable because synthesis is easy.

（式中、Ｒ^１およびＲ^２はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｒ^１２〜Ｒ^１６はそれぞれ、水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基、または炭素数６〜１２のアリール基、またはハロゲン基、またはトリフルオロメチル基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、あるいは第１０族元素を表す。また、Ｌはモノアニオン性の配位子を表す。また、前記中心金属が第９族元素の時はｎ＝２であり、第１０族元素の時はｎ＝１である。）

(Wherein R ¹ and R ² each represent hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms. Also, R ^{12 to} R ¹⁶ are each hydrogen. Or an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, an aryl group having 6 to 12 carbon atoms, a halogen group, or a trifluoromethyl group, and M represents It is a central metal and represents a Group 9 element or a Group 10 element, L represents a monoanionic ligand, and n = 2 when the central metal is a Group 9 element. In the case of a Group 10 element, n = 1.)

Note that in General Formula (G18), R ^{12 to} R ¹⁶ are preferably hydrogen, a fluoro group, or a trifluoromethyl group. With such a configuration, red light emission in the vicinity of the red chromaticity (that is, (x, y) = (0.67, 0.33)) defined by NTSC (National Television Standards Committee) is obtained. Can do.

In addition, when R ¹ in the pyrazine derivative represented by the above general formula (G0) is hydrogen or a methyl group, the pyrazine derivative has a small steric hindrance, so that it is easy to orthometalate to a metal ion, and the viewpoint of synthesis yield Is preferable. Therefore, a preferable structure of the present invention is an organometallic complex in which R ¹ is hydrogen or a methyl group in the organometallic complexes represented by the general formulas (G10) to (G18) described above.

The monoanionic ligand L described above is a monoanionic bidentate chelate ligand having a beta diketone structure, a monoanionic bidentate chelate ligand having a carboxyl group, or a phenolic hydroxyl group. One of the monoanionic bidentate chelate ligands having a hydrogen atom and the monoanionic bidentate chelate ligand in which both of the two coordination elements are nitrogen is preferable because of high coordination ability. Particularly preferred are monoanionic ligands represented by the following structural formulas (L1) to (L8). These ligands are effective because they have high coordination ability and can be obtained at low cost.

  Further, in order to emit phosphorescence more efficiently, a heavy metal is preferable as the central metal from the viewpoint of the heavy atom effect. Therefore, the present invention is characterized in that the central metal M is iridium or platinum in the organometallic complex of the present invention described above. Especially, since the heat resistance of an organometallic complex improves by making the central metal M into iridium, iridium is particularly preferable as the central metal M.

  By the way, organometallic complexes having the structures represented by the above general formulas (G1) to (G9) (that is, including the organometallic complexes represented by the above general formulas (G10) to (G18)) are generally used. A coordination structure in which the pyrazine derivative represented by the formula (G0) is orthometalated to a metal ion greatly contributes to the function of phosphorescence emission. Therefore, another structure of the present invention is a light-emitting material containing an organometallic complex as described above.

  In addition, since the organometallic complex of the present invention can emit phosphorescence, that is, it can convert triplet excitation energy into light emission, it can be highly efficient when applied to a light-emitting element, and is very effective. Therefore, the present invention includes a light-emitting element using the organometallic complex of the present invention.

  At this time, the organometallic complex of the present invention is effective in terms of luminous efficiency when used as a luminescent substance. Therefore, the present invention is characterized by a light-emitting element using the organometallic complex of the present invention as a light-emitting substance. Preferably, a light-emitting element having a light-emitting layer between a pair of electrodes and having a structure in which the organometallic complex of the present invention is dispersed in a metal complex is preferable. Furthermore, the metal complex is preferably a zinc complex.

  In addition, since the light-emitting element of the present invention thus obtained can achieve high light emission efficiency, a light-emitting device (an image display device or a light-emitting device) using the light-emitting element as a light-emitting element can realize low power consumption. Therefore, the present invention includes light-emitting devices and electronic devices using the light-emitting element of the present invention.

  A light-emitting device of the present invention includes a layer containing a light-emitting substance between a pair of electrodes. It is characterized by having. Note that the light-emitting device in this specification includes an image display device or a light-emitting device using a light-emitting element. In addition, a module in which a connector such as an anisotropic conductive film or TAB (Tape Automated Bonding) tape or TCP (Tape Carrier Package) is attached to a light emitting element, a module in which a printed wiring board is provided on the end of a TAB tape or TCP, Alternatively, a module in which an IC (integrated circuit) is directly mounted on a light emitting element by a COG (Chip On Glass) method is included in the light emitting device. Furthermore, a light emitting device used for a lighting fixture or the like is also included.

  According to another aspect of the invention, there is provided an electronic apparatus including a display portion, the display portion including the above-described light emitting element and a control unit that controls light emission of the light emitting element.

  The organometallic complex of the present invention can emit red light. Further, the organometallic complex of the present invention is an organometallic complex having high emission efficiency. Moreover, red light emission with high luminous efficiency (Luminous efficiency, unit: cd / A) can be obtained.

  In addition, a light-emitting element with high emission efficiency can be obtained by manufacturing a light-emitting element using the organometallic complex of the present invention. Moreover, red light emission with high luminous efficiency can be obtained.

In addition, by using the organometallic complex of the present invention, a light-emitting device and an electronic device with reduced power consumption can be provided.

  Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings. However, the present invention is not limited to the following description, and it will be easily understood by those skilled in the art that modes and details can be variously changed without departing from the spirit and scope of the present invention. Therefore, the present invention should not be construed as being limited to the description of the embodiments below.

(Embodiment 1)
In Embodiment Mode 1, an organometallic complex of the present invention will be described.

<< Method for Synthesizing Pyrazine Derivative Represented by General Formula (G0) >>
In the present invention, the pyrazine derivative represented by the following general formula (G0) is orthometalated with respect to a group 9 or group 10 metal ion to form an organometallic complex.

（式中、Ａは炭素数６〜２５の芳香族炭化水素基を表す。また、Ｚは水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基、または炭素数６〜２５のアリール基のいずれかを表す。また、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。）

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms. Z represents hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, or 6 carbon atoms. and an aryl group 25. _{Further, a} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. also, ^{R 1} represents hydrogen or an alkyl group having 1 to 4 carbon atoms, or from 1 to carbon atoms, 4 represents an alkoxy group.)

Hereinafter, regarding the synthesis method of the pyrazine derivative represented by the general formula (G0), when Z in the general formula (G0) is an aryl group (the following general formula (G0-1)), Z is hydrogen or alkyl. In the case of a group or an alkoxy group (the following general formula (G0-2)), the description will be divided.

（式中、Ａは炭素数６〜２５の芳香族炭化水素基を表す。また、Ａ_ｒ ^１およびＡ_ｒ ^２は炭素数６〜２５のアリール基を表す。また、Ｒ^１は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。）

（式中、Ａは炭素数６〜２５の芳香族炭化水素基を表す。また、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１およびＲ^２は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。）

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms, A _r ¹ and A _r ² represent an aryl group having 6 to 25 carbon atoms, and R ¹ represents hydrogen or carbon. It represents either an alkyl group having 1 to 4 carbon atoms or an alkoxy group having 1 to 4 carbon atoms.)

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms. _{Further, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} and ^{R 2} are hydrogen or carbon atoms, It represents either an alkyl group having 1 to 4 or an alkoxy group having 1 to 4 carbon atoms.)

  First, the pyrazine derivative represented by the general formula (G0-1) can be synthesized by the following simple synthesis scheme. For example, as shown in the following scheme (a), it can be obtained by reacting a pyrazine derivative (A1) with an aryllithium or arylmagnesium bromide compound (A2). Alternatively, it can be obtained by reacting a pyrazine derivative (A1 ') with an aryllithium or arylmagnesium bromide compound (A2') as shown in the following scheme (a ').

On the other hand, the pyrazine derivative represented by the general formula (G0-2) can be synthesized by the following simple synthesis scheme. For example, as shown in the following scheme (a ″), it can be obtained by reacting a pyrazine derivative (A1 ″) with an aryllithium or arylmagnesium bromide compound (A2 ″). Alternatively, when A = A _r ¹ and R ¹ = R ² = H, the arene α-haloketone (the following structural formula (A3)) is treated with NH ₃ to perform self-condensation of the arene α-aminoketone. Can be obtained via. Note that in the structural formula (A3), X represents a halogen element.

Various types of the above-mentioned compounds (A1), (A2), (A1 ′), (A2 ′), (A1 ″), (A2 ″), and (A3) are commercially available or can be synthesized. Therefore, many types of pyrazine derivatives represented by the above general formula (G0) can be synthesized.

<< Method for Synthesizing Organometallic Complex of the Present Invention Having a Structure Represented by General Formula (G1) >>
Next, an organometallic complex of the present invention formed by orthometalation of a pyrazine derivative represented by the general formula (G0), that is, an organometallic complex having a structure represented by the following general formula (G1) will be described.

（式中、Ａは炭素数６〜２５の芳香族炭化水素基を表す。また、Ｚは水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基、または炭素数６〜２５のアリール基のいずれかを表す。また、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、または第１０族元素のいずれかを表す。）

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms. Z represents hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, or 6 carbon atoms. and an aryl group 25. _{Further, a} ^{r 1} represents a aryl group having 6 to 25 carbon atoms. also, ^{R 1} represents hydrogen or an alkyl group having 1 to 4 carbon atoms, or from 1 to carbon atoms, 4 represents an alkoxy group of 4. M is a central metal, and represents either a Group 9 element or a Group 10 element.)

  First, as shown in the following synthesis scheme (b), a pyrazine derivative represented by the general formula (G0) and a group 9 or group 10 metal compound containing a halogen (metal halide or metal complex) are mixed in an appropriate solvent. By heating in, the binuclear complex (B) which is 1 type of the organometallic complex of this invention which has a structure represented by general formula (G1) can be obtained. Examples of Group 9 or Group 10 metal compounds containing halogen include rhodium chloride hydrate, palladium chloride, iridium chloride hydrate, iridium chloride hydrate hydrochloride, potassium tetrachloroplatinate (II), and the like. However, it is not limited to these. In scheme (b), M represents a Group 9 or Group 10 element, and X represents a halogen element. When M is a Group 9 element, n = 2, and when M is a Group 10 element, n = 1.

Furthermore, as shown in the following synthesis scheme (c ′), the binuclear complex (B) and the pyrazine derivative represented by the general formula (G0) are heated at a high temperature of about 200 ° C. in a high boiling point solvent such as glycerol. Thus, a kind (C ′) of the organometallic complex of the present invention having a structure represented by the general formula (G1) can be obtained. In addition, as shown in the following synthesis scheme (c ″), a binuclear complex (B) and a compound that can be orthometalated such as phenylpyridine (more generally, a compound that can be cyclometalated), By heating at a high temperature of about 200 ° C. in a high boiling point solvent such as glycerol, a kind of organometallic complex of the present invention (C ″) having a structure represented by the general formula (G1) can be obtained. Note that in schemes (c ′) and (c ″), M represents a Group 9 element or Group 10 element, and X represents a halogen element. When M is a Group 9 element, n = 2, and when M is a Group 10 element, n = 1.

<< Method for Synthesizing Organometallic Complex of the Present Invention Represented by General Formula (G10) >>
Here, among the organometallic complexes having the structure represented by the general formula (G1) described above, an organometallic complex represented by the following general formula (G10) which is a preferred specific example will be described.

（式中、Ａは炭素数６〜２５の芳香族炭化水素基を表す。また、Ｚは水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基、または炭素数６〜２５のアリール基のいずれかを表す。また、Ａ_ｒ ^１は炭素数６〜２５のアリール基を表す。また、Ｒ^１は水素、または炭素数１〜４のアルキル基、または炭素数１〜４のアルコキシ基のいずれかを表す。また、Ｍは中心金属であり、第９族元素、または第１０族元素のいずれかを表す。また、Ｌはモノアニオン性の配位子を表す。また、前記中心金属が第９族元素の時はｎ＝２であり、第１０族元素の時はｎ＝１である。）

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms. Z represents hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, or 6 carbon atoms. and an aryl group 25. _{Further, a} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. also, ^{R 1} represents hydrogen or an alkyl group having 1 to 4 carbon atoms, or from 1 to carbon atoms, And M represents a central metal and represents either a Group 9 element or a Group 10 element, and L represents a monoanionic ligand. When the central metal is a Group 9 element, n = 2, and when the central metal is a Group 10 element, n = 1.)

  The organometallic complex of the present invention represented by the general formula (G10) can be synthesized by the following scheme (c). That is, by reacting the binuclear complex (B) obtained in the above-mentioned scheme (b) with HL which is a raw material of the monoanionic ligand L, protons of HL are desorbed and distributed to the central metal M. And the organometallic complex of the present invention represented by the general formula (G10) is obtained. In scheme (c), M represents a Group 9 element or Group 10 element, and X represents a halogen element. When M is a Group 9 element, n = 2, and when M is a Group 10 element, n = 1.

<< Specific Structural Formula of Organometallic Complex of the Present Invention Having the Structure Represented by General Formula (G1) and Organometallic Complex of the Present Invention Represented by General Formula (G10) >>
Next, a specific structural formula of the organometallic complex of the present invention having the structure represented by the general formula (G1) and the organometallic complex of the present invention represented by the general formula (G10) will be disclosed.

First, M as the central metal is selected from Group 9 elements and Group 10 elements, but iridium (III) and platinum (II) are preferred from the viewpoint of luminous efficiency. In particular, iridium (III) is suitable because it is thermally stable.

Next, in the following general formulas (G1) and (G10), the ligand portion P surrounded by a broken line will be described. Note that M represents either a Group 9 element or a Group 10 element as described above. L represents a monoanionic ligand (specific examples will be described later). When M is a Group 9 element, n = 2, and when M is a Group 10 element, n = 1.

Specific examples of the aromatic hydrocarbon group A include a substituted or unsubstituted 1,2-phenylene group, 1,2-naphthylene group, 2,3-naphthylene group, spirofluorene-2,3-diyl group, 9 9,9-Dialkylfluorene-2,3-diyl group such as 9,9-dimethylfluorene-2,3-diyl group can be applied. In particular, when the aromatic hydrocarbon group A is a substituted or unsubstituted 1,2-phenylene group, an increase in evaporation temperature due to an increase in molecular weight can be suppressed. It is effective when evaporating for the purpose. When the 1,2-phenylene group has a substituent, more specifically, as the substituent, an alkyl group such as a methyl group, an ethyl group, an isopropyl group, a tert-butyl group, a methoxy group, an ethoxy group, an iso Examples include an alkoxy group such as a propoxy group and a tert-butoxy group, an aryl group such as a phenyl group and a 4-biphenylyl group, a halogen group such as a fluoro group, and a trifluoromethyl group. Of the specific examples of the aromatic hydrocarbon group A, an unsubstituted 1,2-phenylene group is particularly preferable.

Specific examples of the substituent Z include 9 such as a substituted or unsubstituted phenyl group, 1-naphthyl group, 2-naphthyl group, spirofluoren-2-yl group, and 9,9-dimethylfluoren-2-yl group. Various aryl groups such as, 9-dialkylfluoren-2-yl group can be applied. In this case, in particular, when the substituent Z is a substituted or unsubstituted phenyl group, an increase in evaporation temperature due to an increase in molecular weight can be suppressed. Therefore, when the organometallic complex of the present invention is evaporated for the purpose of sublimation purification or the like. Is effective. When the phenyl group has a substituent, the substituent is more specifically an alkyl group such as a methyl group, an ethyl group, an isopropyl group or a tert-butyl group, a methoxy group, an ethoxy group, an isopropoxy group, a tert group. -An alkoxy group such as a butoxy group, an aryl group such as a phenyl group and a 4-biphenylyl group, a halogen group such as a fluoro group, and a trifluoromethyl group. In the case where the substituent Z is an aryl group, an unsubstituted phenyl group is particularly preferable among the specific examples. The substituent Z may be an alkyl group such as a methyl group, an ethyl group, an isopropyl group, or a tert-butyl group, or an alkoxy group such as a methoxy group, an ethoxy group, an isopropoxy group, or a tert-butoxy group. The substituent Z may be hydrogen.

Specific examples of the aryl group A _r ¹ include a substituted or unsubstituted phenyl group, 1-naphthyl group, 2-naphthyl group, spirofluoren-2-yl group, and 9,9-dimethylfluoren-2-yl group. A 9,9-dialkylfluoren-2-yl group or the like can be applied. In particular, when the aryl group A _r ¹ is a substituted or unsubstituted phenyl group, red light emission with high color purity and high luminous efficiency (unit: cd / A) can be obtained. When the phenyl group has a substituent, the substituent is more specifically an alkyl group such as a methyl group, an ethyl group, an isopropyl group or a tert-butyl group, a methoxy group, an ethoxy group, an isopropoxy group, a tert group. -An alkoxy group such as a butoxy group, an aryl group such as a phenyl group and a 4-biphenylyl group, a halogen group such as a fluoro group, and a trifluoromethyl group.

When the aromatic hydrocarbon group A is an unsubstituted 1,2-phenylene group, the aryl group A _r ¹ is an unsubstituted phenyl group, a phenyl group substituted with a fluoro group, or a trifluoromethyl group. By using a substituted phenyl group, red emission near the red chromaticity (ie, (x, y) = (0.67, 0.33)) defined by NTSC (National Television Standards Committee) is obtained. This is preferable.

Specific examples of the substituent R ¹ include alkyl groups such as methyl group, ethyl group, isopropyl group and tert-butyl group, and alkoxy groups such as methoxy group, ethoxy group, isopropoxy group and tert-butoxy group. However, when R ¹ is hydrogen or a methyl group, the steric hindrance of the ligand portion P becomes small, so that it is easy to orthometalate to a metal ion, which is preferable from the viewpoint of synthesis yield.

More specifically, any of the structures shown in the following ligand groups 1 to 9 can be applied as the structure of the ligand moiety P in the general formulas (G0) and (G10). However, the present invention is not limited to these. In the figure, α represents the position of carbon bonded to the central metal M. Β represents the position of nitrogen coordinated to the central metal M.

Next, the monoanionic ligand L in the general formula (G10) will be described. The monoanionic ligand L is a monoanionic bidentate chelate ligand having a beta diketone structure, a monoanionic bidentate chelate ligand having a carboxyl group, or a monoanion having a phenolic hydroxyl group Any of the bidentate bidentate chelate ligands or the monoanionic bidentate chelate ligands in which the two coordinating elements are both nitrogen are preferable. More specifically, monoanionic ligands represented by the following structural formulas (L1) to (L8) are exemplified, but the invention is not limited thereto.

  The organometallic complex of the present invention is constituted by appropriately combining the central metal M, the ligand groups 1 to 9 and the monoanionic ligand L as described above. Specific structural formulas of the organometallic complexes are listed (the following structural formulas (1) to (44)). However, the present invention is not limited to these.

  The organometallic complexes represented by the structural formulas (1) to (44) may have geometric isomers and stereoisomers depending on the type of ligand, but the organometallic complexes of the present invention include All of these isomers are also included.

  In addition, the organometallic complex represented by the structural formula (43) and the organometallic complex represented by the structural formula (44) have two geometric isomers, a facial isomer and a meridional isomer. Any isomers are included in the organometallic complex of the present invention.

The organometallic complex of the present invention described above can be used as a photosensitizer because intersystem crossing is possible. In addition, since it can emit phosphorescence, it can be used as a light-emitting material or a light-emitting substance of a light-emitting element.

(Embodiment 2)
In Embodiment Mode 2, a mode of a light-emitting element using the organometallic complex of the present invention described in Embodiment Mode 1 as a light-emitting substance will be described with reference to FIGS.

  FIG. 1 is a diagram illustrating a light-emitting element having a light-emitting layer 113 between a first electrode 101 and a second electrode 102. The light emitting layer 113 contains the organometallic complex of the present invention as described in Embodiment 1 above.

  By applying a voltage to such a light-emitting element, holes injected from the first electrode 101 side and electrons injected from the second electrode 102 side recombine in the light-emitting layer 113, and The organometallic complex of the present invention is brought into an excited state. Light is emitted when the organometallic complex in the excited state returns to the ground state. As described above, the organometallic complex of the present invention functions as a light-emitting substance of a light-emitting element. Note that in the light-emitting element of Embodiment 2, the first electrode 101 functions as an anode, and the second electrode 102 functions as a cathode.

  Here, the light emitting layer 113 contains the organometallic complex of the present invention. The structure of the light-emitting layer 113 is preferably a layer in which a substance having triplet excitation energy larger than that of the organometallic complex of the present invention is used as a host and the organometallic complex of the present invention is dispersed as a guest. This can prevent light emission from the organometallic complex of the present invention from being quenched due to concentration. The triplet excitation energy is an energy difference between the ground state and the triplet excited state.

There is no particular limitation on a substance used for dispersing the organometallic complex of the present invention (that is, a host), but 2,3-bis (4-diphenylaminophenyl) quinoxaline (abbreviation: TPAQn), 4,4′- In addition to compounds having an arylamine skeleton such as bis [N- (1-naphthyl) -N-phenylamino] biphenyl (abbreviation: NPB), 4,4′-di (N-carbazolyl) biphenyl (abbreviation: CBP) , Carbazole derivatives such as 4,4 ′, 4 ″ -tri (N-carbazolyl) triphenylamine (abbreviation: TCTA), bis [2- (2-hydroxyphenyl) pyridinato] zinc (abbreviation: Znpp ₂ ), Bis [2- (2-hydroxyphenyl) benzoxazolate] zinc (abbreviation: ZnBOX), bis (2-methyl-8-quinolinolato) (4-pheny A metal complex such as rufenolato) aluminum (abbreviation: BAlq) and tris (8-quinolinolato) aluminum (abbreviation: Alq ₃ ) is preferable. Alternatively, a high molecular compound such as poly (N-vinylcarbazole) (abbreviation: PVK) can be used. In particular, bis [2- (2-hydroxyphenyl) pyridinato] zinc (abbreviation: Znpp ₂ ), bis [2- (2-hydroxyphenyl) benzoxazolate] zinc (abbreviation: ZnBOX), bis (2-methyl- When a metal complex such as 8-quinolinolato) (4-phenylphenolato) aluminum (abbreviation: BAlq) is used, the organometallic complex of the present invention can emit light efficiently. More preferably, a zinc complex is used.

Note that since the organometallic complex of the present invention can emit red light, a light-emitting element that emits red light can be obtained. In addition, since the organometallic complex of the present invention has high emission efficiency, a light-emitting element with high emission efficiency can be obtained. Further, a light-emitting element that emits red light with high luminous efficiency (unit: cd / A) can be obtained.

  Further, since the light-emitting element of the present invention has high light emission efficiency, power consumption can be reduced.

  Although there is no particular limitation on the first electrode 101, it is preferable that the first electrode 101 be formed of a material having a high work function when functioning as an anode as in the second embodiment. Specifically, indium tin oxide (ITO), indium tin oxide containing silicon oxide (ITSO), indium oxide containing 2 to 20 wt% zinc oxide (IZO), gold (Au), platinum ( Pt), nickel (Ni), tungsten (W), chromium (Cr), molybdenum (Mo), iron (Fe), cobalt (Co), copper (Cu), palladium (Pd), or the like can be used. Note that the first electrode 101 can be formed using, for example, a sputtering method, an evaporation method, or the like.

  Although there is no particular limitation on the second electrode 102, it is preferable that the second electrode 102 be formed using a substance having a low work function when functioning as a cathode as in the second embodiment. Specifically, in addition to aluminum (Al) and indium (In), alkali metals such as lithium (Li) and cesium (Cs), alkaline earth metals such as magnesium (Mg) and calcium (Ca), erbium (Er Or rare earth metals such as ytterbium (Yb). An alloy such as an aluminum lithium alloy (AlLi) or a magnesium silver alloy (MgAg) can also be used. Note that the second electrode 102 can be formed by, for example, a sputtering method, an evaporation method, or the like.

  Note that in order to extract emitted light to the outside, one or both of the first electrode 101 and the second electrode 102 is an electrode made of a conductive film that transmits visible light such as ITO, or transmits visible light. It is preferable that the electrode is formed with a thickness of several to several tens of nm so as to be able to.

  Further, a hole transport layer 112 may be provided between the first electrode 101 and the light emitting layer 113 as shown in FIG. Here, the hole transport layer is a layer having a function of transporting holes injected from the first electrode 101 to the light-emitting layer 113. In this manner, by providing the hole-transport layer 112 and separating the first electrode 101 and the light-emitting layer 113, it is possible to prevent the light emission from being quenched due to the metal. However, the hole transport layer 112 is not always necessary.

  There is no particular limitation on a substance included in the hole-transport layer 112; typically, 4,4′-bis [N- (1-naphthyl) -N-phenylamino] biphenyl (abbreviation: NPB), 4, 4′-bis [N- (3-methylphenyl) -N-phenylamino] biphenyl (abbreviation: TPD), 4,4′-bis [N- (9,9-dimethylfluoren-2-yl) -N— Phenylamino] biphenyl (abbreviation: DFLDPBi), 4,4 ′, 4 ″ -tris (N, N-diphenylamino) triphenylamine (abbreviation: TDATA), 4,4 ′, 4 ″ -tris [N— An aromatic amine compound such as (3-methylphenyl) -N-phenylamino] triphenylamine (abbreviation: m-MTDATA) can be used. Alternatively, a high molecular compound such as poly (4-vinyltriphenylamine) (abbreviation: PVTPA) can be used.

  Note that the hole transport layer 112 may have a multilayer structure formed by stacking two or more layers. Further, two or more kinds of substances may be mixed and formed.

  Further, an electron transport layer 114 may be provided between the second electrode 102 and the light emitting layer 113 as shown in FIG. Here, the electron transporting layer is a layer having a function of transporting electrons injected from the second electrode 102 to the light emitting layer 113. In this manner, by providing the electron-transport layer 114 and separating the second electrode 102 and the light-emitting layer 113, it is possible to prevent the light emission from being quenched due to the metal. However, the electron transport layer 114 is not always necessary.

Although there is no particular limitation on a substance included in the electron-transport layer 114, typically, tris (8-quinolinolato) aluminum (abbreviation: Alq ₃ ), tris (4-methyl-8-quinolinolato) aluminum (abbreviation: Almq _3). ), Bis (10-hydroxybenzo [h] quinolinato) beryllium (abbreviation: BeBq ₂ ), bis (2-methyl-8-quinolinolato) (4-phenylphenolato) aluminum (abbreviation: BAlq), bis [2- ( 2-hydroxyphenyl) benzoxazolate] zinc (abbreviation: ZnBOX), bis [2- (2-hydroxyphenyl) benzothiazolate] zinc (abbreviation: Zn (BTZ) ₂ ), and the like. 2- (4-biphenylyl) -5- (4-tert-butylphenyl) -1,3,4-oxadiazole (abbreviation: PBD), 1,3-bis [5- (p-tert-butyl) Phenyl) -1,3,4-oxadiazol-2-yl] benzene (abbreviation: OXD-7), 3- (4-tert-butylphenyl) -4-phenyl-5- (4-biphenylyl) -1 , 2,4-triazole (abbreviation: TAZ), 3- (4-tert-butylphenyl) -4- (4-ethylphenyl) -5- (4-biphenylyl) -1,2,4-triazole (abbreviation: p-EtTAZ), bathophenanthroline (abbreviation: BPhen), bathocuproin (abbreviation: BCP), 4,4′-bis (5-methylbenzoxazol-2-yl) stilbene (abbreviation: BzOs), etc. Aromatic aromatic compounds can also be used. Alternatively, a high molecular compound such as poly (2,5-pyridine-diyl) (abbreviation: PPy) can be used.

  Note that the electron transport layer 114 may have a multilayer structure formed by stacking two or more layers. Further, two or more kinds of substances may be mixed and formed.

  Further, a hole injection layer 111 may be provided between the first electrode 101 and the hole transport layer 112 as shown in FIG. Here, the hole injection layer is a layer having a function of assisting injection of holes from the electrode functioning as an anode into the hole transport layer 112. However, the hole injection layer 111 is not always necessary.

Although there is no particular limitation on the substance constituting the hole injection layer 111, vanadium oxide (VOx), niobium oxide (NbOx), tantalum oxide (TaOx), chromium oxide (CrOx), molybdenum oxide (MoOx) Metal oxides such as tungsten oxide (WOx), manganese oxide (MnOx), rhenium oxide (ReOx), and ruthenium oxide (RuOx) can be used. Alternatively, a phthalocyanine compound such as phthalocyanine (abbreviation: H ₂ Pc) or copper phthalocyanine (CuPC) can be used. In addition, a substance constituting the hole transport layer 112 described above can be used. Alternatively, a high molecular compound such as a mixture of poly (ethylenedioxythiophene) and poly (styrenesulfonic acid) (abbreviation: PEDOT / PSS) can be used.

  Alternatively, a composite material obtained by mixing an organic compound and an electron acceptor may be used for the hole injection layer 111. Such a composite material is excellent in hole injecting property and hole transporting property because holes are generated in the organic compound by the electron acceptor. In this case, the organic compound is preferably a material excellent in transporting the generated holes, and specifically, for example, a substance (such as an aromatic amine compound) constituting the hole transport layer 112 described above is used. be able to. The electron acceptor may be any substance that exhibits an electron accepting property with respect to an organic compound. Specifically, it is preferably a transition metal oxide, for example, vanadium oxide (VOx), niobium oxide (NbOx), tantalum oxide (TaOx), chromium oxide (CrOx), molybdenum oxide (MoOx). ), Tungsten oxide (WOx), manganese oxide (MnOx), rhenium oxide (ReOx), ruthenium oxide (RuOx), and the like. A Lewis acid such as iron (III) chloride or aluminum (III) chloride can also be used. Alternatively, an organic compound such as 7,7,8,8-tetracyano-2,3,5,6-tetrafluoroquinodimethane (abbreviation: F4-TCNQ) can be used.

  Note that the hole injection layer 111 may have a multilayer structure in which two or more layers are stacked. Further, two or more kinds of substances may be mixed and formed.

  Further, an electron injection layer 115 may be provided between the second electrode 102 and the electron transport layer 114 as shown in FIG. Here, the electron injection layer is a layer having a function of assisting injection of electrons from the electrode functioning as a cathode to the electron transport layer 114. However, the electron injection layer 115 is not always necessary.

Although there is no particular limitation on the substance constituting the electron injection layer 115, an alkali metal compound such as lithium fluoride (LiF), cesium fluoride (CsF), calcium fluoride (CaF ₂ ), lithium oxide (LiOx), or Alkaline earth metal compounds can be used. Alternatively, a rare earth metal compound such as erbium fluoride (ErF ₃ ) can be used. In addition, a substance constituting the electron transport layer 114 described above can be used.

  Alternatively, a composite material obtained by mixing an organic compound and an electron donor may be used for the electron injection layer 115. Such a composite material is excellent in electron injecting property and electron transporting property because electrons are generated in the organic compound by the electron donor. In this case, the organic compound is preferably a material excellent in transporting the generated electrons. Specifically, for example, a substance (metal complex, heteroaromatic compound, or the like) constituting the electron transport layer 114 described above is used. Can be used. The electron donor may be any substance that exhibits an electron donating property to the organic compound. Specifically, alkali metals, alkaline earth metals, and rare earth metals are preferable, and lithium, cesium, magnesium, calcium, erbium, ytterbium, and the like can be given. Alkali metal oxides and alkaline earth metal oxides are preferable, and examples include lithium oxide (LiOx), calcium oxide (CaOx), and barium oxide (BaOx). A Lewis base such as magnesium oxide can also be used. Alternatively, an organic compound such as tetrathiafulvalene (abbreviation: TTF) can be used.

  In the light-emitting element of the present invention described above, the hole injection layer 111, the hole transport layer 112, the light-emitting layer 113, the electron transport layer 114, and the electron injection layer 115 are formed by an evaporation method, an inkjet method, or a coating method, respectively. Or any other method. The first electrode 101 or the second electrode 102 may be formed by any method such as a sputtering method, an evaporation method, an inkjet method, or a coating method.

(Embodiment 3)
The light emitting device of the present invention may have a plurality of light emitting layers. By providing a plurality of light emitting layers and emitting light from each of the light emitting layers, light emission in which a plurality of light emissions are mixed can be obtained. Thus, for example, white light can be obtained. In Embodiment Mode 3, an embodiment of a light-emitting element having a plurality of light-emitting layers will be described with reference to FIGS.

  In FIG. 2, a first light-emitting layer 213 and a second light-emitting layer 215 are provided between the first electrode 201 and the second electrode 202, and light emission from the first light-emitting layer 213 and the second light-emitting layer 213 are performed. Light emission in which light emission in the second light-emitting layer 215 is mixed can be obtained. A separation layer 214 is preferably provided between the first light-emitting layer 213 and the second light-emitting layer 215.

  When a voltage is applied so that the potential of the first electrode 201 is higher than the potential of the second electrode 202, a current flows between the first electrode 201 and the second electrode 202, and the first light emitting layer Holes and electrons recombine in 213, the second light-emitting layer 215, or the separation layer 214. The generated excitation energy is distributed to both the first light-emitting layer 213 and the second light-emitting layer 215, and is included in the first light-emitting substance and the second light-emitting layer 215 included in the first light-emitting layer 213. The second luminescent material is brought into an excited state. The first light-emitting substance and the second light-emitting substance that are in the excited state emit light when returning to the ground state.

The first light-emitting layer 213 includes perylene, 2,5,8,11-tetra (tert-butyl) perylene (abbreviation: TBP), 4,4′-bis (2,2-diphenylvinyl) biphenyl (abbreviation: DPVBi), 4,4′-bis [2- (N-ethylcarbazol-3-yl) vinyl] biphenyl (abbreviation: BCzVBi), bis (2-methyl-8-quinolinolato) (4-phenylphenolato) aluminum ( Abbreviations: BAlq), fluorescent compounds such as bis (2-methyl-8-quinolinolato) gallium chloride (Gamq ₂ Cl), bis {2- [3,5-bis (trifluoromethyl) phenyl] pyridinato-N, C ^{2 '}} iridium (III) picolinate _{(abbreviation: Ir (CF 3 ppy) 2} (pic)), bis [2- (4,6-difluorophenyl) pyridine DOO -N, C ^{2 ']} iridium (III) acetylacetonate (abbreviation: FIr (acac)), bis [2- (4,6-difluorophenyl) pyridinato -N, C ^2'] iridium (III) picolinate ( Abbreviation: FIrpic), represented by phosphorescent compounds such as bis [2- (4,6-difluorophenyl) pyridinato-N, C ^{2 ′} ] iridium (III) tetra (1-pyrazolyl) borate (abbreviation: FIr6) The first light-emitting substance is contained, and light emission having an emission spectrum peak at 450 to 510 nm (that is, blue to blue-green) is obtained. In addition, when the first light-emitting substance is a fluorescent compound, the first light-emitting layer 213 uses a substance having a singlet excitation energy higher than that of the first light-emitting substance as the first host. A layer in which a light-emitting substance is dispersed as a guest is preferable. In the case where the first light-emitting substance is a phosphorescent compound, a layer having a triplet excitation energy higher than that of the first light-emitting substance is used as the first host, and the first light-emitting substance is dispersed as a guest. It is preferable that As the first host, 9,10-di (2-naphthyl) anthracene (abbreviation: DNA), 2-tert-butyl-9,10-di (2) other than NPB, CBP, TCTA and the like described above. -Naphthyl) anthracene (abbreviation: t-BuDNA) or the like can be used. The singlet excitation energy is an energy difference between the ground state and the singlet excited state. The triplet excitation energy is an energy difference between the ground state and the triplet excited state.

On the other hand, the second light-emitting layer 215 contains the organometallic complex of the present invention and can emit red light. In addition, since the organometallic complex of the present invention exhibits high light emission efficiency, a light emitting element with high light emission efficiency can be obtained. In addition, a light-emitting element with reduced power consumption can be obtained.

  The structure of the second light-emitting layer 215 may be the same as that of the light-emitting layer 113 described in Embodiment 2.

Specifically, the separation layer 214 can be formed using the above-described TPAQn, NPB, CBP, TCTA, Znpp ₂ , ZnBOX, or the like. In this manner, by providing the separation layer 214, it is possible to prevent a problem that the light emission intensity of only one of the first light-emitting layer 213 and the second light-emitting layer 215 is increased. Note that the separation layer 214 is not necessarily provided and may be provided as appropriate in order to adjust the ratio between the light emission intensity of the first light-emitting layer 213 and the light emission intensity of the second light-emitting layer 215.

  Note that in Embodiment Mode 3, the organometallic complex of the present invention is used for the second light-emitting layer 215 and another light-emitting substance is applied to the first light-emitting layer. Another light-emitting substance may be applied to the second light-emitting layer 215 using the organometallic complex of the invention.

  In the third embodiment, a light emitting element provided with two light emitting layers as shown in FIG. 2 is described. However, the number of light emitting layers is not limited to two, for example, three. There may be. And what is necessary is just to mix the light emission from each light emitting layer. As a result, for example, white light is obtained.

  Note that the first electrode 201 may have a structure similar to that of the first electrode 101 described in Embodiment 2 above. The second electrode 202 may have a structure similar to that of the second electrode 102 described in Embodiment 2 above.

In the third embodiment, as shown in FIG. 2, the hole injection layer 211, the hole transport layer 212, the electron transport layer 216, and the electron injection layer 217 are provided. The structure of each layer described in Embodiment 2 may be applied. However, these layers are not necessarily required, and may be provided as appropriate depending on the characteristics of the element.

(Embodiment 4)
In the fourth embodiment, a light-emitting element in which a plurality of light-emitting layers are provided and light is emitted from each light-emitting layer with an element structure different from that in the third embodiment will be exemplified. Therefore, also in the fourth embodiment, light emission in which a plurality of light emissions are mixed can be obtained. That is, for example, white light can be obtained. Hereinafter, a description will be given with reference to FIG.

  In the light-emitting element in FIG. 3, a first light-emitting layer 313 and a second light-emitting layer 323 are provided between the first electrode 301 and the second electrode 302. Further, an N layer 315 and a P layer 321 are provided as charge generation layers between the first light emitting layer 313 and the second light emitting layer 323.

  The N layer 315 is a layer that generates electrons, and the P layer 321 is a layer that generates holes. When a voltage is applied so that the potential of the first electrode 301 is higher than the potential of the second electrode 302, the holes injected from the first electrode 301 and the electrons injected from the N layer 315 are The first light-emitting layer 313 recombines and the first light-emitting substance contained in the first light-emitting layer 313 emits light. Further, electrons injected from the second electrode 302 and holes injected from the P layer 321 are recombined in the second light-emitting layer 323, and the second light-emitting substance contained in the second light-emitting layer 323 is used. Emits light.

  The first light-emitting layer 313 may have a structure similar to that of the first light-emitting layer 213 in Embodiment 3, and light emission having an emission spectrum peak at 450 to 510 nm (that is, blue to blue green) is obtained. The second light-emitting layer 323 may have a structure similar to that of the second light-emitting layer 215 in Embodiment 3 and includes the organometallic complex of the present invention, so that red light emission can be obtained. Since the organometallic complex of the present invention exhibits high light emission efficiency, a light emitting element with high light emission efficiency can be obtained. In addition, a light-emitting element with reduced power consumption can be obtained.

  Since the N layer 315 is a layer that generates electrons, the N layer 315 may be formed using a composite material in which the organic compound described in Embodiment 2 and an electron donor are mixed. With such a structure, electrons can be injected into the first light-emitting layer 313 side.

  Since the P layer 321 is a layer that generates holes, the P layer 321 may be formed using a composite material obtained by mixing the organic compound described in Embodiment 2 and an electron acceptor. With such a structure, holes can be injected into the second light-emitting layer 323 side. The P layer 321 can also be made of a metal oxide having excellent hole injection properties such as MoOx, VOx, ITO, ITSO.

  Further, in Embodiment 4, a light emitting element provided with two light emitting layers as shown in FIG. 3 is described, but the number of light emitting layers is not limited to two. May be. And what is necessary is just to mix the light emission from each light emitting layer. As a result, for example, white light is obtained.

  Note that the first electrode 301 may have a structure similar to that of the first electrode 101 described in Embodiment 2 above. The second electrode 302 may have a structure similar to that of the second electrode 102 described in Embodiment 2 above.

In the fourth embodiment, as shown in FIG. 3, a hole injection layer 311, hole transport layers 312 and 322, electron transport layers 314 and 324, and an electron injection layer 325 are provided. Regarding the configuration, the configuration of each layer described in Embodiment 2 may be applied. However, these layers are not necessarily required, and may be provided as appropriate depending on the characteristics of the element.

(Embodiment 5)
In Embodiment Mode 5, an embodiment of a light-emitting element using the organometallic complex of the present invention as a sensitizer will be described with reference to FIGS.

  FIG. 1 shows a light-emitting element having a light-emitting layer 113 between the first electrode 101 and the second electrode 102. The light-emitting layer 113 includes the organometallic complex of the present invention as described in Embodiment 1 above and a fluorescent compound that can emit light having a longer wavelength than the organometallic complex of the present invention. It is.

  In such a light-emitting element, holes injected from the first electrode 101 and electrons injected from the second electrode 102 are recombined in the light-emitting layer 113, so that the fluorescent compound is excited. The excited fluorescent compound emits light when returning to the ground state. At this time, the organometallic complex of the present invention acts as a sensitizer for the fluorescent compound, and amplifies the number of molecules in the singlet excited state of the fluorescent compound. As described above, a light-emitting element with high emission efficiency can be obtained by using the organometallic complex of the present invention as a sensitizer. Note that in the light-emitting element of Embodiment 5, the first electrode 101 functions as an anode and the second electrode 102 functions as a cathode.

  The light-emitting layer 113 includes the organometallic complex of the present invention and a fluorescent compound that can emit light having a longer wavelength than the organometallic complex of the present invention. The constitution is such that a substance having a triplet excitation energy larger than that of the organometallic complex of the present invention and a singlet excitation energy larger than that of the fluorescent compound is used as a host. A layer in which a compound is dispersed as a guest is preferable.

There is no particular limitation on a substance (that is, a host) used for bringing the organometallic complex and the fluorescent compound of the present invention into a dispersed state, and the substances mentioned as the host in Embodiment 2 can be used.

  Further, the fluorescent compound is not particularly limited, but 4-dicyanomethylene-2-isopropyl-6- [2- (1,1,7,7-tetramethyljulolidin-9-yl) ethenyl] -4H- A compound exhibiting red to infrared light emission such as pyran (abbreviation: DCJTI), magnesium phthalocyanine, magnesium porphyrin, phthalocyanine and the like is preferable.

  Note that both the first electrode 101 and the second electrode 102 may have a structure similar to that of the first electrode and the second electrode described in Embodiment 2.

In the fifth embodiment, as shown in FIG. 1, the hole injection layer 111, the hole transport layer 112, the electron transport layer 114, and the electron injection layer 115 are provided. The structure of each layer described in Embodiment 2 may be applied. However, these layers are not necessarily required, and may be provided as appropriate depending on the characteristics of the element.

  The light-emitting element described above can emit light with high efficiency by using the organometallic complex of the present invention as a sensitizer.

(Embodiment 6)
In this embodiment, a light-emitting device manufactured using the organometallic complex of the present invention will be described.

  In this embodiment mode, a light-emitting device manufactured using the organometallic complex of the present invention will be described with reference to FIGS. 4A is a top view illustrating the light-emitting device, and FIG. 4B is a cross-sectional view taken along lines A-A ′ and B-B ′ in FIG. 4A. Reference numeral 601 indicated by a dotted line denotes a driving circuit portion (source side driving circuit), 602 denotes a pixel portion, and 603 denotes a driving circuit portion (gate side driving circuit). Reference numeral 604 denotes a sealing substrate, reference numeral 605 denotes a sealing material, and the inside surrounded by the sealing material 605 is a space 607.

  Note that the routing wiring 608 is a wiring for transmitting a signal input to the source side driving circuit 601 and the gate side driving circuit 603, and a video signal, a clock signal, an FPC (flexible printed circuit) 609 serving as an external input terminal, Receives start signal, reset signal, etc. Although only the FPC is shown here, a printed wiring board (PWB) may be attached to the FPC. The light-emitting device in this specification includes not only a light-emitting device body but also a state in which an FPC or a PWB is attached thereto.

  Next, a cross-sectional structure is described with reference to FIG. A driver circuit portion and a pixel portion are formed over the element substrate 610. Here, a source-side driver circuit 601 that is a driver circuit portion and one pixel in the pixel portion 602 are illustrated.

  Note that a CMOS circuit in which an n-channel TFT 623 and a p-channel TFT 624 are combined is formed in the source side driver circuit 601. The drive circuit may be formed of various CMOS circuits, PMOS circuits, or NMOS circuits. In this embodiment mode, a driver integrated type in which a driver circuit is formed over a substrate is shown; however, this is not necessarily required, and the driver circuit can be formed outside the substrate.

  The pixel portion 602 is formed by a plurality of pixels including a switching TFT 611, a current control TFT 612, and a first electrode 613 electrically connected to the drain thereof. Note that an insulator 614 is formed so as to cover an end portion of the first electrode 613. Here, a positive photosensitive acrylic resin film is used.

  In order to improve the coverage, a curved surface having a curvature is formed at the upper end or the lower end of the insulator 614. For example, when positive photosensitive acrylic is used as a material for the insulator 614, it is preferable that only the upper end portion of the insulator 614 has a curved surface with a curvature radius (0.2 μm to 3 μm). As the insulator 614, either a negative type that becomes insoluble in an etchant by light irradiation or a positive type that becomes soluble in an etchant by light irradiation can be used.

  Over the first electrode 613, a layer 616 containing a light-emitting substance and a second electrode 617 are formed. Here, as a material used for the first electrode 613 functioning as an anode, a material having a high work function is preferably used. For example, an ITO film or an indium tin oxide film containing silicon, an indium oxide film containing 2 to 20 wt% zinc oxide, a titanium nitride film, a chromium film, a tungsten film, a Zn film, a Pt film, or the like In addition, a stack of titanium nitride and a film containing aluminum as a main component, a three-layer structure including a titanium nitride film, a film containing aluminum as a main component, and a titanium nitride film can be used. Note that with a stacked structure, resistance as a wiring is low, good ohmic contact can be obtained, and a function as an anode can be obtained.

  The layer 616 containing a light-emitting substance is formed by various methods such as an evaporation method using an evaporation mask, an inkjet method, and a spin coating method. The layer 616 containing a light-emitting substance contains the organometallic complex of the present invention described in Embodiment Mode 1. In addition, another material included in the layer 616 containing a light-emitting substance may be a low molecular material, a medium molecular material (including an oligomer or a dendrimer), or a high molecular material.

Further, as a material used for the second electrode 617 formed over the light-emitting substance-containing layer 616 and functioning as a cathode, a material having a low work function (Al, Mg, Li, Ca, or an alloy or compound thereof, MgAg, or the like) , MgIn, AlLi, LiF, be used or CaF ₂₎ preferred. Note that in the case where light generated in the layer 616 containing a light-emitting substance passes through the second electrode 617, the second electrode 617 includes a thin metal film and a transparent conductive film (ITO, 2 to 20 wt. % Of indium oxide containing zinc oxide, indium tin oxide containing silicon, zinc oxide (ZnO), or the like is preferably used.

  Further, the sealing substrate 604 is bonded to the element substrate 610 with the sealant 605, whereby the light-emitting element 618 is provided in the space 607 surrounded by the element substrate 610, the sealing substrate 604, and the sealant 605. Yes. Note that the space 607 is filled with a filler, and may be filled with a sealant 605 in addition to an inert gas (such as nitrogen or argon).

  Note that an epoxy-based resin is preferably used for the sealant 605. Moreover, it is desirable that these materials are materials that do not transmit moisture and oxygen as much as possible. In addition to a glass substrate and a quartz substrate, a plastic substrate made of FRP (Fiberglass-Reinforced Plastics), PVF (polyvinyl fluoride), polyester, acrylic, or the like can be used as a material used for the sealing substrate 604.

  As described above, a light-emitting device manufactured using the organometallic complex of the present invention can be obtained.

  Since the light-emitting device of the present invention uses the organometallic complex described in Embodiment Mode 1, a light-emitting device having favorable characteristics can be obtained. Specifically, since the light-emitting element with high emission efficiency is included, a light-emitting device with reduced power consumption can be obtained. In addition, since red light emission with high luminous efficiency is possible, the light-emitting device is suitable for a full-color display, has low power consumption, and excellent color reproducibility.

  As described above, in this embodiment mode, an active light-emitting device that controls driving of a light-emitting element using a transistor has been described; A passive light emitting device may be used. FIG. 5 is a perspective view of a passive light emitting device manufactured by applying the present invention. In FIG. 5, a layer 955 containing a light-emitting substance is provided over the substrate 951 between the electrode 952 and the electrode 956. An end portion of the electrode 952 is covered with an insulating layer 953. A partition layer 954 is provided over the insulating layer 953. The side wall of the partition wall layer 954 has an inclination such that the distance between one side wall and the other side wall becomes narrower as it approaches the substrate surface. That is, the cross section in the short side direction of the partition wall layer 954 has a trapezoidal shape, and the bottom side (side facing the surface direction of the insulating layer 953 and in contact with the insulating layer 953) is the top side (surface of the insulating layer 953). The direction is the same as the direction and is shorter than the side not in contact with the insulating layer 953. In this manner, by providing the partition layer 954, defects in the light-emitting element due to static electricity or the like can be prevented. A passive light-emitting device can also be driven with low power consumption by including the light-emitting element of the present invention with high light emission efficiency.

(Embodiment 7)
In this embodiment mode, electronic devices of the present invention which include the light-emitting device described in Embodiment Mode 6 as a part thereof will be described. The electronic device of the present invention includes the organometallic complex described in Embodiment 1 and has a display portion with high emission efficiency and reduced power consumption. In addition, it has a display portion with excellent color reproducibility. When the organometallic complex of the present invention is used for a full-color display, a light-emitting element having the same structure as that described in Embodiments 2 to 5 can be applied using various light-emitting substances other than the red light-emitting element. .

  As an electronic device having a light-emitting element manufactured using the organometallic complex of the present invention, a video camera, a digital camera, a goggle-type display, a navigation system, an audio playback device (car audio, audio component, etc.), a computer, a game device, Play back a recording medium such as a portable information terminal (mobile computer, mobile phone, portable game machine or electronic book), an image playback device (specifically, Digital Versatile Disc (DVD)) equipped with a recording medium, And a device provided with a display device capable of displaying). Specific examples of these electronic devices are shown in FIGS.

  FIG. 6A illustrates a television device according to the present invention, which includes a housing 9101, a supporting base 9102, a display portion 9103, a speaker portion 9104, a video input terminal 9105, and the like. In this television device, the display portion 9103 is formed by arranging light-emitting elements similar to those described in Embodiment Modes 2 to 5 in a matrix. The light-emitting element has a feature of high luminous efficiency and low power consumption. Moreover, it has the characteristic that red light emission with high luminous efficiency is possible. Since the display portion 9103 including the light-emitting elements has similar features, this television set has no deterioration in image quality and low power consumption. With such a feature, the deterioration compensation function and the power supply circuit can be significantly reduced or reduced in the television device, so that the housing 9101 and the support base 9102 can be reduced in size and weight. In the television device according to the present invention, low power consumption, high image quality, and reduction in size and weight are achieved, so that a product suitable for a living environment can be provided. In addition, since the light-emitting element that can emit red light with high luminous efficiency is included, a television device having a display portion with low power consumption and excellent color reproducibility can be obtained.

  FIG. 6B illustrates a computer according to the present invention, which includes a main body 9201, a housing 9202, a display portion 9203, a keyboard 9204, an external connection port 9205, a pointing device 9206, and the like. In this computer, the display portion 9203 is formed by arranging light-emitting elements similar to those described in Embodiment Modes 2 to 5 in a matrix. The light-emitting element has a feature of high luminous efficiency and low power consumption. Moreover, it has the characteristic that red light emission with high luminous efficiency is possible. Since the display portion 9203 including the light-emitting elements has similar features, this computer has no deterioration in image quality and has low power consumption. With such a feature, the deterioration compensation function and the power supply circuit can be significantly reduced or reduced in the computer, so that the main body 9201 and the housing 9202 can be reduced in size and weight. In the computer according to the present invention, low power consumption, high image quality, and reduction in size and weight are achieved; therefore, a product suitable for the environment can be provided. In addition, since the light-emitting element that can emit red light with high luminous efficiency is included, a computer having a display portion with low power consumption and excellent color reproducibility can be obtained.

  6C illustrates a cellular phone according to the present invention, which includes a main body 9401, a housing 9402, a display portion 9403, an audio input portion 9404, an audio output portion 9405, operation keys 9406, an external connection port 9407, an antenna 9408, and the like. . In this cellular phone, the display portion 9403 is formed by arranging light-emitting elements similar to those described in Embodiments 2 to 5 in a matrix. The light-emitting element has a feature of high luminous efficiency and low power consumption. Moreover, it has the characteristic that red light emission with high luminous efficiency is possible. Since the display portion 9403 including the light-emitting elements has similar features, the cellular phone has no deterioration in image quality and low power consumption. With such a feature, the deterioration compensation function and the power supply circuit can be significantly reduced or reduced in the mobile phone, so that the main body 9401 and the housing 9402 can be reduced in size and weight. Since the cellular phone according to the present invention has low power consumption, high image quality, and reduced size and weight, a product suitable for carrying can be provided. In addition, since the light-emitting element that can emit red light with high luminous efficiency is included, a mobile phone having a display portion with low power consumption and excellent color reproducibility can be obtained.

  6D illustrates a camera according to the present invention, which includes a main body 9501, a display portion 9502, a housing 9503, an external connection port 9504, a remote control receiving portion 9505, an image receiving portion 9506, a battery 9507, an audio input portion 9508, and operation keys 9509. , An eyepiece 9510 and the like. In this camera, the display portion 9502 is configured by arranging light-emitting elements similar to those described in Embodiment Modes 2 to 5 in a matrix. The light-emitting element has a feature of high luminous efficiency and low power consumption. Moreover, it has the characteristic that red light emission with high luminous efficiency is possible. Since the display portion 9502 including the light-emitting elements has similar features, this camera has no deterioration in image quality and has low power consumption. With such a feature, a deterioration compensation function and a power supply circuit can be significantly reduced or reduced in the camera, so that the main body 9501 can be reduced in size and weight. Since the camera according to the present invention has low power consumption, high image quality, and small size and light weight, a product suitable for carrying can be provided. In addition, since the light-emitting element that can emit red light with high luminous efficiency is included, a camera having a display portion with low power consumption and excellent color reproducibility can be obtained.

  As described above, the applicable range of the light-emitting device of the present invention is so wide that the light-emitting device can be applied to electronic devices in various fields. By using the organometallic complex of the present invention, an electronic device having a display portion with low power consumption and excellent color reproducibility can be provided.

  The light-emitting device of the present invention can also be used as a lighting device. One mode in which the light-emitting element of the present invention is used as a lighting device will be described with reference to FIGS.

  FIG. 7 illustrates an example of a liquid crystal display device using the light-emitting device of the present invention as a backlight. The liquid crystal display device illustrated in FIG. 7 includes a housing 901, a liquid crystal layer 902, a backlight 903, and a housing 904, and the liquid crystal layer 902 is connected to a driver IC 905. The backlight 903 uses the light-emitting device of the present invention, and a current is supplied from a terminal 906.

  By using the light-emitting device of the present invention as a backlight of a liquid crystal display device, a backlight with reduced power consumption can be obtained. Further, the light-emitting device of the present invention is a surface-emitting illumination device and can have a large area, so that the backlight can have a large area and a liquid crystal display device can have a large area. Further, since the light-emitting device of the present invention is thin and has low power consumption, the display device can be thinned and the power consumption can be reduced.

  FIG. 8 illustrates an example in which the light-emitting device to which the present invention is applied is used as a table lamp which is a lighting device. A table lamp illustrated in FIG. 8 includes a housing 2001 and a light source 2002, and the light-emitting device of the present invention is used as the light source 2002. Since the light-emitting device of the present invention can emit light with high luminance, the hand can be brightly illuminated when performing fine work.

  FIG. 9 illustrates an example in which the light-emitting device to which the present invention is applied is used as an indoor lighting device 3001. Since the light-emitting device of the present invention can have a large area, it can be used as a large-area lighting device. In addition, since the light-emitting device of the present invention is thin and has low power consumption, it can be used as a lighting device with low thickness and low power consumption. In this manner, in the room where the light-emitting device to which the present invention is applied is used as an indoor lighting device 3001, the television device 3002 according to the present invention as described with reference to FIG. Can be appreciated. In such a case, since both devices have low power consumption, powerful images can be viewed in a bright room without worrying about electricity charges.

<< Synthesis Example 1 >>
In Synthesis Example 1, the organometallic complex of the present invention represented by the structural formula (1) of Embodiment 1, (acetylacetonato) bis (2,3,5-triphenylpyrazinato) iridium (III) A synthesis example of (abbreviation: [Ir (tppr) ₂ (acac)]) is specifically exemplified.

<Step 1; Synthesis of 2,3,5-triphenylpyrazine (abbreviation: Htppr)>
First, in a nitrogen atmosphere, a solution in which 5.5 mL of phenyllithium dibutyl ether solution (2.1 mol / L, manufactured by Wako Pure Chemical Industries, Ltd.) and 50 mL of diethyl ether were mixed was prepared. Next, 2.43 g of 2,3-diphenylpyrazine was added dropwise to this solution while cooling with ice, followed by stirring at room temperature for 24 hours. After stirring, water was added to the mixture, and the organic layer was extracted with diethyl ether. The extracted organic layer was washed with water and dried over magnesium sulfate. After drying, an excess of active manganese dioxide was added to the organic layer, and the mixture was stirred well and then filtered. After the solvent of the filtrate was distilled off, the obtained residue was recrystallized with ethanol to obtain a pyrazine derivative Htppr (yellow powder, yield 56%). The synthesis scheme of Step 1 is shown in (a-1) below.

<Step 2; Synthesis of di-μ-chloro-bis [bis (2,3,5-triphenylpyrazinato) iridium (III)] (abbreviation: [Ir (tppr) ₂ Cl] ₂ )>
Next, in a mixed solvent of 30 mL of 2-ethoxyethanol and 10 mL of water, 1.08 g of the pyrazine derivative Htppr obtained in Step 1 above, iridium chloride hydrate (IrCl ₃ .H ₂ O) (manufactured by Sigma-Aldrich) ) Was mixed, and the mixture was refluxed for 16 hours in a nitrogen atmosphere. The precipitated powder was filtered and washed with ethanol, ether, and hexane to obtain a binuclear complex [Ir (tppr) ₂ Cl] ₂ (orange powder, yield 97%). The synthesis scheme of Step 2 is shown in (b-1) below.

<Step 3; Synthesis of (acetylacetonato) bis (2,3,5-triphenylpyrazinato) iridium (III) (abbreviation: [Ir (tppr) ₂ (acac)])
Furthermore, 2.00 g of the binuclear complex [Ir (tppr) ₂ Cl] ₂ obtained in Step 2 above, 0.37 mL of acetylacetone, and 1.26 g of sodium carbonate were mixed using 40 mL of 2-ethoxyethanol as a solvent, and the mixture Was refluxed for 18 hours under a nitrogen atmosphere. After refluxing, the mixture was filtered and the filtrate was left for one week. Thereafter, the precipitated crystals were removed by filtration, and the solvent of the filtrate was distilled off. The obtained residue was recrystallized with a mixed solvent of dichloromethane and ethanol, and the powder obtained by recrystallization was washed with ethanol and then with ether, whereby the organometallic complex [Ir (tppr) ₂ (acac) of the present invention was obtained. (Red powder, 16% yield). The synthesis scheme of Step 3 is shown in (c-1) below.

In addition, the analysis result by the nuclear magnetic resonance spectroscopy (< ¹ > H-NMR) of the red powder obtained at the said step 3 is shown below. Further, the ¹ H-NMR chart is shown in FIG. FIG. 10B is an enlarged view of the vertical axis of FIG. From this, it was found that in the synthesis example 1, the organometallic complex [Ir (tppr) ₂ (acac)] of the present invention represented by the above structural formula (1) was obtained.

¹ H-NMR. δ (CDCl ₃ ): 1.92 (s, 6H), 5.35 (s, 1H), 6.45-6.54 (m, 4H), 6.67 (td, 2H), 6.91 ( d, 2H), 7.41-7.57 (m, 12H), 7.81 (m, 4H), 8.08 (dd, 4H), 8.98 (s, 2H).

Further, the decomposition temperature T _d of the obtained organometallic complex [Ir (tppr) ₂ (acac)] of the present invention was measured by a differential thermothermal gravimetric simultaneous measurement apparatus (TG / DTA 320 type, manufactured by Seiko Denshi Co., Ltd.). As a result, it was found that T _d = 331 ° C. and good heat resistance was exhibited.

Next, an absorption spectrum of [Ir (tppr) ₂ (acac)] was measured. The absorption spectrum was measured at room temperature using a UV-visible spectrophotometer (V550 type manufactured by JASCO Corporation) and a degassed dichloromethane solution (0.10 mmol / L). In addition, an emission spectrum of [Ir (tppr) ₂ (acac)] was measured. The emission spectrum was measured at room temperature using a fluorometer (FS920, manufactured by Hamamatsu Photonics) using a degassed dichloromethane solution (0.35 mmol / L). The measurement results are shown in FIG. The horizontal axis represents wavelength, and the vertical axis represents molar extinction coefficient and emission intensity.

As shown in FIG. 11, the organometallic complex [Ir (tppr) ₂ (acac)] of the present invention has an emission peak at 622 nm, and red-orange emission was observed from the solution.

In the organometallic complex [Ir (tppr) ₂ (acac)] of the present invention, a number of absorption peaks are observed in the visible light region. This is a unique absorption found in some organometallic complexes such as ortho-metal complexes, and is analogized to correspond to singlet MLCT transitions, triplet π-π ^* transitions, triplet MLCT transitions, and the like. In particular, the absorption peak on the longest wavelength side has a broad tail in the visible light region, which is considered to be a triplet MLCT transition. That is, it was found that the organometallic complex [Ir (tppr) ₂ (acac)] of the present invention is a compound capable of direct photoexcitation and intersystem crossing to a triplet excited state. Therefore, the obtained light emission is also considered to be light emission from a triplet excited state, that is, phosphorescence.

<< Synthesis Example 2 >>
In Synthesis Example 2, a synthesis method different from Synthesis Example 1 is illustrated with respect to 2,3,5-triphenylpyrazine (abbreviation: Htppr) synthesized in Step 1 of Synthesis Example 1 described above.

First, using ethanol 200 mL as a solvent, 4.60 g of phenylglyoxal (manufactured by Tokyo Chemical Industry Co., Ltd.) and 7.28 g of meso-1,2-diphenylethylenediamine (manufactured by Sigma-Aldrich Co., Ltd.) are mixed, and the mixture is mixed with a nitrogen atmosphere. At reflux for 6 hours. After refluxing, the solvent of this mixture was distilled off, and the resulting residue was recrystallized from ethanol. The ocherous powder obtained by recrystallization was dissolved in dichloromethane, and activated manganese dioxide was added to this solution in excess, and the mixture was stirred well and then filtered. After the solvent of the filtrate was distilled off, the obtained residue was recrystallized with ethanol to obtain a pyrazine derivative Htppr (yellow powder, yield 37%). The synthesis scheme of Synthesis Example 2 is shown in (a-1-2) below.

  In this example, a light-emitting element of the present invention will be described with reference to FIG. The chemical formulas of the materials used in this example and Example 3 are shown below.

(Light emitting element 1)
First, indium tin oxide containing silicon oxide was formed over a glass substrate 2101 by a sputtering method, so that a first electrode 2102 was formed. The film thickness was 110 nm and the electrode area was 2 mm × 2 mm.

Next, the substrate on which the first electrode is formed is fixed to a substrate holder provided in the vacuum evaporation apparatus so that the surface on which the first electrode is formed is downward, and the pressure is reduced to about 10 ⁻⁴ Pa. After that, NPB and molybdenum oxide (VI) were co-evaporated on the first electrode 2102 to form a layer 2103 including a composite material formed by combining an organic compound and an inorganic compound. The film thickness was 50 nm, and the weight ratio of NPB and molybdenum oxide (VI) was adjusted to 4: 1 (= NPB: molybdenum oxide). Note that the co-evaporation method is an evaporation method in which evaporation is performed simultaneously from a plurality of evaporation sources in one processing chamber.

  Next, a 4 nm film of 4,4′-bis [N- (1-naphthyl) -N-phenylamino] biphenyl (abbreviation: NPB) is formed over the layer 2103 containing the composite material by an evaporation method using resistance heating. The hole transport layer 2104 was formed by forming the film so as to have a thickness.

Further, 2,3-bis {4- [N- (4-biphenylyl) -N-phenylamino] phenyl} quinoxaline (abbreviation: BPAPQ) and (acetylacetonato) bis (2) represented by the structural formula (1) , 3,5-triphenylpyrazinato) iridium (III) (abbreviation: Ir (tppr) ₂ (acac)) is co-evaporated to form a light-emitting layer 2105 having a thickness of 30 nm on the hole-transport layer 2104. Formed. Here, the weight ratio between BPAPQ and Ir _(tppr) 2 (acac) is 1: 0.05: was adjusted to (= BPAPQ Ir _(tppr) 2 (acac)).

  Thereafter, bis (2-methyl-8-quinolinolato) (4-phenylphenolato) aluminum (abbreviation: BAlq) is formed to a thickness of 10 nm over the light-emitting layer 2105 by a resistance heating vapor deposition method. Then, an electron transport layer 2106 was formed.

  Further, tris (8-quinolinolato) aluminum (abbreviation: Alq) and lithium were co-evaporated on the electron transport layer 2106, whereby an electron injection layer 2107 was formed with a thickness of 50 nm. Here, the weight ratio of Alq to lithium was adjusted to be 1: 0.01 (= Alq: lithium).

  Finally, a light-emitting element 1 was manufactured by forming a second electrode 2108 by depositing aluminum on the electron injection layer 2107 so as to have a thickness of 200 nm by using a resistance heating vapor deposition method. .

FIG. 13 shows current density-luminance characteristics of the light-emitting element 1. Further, voltage-luminance characteristics are shown in FIG. Further, FIG. 15 shows luminance-current efficiency characteristics. In addition, FIG. 16 shows luminance vs. external quantum efficiency characteristics. In addition, FIG. 17 shows an emission spectrum when a current of 1 mA is passed. FIG. 17 indicates that light emission of the light-emitting element 1 is Ir (tppr) ₂ (acac). The CIE chromaticity coordinates of the light-emitting element 1 are (x, y) = (0.66, 0.34) when the luminance is 1000 cd / m ² , and the light emission of the light-emitting element 1 is red. Further, as can be seen from FIG. 16, the light-emitting element 1 shows a high external quantum efficiency. Therefore, the light emission efficiency of the light emitting element 1 is high. 15 shows that the light-emitting element 1 has high luminous efficiency. Further, from FIG. 14, the voltage for obtaining a certain luminance is low. Therefore, it can be seen that the power consumption of the light emitting element 1 is small.

Note that when the initial luminance was set to 1000 cd / m ² and the light-emitting element 1 of this example was driven under the condition of a constant current density, the luminance after 100 hours maintained 97% of the initial luminance and almost deteriorated. There wasn't.

  In this example, a light-emitting element of the present invention will be described with reference to FIG.

(Light emitting element 2)
First, indium tin oxide containing silicon oxide was formed over a glass substrate 2101 by a sputtering method, so that a first electrode 2102 was formed. The film thickness was 110 nm and the electrode area was 2 mm × 2 mm.

Next, the substrate on which the first electrode is formed is fixed to a substrate holder provided in the vacuum evaporation apparatus so that the surface on which the first electrode is formed is downward, and the pressure is reduced to about 10 ⁻⁴ Pa. After that, NPB and molybdenum oxide (VI) were co-evaporated on the first electrode 2102 to form a layer 2103 including a composite material formed by combining an organic compound and an inorganic compound. The film thickness was 50 nm, and the weight ratio of NPB and molybdenum oxide (VI) was adjusted to 4: 1 (= NPB: molybdenum oxide). Note that the co-evaporation method is an evaporation method in which evaporation is performed simultaneously from a plurality of evaporation sources in one processing chamber.

  Next, a 4 nm film of 4,4′-bis [N- (1-naphthyl) -N-phenylamino] biphenyl (abbreviation: NPB) is formed over the layer 2103 containing the composite material by an evaporation method using resistance heating. The hole transport layer 2104 was formed by forming the film so as to have a thickness.

Furthermore, bis [2- (2-hydroxyphenyl) benzoxazolate] zinc (abbreviation: Zn (PBO) ₂ ) and (acetylacetonato) bis (2,3,5-) represented by the structural formula (1) A triphenylpyrazinato) iridium (III) (abbreviation: Ir (tppr) ₂ (acac)) was co-evaporated to form a light-emitting layer 2105 with a thickness of 30 nm on the hole-transport layer 2104. Here, the weight ratio of Zn _{(PBO) 2} and Ir _(tppr) 2 (acac) _{is, 1: 0.05 (= Zn (} PBO) 2: Ir (tppr) 2 (acac)) adjusted to be did.

  Thereafter, bis (2-methyl-8-quinolinolato) (4-phenylphenolato) aluminum (abbreviation: BAlq) is formed to a thickness of 10 nm over the light-emitting layer 2105 by a resistance heating vapor deposition method. Then, an electron transport layer 2106 was formed.

  Further, tris (8-quinolinolato) aluminum (abbreviation: Alq) and lithium were co-evaporated on the electron transport layer 2106, whereby an electron injection layer 2107 was formed with a thickness of 50 nm. Here, the weight ratio of Alq to lithium was adjusted to be 1: 0.01 (= Alq: lithium).

  Finally, a light-emitting element 2 was manufactured by forming a second electrode 2108 by depositing aluminum on the electron injection layer 2107 to have a thickness of 200 nm using a resistance heating vapor deposition method. .

FIG. 18 shows current density-luminance characteristics of the light-emitting element 2. Further, voltage-luminance characteristics are shown in FIG. Further, FIG. 20 shows luminance-current efficiency characteristics. In addition, FIG. 21 shows luminance vs. external quantum efficiency characteristics. In addition, FIG. 22 shows an emission spectrum when a current of 1 mA is passed. FIG. 22 shows that light emission of the light-emitting element 2 is Ir (tppr) ₂ (acac). The CIE chromaticity coordinates of the light emitting element 2 are (x, y) = (0.67, 0.33) when the luminance is 1000 cd / m ² , and the light emission of the light emitting element 2 is red. In addition, as can be seen from FIG. 21, the light-emitting element 2 shows high external quantum efficiency. In particular, it can be seen that the light-emitting element 2 exhibits a higher external quantum efficiency than the light-emitting element 1 manufactured in Example 1. The light-emitting element 2 uses the organometallic complex and the zinc complex of the present invention as the light-emitting layer, and thus it is considered that higher external quantum efficiency can be realized.

  20 shows that the light-emitting element 2 has high luminous efficiency. Further, FIG. 19 shows that the voltage for obtaining a certain luminance is reduced. Therefore, it can be seen that the power consumption of the light emitting element 2 is small.

<< Synthesis Example 3 >>
In Synthesis Example 3, the organometallic complex of the present invention represented by the structural formula (20) of Embodiment 1, (acetylacetonato) bis (2,3-diphenyl-5-p-tolylpyrazinato) iridium (III) A synthesis example of (abbreviation: [Ir (dppr-MP) ₂ (acac)]) is specifically exemplified.

<Step 1; Synthesis of 2,3-diphenyl-5-p-tolylpyrazine (abbreviation: Hdppr-MP)>
First, in a nitrogen atmosphere, 0.49 g of magnesium and 3 mL of THF are suspended, a small amount of 1,2-dibromoethane is added, and then a mixed solution in which 3.42 g of 4-bromotoluene is dissolved in 20 mL of THF is dropped, The Grignard reagent was prepared by stirring for 3 hours under heating to reflux. Next, 4.22 g of 2,3-diphenylpyrazine was dissolved in 20 mL of THF, the Grignard reagent prepared earlier was added dropwise, and the mixture was stirred for 5 hours with heating under reflux. Water was added to this mixture, and the organic layer was extracted with chloroform. The obtained organic layer was dried over magnesium sulfate. Manganese dioxide was added to the dried solution, shaken lightly, and then filtered, and the solvent of this solution was distilled off. The residue obtained by evaporation was dissolved in dichloromethane, ethanol was added and the mixture was allowed to stand, and yellow crystals were precipitated. The crystals were collected by filtration and washed with ethanol to obtain the target pyrazine derivative Hdppr-MP (yield 30%). The synthesis scheme of Step 1 is shown in (a-2) below.

<Step 2; Synthesis of di-μ-chloro-bis [bis (2,3-diphenyl-5-p-tolylpyrazinato) iridium (III)] (abbreviation: [Ir (dppr-MP) ₂ Cl] ₂ )>
Next, 24 mL of 2-ethoxyethanol and 8 mL of water, 0.64 g of the pyrazine derivative Hdppr-MP obtained in Step 1 above, 0.30 g of iridium chloride hydrate (IrCl ₃ .H ₂ O) (manufactured by Sigma-Aldrich) The flask was placed in a recovery flask equipped with a reflux tube, and the atmosphere in the flask was replaced with argon. Thereafter, microwaves (2.45 GHz 150 W) were irradiated for 1 hour and reacted. The orange powder precipitated from the reaction solution was filtered and washed with ethanol to obtain a binuclear complex [Ir (dppr-MP) ₂ Cl] ₂ (yield 58%). Note that a microwave synthesizer (Discovery manufactured by CEM) was used for microwave irradiation. The synthesis scheme of Step 2 is shown in (b-2) below.

<Step 3; Synthesis of (acetylacetonato) bis (2,3-diphenyl-5-p-tolylpyrazinato) iridium (III) (abbreviation: [Ir (dppr-MP) ₂ (acac)])
Furthermore, 20 mL of 2-ethoxyethanol, 0.50 g of the binuclear complex [Ir (dppr-MP) ₂ Cl] ₂ obtained in Step 2 above, 0.09 mL of acetylacetone, and 0.31 g of sodium carbonate were added to an eggplant flask equipped with a reflux tube. The flask was purged with argon. Then, the microwave (2.45 GHz 150W) was irradiated for 30 minutes, and it was made to react. The reaction solution was filtered, and the obtained filtrate was concentrated to dryness. The obtained residue was recrystallized with ethanol, and the obtained red powder was washed with ethanol and then with ether to obtain the organometallic complex [Ir (dppr-MP) ₂ (acac)] of the present invention. (Yield 96%). The synthesis scheme of Step 3 is shown in (c-2) below.

In addition, the analysis result by the nuclear magnetic resonance spectroscopy (< ¹ > H-NMR) of the red powder obtained at the said step 3 is shown below. A ¹ H-NMR chart is shown in FIG. From this, it was found that in this synthesis example 3, the organometallic complex [Ir (dppr-MP) ₂ (acac)] of the present invention represented by the above structural formula (20) was obtained.

¹ H-NMR. δ (CDCl ₃ ): 1.91 (s, 6H), 2.44 (s, 6H), 5.33 (s, 1H), 6.47 (m, 4H), 6.66 (t, 2H) 6.89 (d, 2H), 7.33 (m, 5H), 7.54 (m, 7H), 7.80 (m, 4H), 7.79 (d, 4H), 8.94 ( s, 2H).

In addition, the decomposition temperature of the obtained organometallic complex [Ir (dppr-MP) ₂ (acac)] of the present invention was measured using a high vacuum differential type differential thermal balance (manufactured by Bruker AXS Co., Ltd., TG-DTA2410SA). It was measured. When the rate of temperature increase was set to 10 ° C./min and the temperature was increased under normal pressure, a 5% weight loss was observed at 338 ° C., indicating that good heat resistance was exhibited.

Next, an absorption spectrum of [Ir (dppr-MP) ₂ (acac)] was measured. The absorption spectrum was measured at room temperature using a UV-visible spectrophotometer (V550 type manufactured by JASCO Corporation) and a dichloromethane solution (0.10 mmol / L). In addition, an emission spectrum of [Ir (dppr-MP) ₂ (acac)] was measured. The emission spectrum was measured at room temperature using a fluorometer (FS920, manufactured by Hamamatsu Photonics) using a degassed dichloromethane solution (0.35 mmol / L). The measurement results are shown in FIG. The horizontal axis represents wavelength, and the vertical axis represents molar extinction coefficient and emission intensity.

As shown in FIG. 25, the organometallic complex [Ir (dppr-MP) ₂ (acac)] of the present invention has an emission peak at 620 nm, and red light emission was observed from the solution.

<< Synthesis Example 4 >>
In Synthesis Example 4, the organometallic complex of the present invention represented by Structural Formula (27) of Embodiment 1, (acetylacetonato) bis (5-phenyl-2,3-di-p-tolylpyrazinato) iridium (III ) (Abbreviation: [Ir (Mdppr-P) ₂ (acac)]) is specifically exemplified.

<Step 1; Synthesis of 2,3-di-p-tolylpyrazine>
First, in a nitrogen atmosphere, 300 mL of dehydrated ethanol was used as a solvent, 25.52 g of 4,4′-dimethylbenzyl and 6.44 g of anhydrous ethylenediamine were dissolved, and the mixture was reacted for 12 and a half hours by refluxing. To this reaction solution, 34.71 g of iron (III) chloride was added, and the mixture was reacted with gentle heating and stirring at 70 ° C. or lower for 2.5 hours. Water was added to this mixture, and the organic layer was extracted with dichloromethane. The obtained organic layer was dried over magnesium sulfate. After drying, it was filtered and the solvent of this solution was distilled off. The residue obtained by distillation was purified by silica gel column chromatography using dichloromethane as a developing solvent to obtain 2,3-di-p-tolylpyrazine as an intermediate (orange powder, 31% yield).

<Step 2; Synthesis of 5-phenyl-2,3-di-p-tolylpyrazine (abbreviation: HMdppr-P)>
Next, in a nitrogen atmosphere, 6.48 mL of phenyllithium dibutyl ether solution (manufactured by Wako Pure Chemical Industries, Ltd., 2.1 mol / L) and 80 mL of diethyl ether were mixed. While cooling this mixed solution with ice, 3.22 g of 2,3-di-p-tolylpyrazine as an intermediate obtained in Step 1 above was added and stirred at room temperature for 24 hours. Water was added to this mixture, and the organic layer was extracted with dichloromethane. The obtained organic layer was washed with water and dried over magnesium sulfate. To the solution after drying, an excess of active manganese dioxide was added and filtered. After the solvent of this solution was distilled off, the residue obtained by the distillation was purified by silica gel column chromatography using dichloromethane as a developing solvent to obtain the target pyrazine derivative HMdppr-P (orange powder, yield). Rate 22%). The synthesis scheme of Step 1 and Step 2 is shown in (a-3) below.

<Step 3; Synthesis of di-μ-chloro-bis [bis (5-phenyl-2,3-di-p-tolylpyrazinato) iridium (III)] (abbreviation: [Ir (Mdppr-P) ₂ Cl] ₂ ) >
Furthermore, 18 mL of 2-ethoxyethanol and 6 mL of water, 0.82 g of the pyrazine derivative HMdppr-P obtained in Step 2 above, 0.36 g of iridium chloride hydrate (IrCl ₃ · H ₂ O) (manufactured by Sigma-Aldrich), The flask was placed in an eggplant flask equipped with a reflux tube, and the atmosphere in the flask was replaced with argon. Then, the microwave (2.45 GHz 200W) was irradiated for 1 hour, and was made to react. The orange powder precipitated from the reaction solution was filtered and washed with ethanol to obtain a binuclear complex [Ir (Mdppr-P) ₂ Cl] ₂ (yield 82%). Note that a microwave synthesizer (Discovery manufactured by CEM) was used for microwave irradiation. The synthesis scheme of Step 3 is shown in (b-3) below.

<Step 4; Synthesis of (acetylacetonato) bis (5-phenyl-2,3-di-p-tolylpyrazinato) iridium (III) (abbreviation: [Ir (Mdppr-P) ₂ (acac)])
Further, 20 mL of 2-ethoxyethanol, 0.44 g of the binuclear complex [Ir (Mdppr-P) ₂ Cl] ₂ obtained in Step 3 above, 0.08 mL of acetylacetone, and 0.25 g of sodium carbonate were added to the eggplant flask equipped with a reflux tube. The flask was purged with argon. Then, the microwave (2.45 GHz 200W) was irradiated for 30 minutes, and it was made to react. The reaction solution was filtered, and the obtained filtrate was concentrated to dryness. The obtained residue was recrystallized with ethanol, and the obtained red powder was washed with ethanol and then with ether to obtain the organometallic complex [Ir (Mdppr-P) ₂ (acac)] of the present invention. (Yield 31%). The synthesis scheme of Step 4 is shown in (c-3) below.

In addition, the analysis result by the nuclear magnetic resonance spectroscopy (< ¹ > H-NMR) of the red powder obtained at the said step 4 is shown below. A ¹ H-NMR chart is shown in FIG. From this, it was found that, in Synthesis Example 4, the organometallic complex [Ir (Mdppr-P) ₂ (acac)] of the present invention represented by the above structural formula (27) was obtained.

¹ H-NMR. δ (CDCl ₃ ): 1.91 (s, 6H), 2.02 (s, 6H), 2.48 (s, 6H), 5.33 (s, 1H), 6.28 (s, 2H) , 6.36 (d, 2H), 6.88 (d, 2H), 7.33 (m, 4H), 7.51 (m, 6H), 7.72 (d, 4H), 8.08 ( d, 4H), 8.91 (s, 2H).

Further, the decomposition temperature of the obtained organometallic complex [Ir (Mdppr-P) ₂ (acac)] of the present invention was determined by a high vacuum differential type differential thermal balance (manufactured by Bruker AXS Co., Ltd., TG-DTA2410SA). It was measured. When the rate of temperature increase was set to 10 ° C./min and the temperature was increased under normal pressure, a 5% weight loss was observed at 342 ° C., indicating good heat resistance.

Next, an absorption spectrum of [Ir (Mdppr-P) ₂ (acac)] was measured. The absorption spectrum was measured at room temperature using a UV-visible spectrophotometer (V550 type manufactured by JASCO Corporation) and a dichloromethane solution (0.096 mmol / L). In addition, an emission spectrum of [Ir (Mdppr-P) ₂ (acac)] was measured. The emission spectrum was measured at room temperature using a fluorometer (FS920, manufactured by Hamamatsu Photonics) using a degassed dichloromethane solution (0.34 mmol / L). The measurement results are shown in FIG. The horizontal axis represents wavelength, and the vertical axis represents molar extinction coefficient and emission intensity.

As shown in FIG. 27, the organometallic complex [Ir (Mdppr-P) ₂ (acac)] of the present invention has an emission peak at 620 nm, and red light emission was observed from the solution.

<< Synthesis Example 5 >>
In this synthesis example 5, the organometallic complex of the present invention represented by the structural formula (3) of Embodiment 1, bis (2,3,5-triphenylpyrazinato) (picolinato) iridium (III) (abbreviation: A synthesis example of [Ir (tppr) ₂ (pic)]) is specifically exemplified.

<Synthesis of bis (2,3,5-triphenylpyrazinato) (picolinato) iridium (III) (abbreviation: [Ir (tppr) ₂ (pic)]>
25 mL of dichloromethane, 0.84 g of the binuclear complex [Ir (tppr) ₂ Cl] ₂ obtained in Step 2 of Synthesis Example 1 and 0.49 g of picolinic acid were placed in an eggplant flask equipped with a reflux tube, and the inside of the flask was purged with argon. . Then, the microwave (2.45 GHz 100W) was irradiated for 30 minutes, and it was made to react. The reaction solution was filtered, and the obtained filtrate was concentrated to dryness. The obtained residue was recrystallized with a mixed solvent of methanol and dichloromethane to obtain the organometallic complex [Ir (tppr) ₂ (pic)] of the present invention (yield 84%, reddish orange powder). Note that a microwave synthesizer (Discovery manufactured by CEM) was used for microwave irradiation. The synthesis scheme of this complex is shown in (c-4) below.

In addition, the analysis result by the nuclear magnetic resonance spectroscopy (< ¹ > H-NMR) of the reddish orange powder obtained at the said step is shown below. Further, the ¹ H-NMR chart is shown in FIG. From this, it was found that, in Synthesis Example 5, the organometallic complex [Ir (tppr) ₂ (pic)] of the present invention represented by the above structural formula (3) was obtained.

¹ H-NMR. δ (CDCl ₃ ): 6.42 (d, 1H), 6.58 (m, 3H), 6.77 (m, 2H), 6.93 (m, 2H), 7.39 (m, 3H) 7.45-7.56 (m, 8H), 7.67 (m, 4H), 7.77 (m, 4H), 8.09 (m, 3H), 8.48 (d, 1H), 8.28 (s, 1H).

In addition, the decomposition temperature of the obtained organometallic complex [Ir (tppr) ₂ (pic)] of the present invention was measured with a high vacuum differential type differential thermal balance (TG-DTA2410SA, manufactured by Bruker AXS). . When the rate of temperature increase was set to 10 ° C./min and the temperature was increased under normal pressure, a 5% weight loss was observed at 368 ° C., indicating that good heat resistance was exhibited.

Next, an absorption spectrum of [Ir (tppr) ₂ (pic)] was measured. The absorption spectrum was measured at room temperature using a UV-visible spectrophotometer (V550 type manufactured by JASCO Corporation) and a dichloromethane solution (0.10 mmol / L). In addition, an emission spectrum of [Ir (tppr) ₂ (pic)] was measured. The emission spectrum was measured at room temperature using a fluorometer (FS920, manufactured by Hamamatsu Photonics) using a degassed dichloromethane solution (0.35 mmol / L). The measurement results are shown in FIG. The horizontal axis represents wavelength, and the vertical axis represents molar extinction coefficient and emission intensity.

As shown in FIG. 29, the organometallic complex [Ir (tppr) ₂ (pic)] of the present invention has an emission peak at 606 nm, and orange emission was observed from the solution.

<< Synthesis Example 6 >>
In Synthesis Example 6, the organometallic complex of the present invention represented by the structural formula (34) of Embodiment 1, (acetylacetonato) bis (3-methyl-2,5-diphenylpyrazinato) iridium (III) A synthesis example of (abbreviation: [Ir (mppr-P) ₂ (acac)]) is specifically exemplified.

<Step 1; Synthesis of 3-methyl-2,5-diphenylpyrazine (abbreviation: Hmppr-P)>
First, 10 mL of dibutyl ether solution of phenyl lithium (manufactured by Wako Pure Chemical Industries, Ltd., 2.1 mol / L) and 120 mL of diethyl ether were mixed in a nitrogen atmosphere. While this mixed solution was ice-cooled, 2.87 g of 2-methyl-3-phenylpyrazine was added and stirred at room temperature for 24 hours. Water was added to this mixture, and the organic layer was extracted with ethyl acetate. The obtained organic layer was dried over magnesium sulfate. To the solution after drying, an excess of active manganese dioxide was added and filtered. The residue was obtained by distilling off the solvent of the obtained filtrate. The residue was purified by silica gel column chromatography using dichloromethane as a developing solvent to obtain the target pyrazine derivative Hmppr-P (orange oil, yield 12%). The synthesis scheme of Step 1 is shown in (a-5) below.

<Step 2; Synthesis of di-μ-chloro-bis [bis (3-methyl-2,5-diphenylpyrazinato) iridium (III)] (abbreviation: [Ir (mppr-P) ₂ Cl] ₂ )>
Next, 21 mL of 2-ethoxyethanol and 7 mL of water, 0.49 g of the pyrazine derivative Hmppr-P obtained in Step 1 above, and 0.30 g of iridium chloride hydrate (IrCl ₃ · H ₂ O) (manufactured by Sigma-Aldrich) were added. The flask was placed in a recovery flask equipped with a reflux tube, and the atmosphere in the flask was replaced with argon. Then, the microwave (2.45 GHz 150W) was irradiated for 30 minutes, and it was made to react. The orange powder precipitated from the reaction solution was filtered and washed with ethanol to obtain a binuclear complex [Ir (mppr-P) ₂ Cl] ₂ (yield 10%). Note that a microwave synthesizer (Discovery manufactured by CEM) was used for microwave irradiation. Moreover, the synthesis scheme of Step 2 is shown in (b-5) below.

<Step 3; Synthesis of (acetylacetonato) bis (3-methyl-2,5-diphenylpyrazinato) iridium (III) (abbreviation: [Ir (mppr-P) ₂ (acac)])
Further, 10 mL of 2-ethoxyethanol, 0.14 g of the binuclear complex [Ir (mppr-P) ₂ Cl] ₂ obtained in Step 2 above, 0.03 mL of acetylacetone, and 0.10 g of sodium carbonate were added to an eggplant flask equipped with a reflux tube. The flask was purged with argon. Then, the microwave (2.45 GHz 100W) was irradiated for 30 minutes, and it was made to react. The reddish orange powder precipitated from the reaction solution was filtered and washed with water, ethanol and then ether to obtain the organometallic complex [Ir (mppr-P) ₂ (acac)] of the present invention (yield 77). %). The synthesis scheme of Step 3 is shown in (c-5) below.

In addition, the analysis result by the nuclear magnetic resonance spectroscopy (< ¹ > H-NMR) of the reddish orange powder obtained by the said step is shown below. A ¹ H-NMR chart is shown in FIG. 30. From this, it was found that, in Synthesis Example 6, the organometallic complex [Ir (mppr-P) ₂ (acac)] of the present invention represented by the above structural formula (34) was obtained.

¹ H-NMR. δ (CDCl ₃ ): 1.85 (s, 6H), 3.17 (s, 6H), 5.29 (s, 1H), 6.35 (d, 2H), 6.72 (t, 2H) 6.91 (t, 2H), 7.55 (m, 6H), 7.95 (d, 2H), 8.06 (d, 4H), 8.93 (s, 2H).

Next, an absorption spectrum of [Ir (mppr-P) ₂ (acac)] was measured. The absorption spectrum was measured at room temperature using a UV-visible spectrophotometer (V550 type manufactured by JASCO Corporation) and a dichloromethane solution (0.12 mmol / L). In addition, an emission spectrum of [Ir (mppr-P) ₂ (acac)] was measured. The emission spectrum was measured at room temperature using a fluorometer (FS920, manufactured by Hamamatsu Photonics) using a degassed dichloromethane solution (0.41 mmol / L). The measurement results are shown in FIG. The horizontal axis represents wavelength, and the vertical axis represents molar extinction coefficient and emission intensity.

As shown in FIG. 31, the organometallic complex [Ir (mppr-P) ₂ (acac)] of the present invention has an emission peak at 607 nm, and orange emission was observed from the solution.

  In this example, a light-emitting element of the present invention will be described with reference to FIG. The chemical formula of the material used in this example is shown below.

(Light emitting element 3)
First, indium tin oxide containing silicon oxide was formed over a glass substrate 2101 by a sputtering method, so that a first electrode 2102 was formed. The film thickness was 110 nm and the electrode area was 2 mm × 2 mm.

Next, the substrate on which the first electrode is formed is fixed to a substrate holder provided in the vacuum evaporation apparatus so that the surface on which the first electrode is formed is downward, and the pressure is reduced to about 10 ⁻⁴ Pa. After that, NPB and molybdenum oxide (VI) were co-evaporated on the first electrode 2102 to form a layer 2103 including a composite material formed by combining an organic compound and an inorganic compound. The film thickness was 50 nm, and the weight ratio of NPB and molybdenum oxide (VI) was adjusted to 4: 1 (= NPB: molybdenum oxide). Note that the co-evaporation method is an evaporation method in which evaporation is performed simultaneously from a plurality of evaporation sources in one processing chamber.

  Next, a 4 nm film of 4,4′-bis [N- (1-naphthyl) -N-phenylamino] biphenyl (abbreviation: NPB) is formed over the layer 2103 containing the composite material by an evaporation method using resistance heating. The hole transport layer 2104 was formed by forming the film so as to have a thickness.

Further, 4- (9H-carbazol-9-yl) -4 ′-(5-phenyl-1,3,4-oxadiazol-2-yl) triphenylamine) (abbreviation: YGAO11) and structural formula (1 ) (Acetylacetonato) bis (2,3,5-triphenylpyrazinato) iridium (III) (abbreviation: Ir (tppr) ₂ (acac)) represented by A light emitting layer 2105 having a thickness of 30 nm was formed over the transport layer 2104. Here, the weight ratio between YGAO11 and Ir _(tppr) 2 (acac) is 1: 0.06: was adjusted to (= YGAO11 Ir _(tppr) 2 (acac)).

  Thereafter, bis (2-methyl-8-quinolinolato) (4-phenylphenolato) aluminum (abbreviation: BAlq) is formed to a thickness of 10 nm over the light-emitting layer 2105 by a resistance heating vapor deposition method. Then, an electron transport layer 2106 was formed.

  Further, tris (8-quinolinolato) aluminum (abbreviation: Alq) and lithium were co-evaporated on the electron transport layer 2106, whereby an electron injection layer 2107 was formed with a thickness of 50 nm. Here, the weight ratio of Alq to lithium was adjusted to be 1: 0.01 (= Alq: lithium).

  Finally, a light-emitting element 3 was manufactured by forming a second electrode 2108 by depositing aluminum on the electron injection layer 2107 to have a thickness of 200 nm using a resistance heating vapor deposition method. .

FIG. 32 shows current density-luminance characteristics of the light-emitting element 3. In addition, FIG. 33 shows voltage-luminance characteristics. In addition, FIG. 34 shows luminance-current efficiency characteristics. In addition, FIG. 35 shows luminance vs. external quantum efficiency characteristics. In addition, FIG. 36 shows an emission spectrum when a current of 1 mA is passed. 36 that light emission of the light-emitting element 3 is Ir (tppr) ₂ (acac). The CIE chromaticity coordinates of the light-emitting element 3 are (x, y) = (0.67, 0.34) when the luminance is 1000 cd / m ² , and the light emission of the light-emitting element 3 is red. Further, as can be seen from FIG. 35, it can be seen that the light-emitting element 3 exhibits high external quantum efficiency. In particular, it can be seen that the light-emitting element 3 exhibits a higher external quantum efficiency than the light-emitting element 1 manufactured in Example 1. The light-emitting element 3 uses the organometallic complex and zinc complex of the present invention as the light emitting layer, and it is considered that higher external quantum efficiency can be realized by using the organometallic complex and zinc complex of the present invention.

  FIG. 34 shows that the light-emitting element 3 has high luminous efficiency. FIG. 33 also shows that the voltage for obtaining a certain luminance is reduced. Therefore, it can be seen that the power consumption of the light emitting element 3 is small.

In this example, materials used in other examples will be described.

≪Example of BPAPQ synthesis≫
In this synthesis example, a method for synthesizing 2,3-bis {4- [N- (4-biphenylyl) -N-phenylamino] phenyl} quinoxaline (abbreviation: BPAPQ) represented by the following structural formula (201) will be described. To do.

[Step 1]
A method for synthesizing 2,3-bis (4-bromophenyl) quinoxaline will be described. A synthesis scheme of 2,3-bis (4-bromophenyl) quinoxaline is shown in (D-1).

  Under a nitrogen atmosphere, a chloroform solution (200 mL) of 30.0 g (81.5 mmol) of 4,4′-dibromobenzyl and 9.00 g (83.2 mmol) of o-phenylenediamine was heated to reflux at 80 ° C. for 3 hours. After the reaction solution was cooled to room temperature, the reaction solution was washed with water. The aqueous layer was extracted with chloroform, combined with the organic layer, washed with saturated brine, and the organic layer was further dried over magnesium sulfate. Filtration and concentration were performed to obtain 33 g of a target product, 2,3-bis (4-bromophenyl) quinoxaline, as a white solid in a yield of 92%.

[Step 2]
A method for synthesizing N- (4-biphenylyl) -N-phenylamine will be described. A synthesis scheme of N- (4-biphenylyl) -N-phenylamine is shown in (D-2).

  Under nitrogen atmosphere, xylene suspension of 20.0 g (85.8 mmol) of 4-bromobiphenyl, 16.0 g (172 mmol) of aniline, 0.19 g (0.858 mmol) of palladium acetate, and 23.7 g (172 mmol) of potassium carbonate ( To 150 mL), 5.2 g (2.5 mmol) of tri-tert-butylphosphine (10% hexane solution) was added and refluxed at 120 ° C. for 10 hours. After completion of the reaction, the reaction mixture was washed with water, and the aqueous layer was extracted with toluene. The toluene layer and the organic layer were combined, washed with saturated brine, and dried over magnesium sulfate. After filtration and concentration, the residue was purified by silica gel column chromatography (developing solvent: toluene) and concentrated to give 13.5 g of N-phenyl-N- (4-phenyl) phenylamine as a white solid in a yield of 64%. Obtained.

[Step 3]
A method for synthesizing 2,3-bis {4- [N- (4-biphenylyl) -N-phenylamino] phenyl} quinoxaline (hereinafter referred to as BPAPQ) will be described. A synthesis scheme of BPAPQ is shown in (D-3).

  Under a nitrogen atmosphere, 2,3-bis (4-bromophenyl) quinoxaline 5.0 g (11.4 mmol), N- (4-biphenylyl) -N-phenylamine 6.1 g (25.0 mmol), bis (dibenzylidene) Acetone) 0.33 g (0.58 mmol) of palladium and 5.5 g (56.8 mmol) of tert-butoxy sodium in a toluene suspension (80 mL) 1.2 g (0% hexane solution) of tri-tert-butylphosphine (10% hexane solution) .58 mmol) was added and heated at 80 ° C. for 7 hours. After completion of the reaction, the reaction solution was cooled to room temperature, and the precipitate was filtered. The filtrate was dissolved again in toluene, this solution was filtered using Celite, Florisil, and alumina, and the filtrate was concentrated. The residue was recrystallized from chloroform-hexane to obtain 8.1 g of BPAPQ as a yellow solid in a yield of 78%.

Analysis results of BPAPQ by proton nuclear magnetic resonance spectroscopy ( ¹ H-NMR) were as follows. ¹ H-NMR (300 MHz, CDCl ₃ ); δ = 8.16-8.13 (m, 2H), 7.75-7.72 (m, 2H), 7.58-7.04 (m, 36H) ). FIG. 23A shows an NMR chart of BPAPQ, and FIG. 23B shows an enlarged NMR chart of a portion of 6 to 9 ppm.

≪Synthesis example of YGAO11≫
In this synthesis example, the oxadiazole derivative of the present invention represented by the following structural formula (202), 4- (9H-carbazol-9-yl) -4 ′-(5-phenyl-1,3,4-oxa A synthesis example of diazol-2-yl) triphenylamine) (abbreviation: YGAO11) is specifically exemplified.

<Step 1; Synthesis of 2- (4-bromophenyl) -5-phenyl-1,3,4-oxadiazole (abbreviation: O11Br)>
In Step 1, O11Br was synthesized according to the following procedures (i) to (iii).

(I) Synthesis of 4-bromobenzohydrazide First, 3.0 g (13.9 mmol) of methyl-4-bromobenzoate was placed in a 100 mL three-necked flask, 10 mL of ethanol was added and stirred, and then 4.0 mL of hydrazine monohydrate. And heated and stirred at 78 ° C. for 5 hours. The obtained solid was washed with water and collected by suction filtration to obtain 2.0 g of a white solid of 4-bromobenzohydrazide as a target product (yield 67%).

(Ii) Synthesis of 1-benzoyl-2- (4-bromobenzoyl) hydrazine Next, 2.0 g (13.9 mmol) of 4-bromobenzohydrazide obtained in (i) above was placed in a 300 mL three-necked flask, and N- After adding 7 mL of methyl-2-pyrrolidone (abbreviation: NMP) and stirring, a mixture of 2.5 mL of N-methyl-2-pyrrolidone and 2.5 mL (21.5 mmol) of benzoyl chloride was added dropwise with a 50 mL dropping funnel, Stir at 0 ° C. for 3 hours. The obtained solid was washed with water and an aqueous sodium carbonate solution in this order, and collected by suction filtration. When recrystallization was performed with acetone, 3.6 g of a white solid of 1-benzoyl-2- (4-bromobenzoyl) hydrazine as a target product was obtained (yield 80%).

(Iii) Synthesis of O11Br Further, 15 g (47 mmol) of 1-benzoyl-2- (4-bromobenzoyl) hydrazine obtained by the method shown in (ii) above was placed in a 200 mL three-necked flask, and 100 mL of phosphoryl chloride was added, The mixture was heated and stirred at 100 ° C. for 5 hours. After the reaction, phosphoryl chloride was completely distilled off, and the resulting solid was washed with water and an aqueous sodium carbonate solution in this order, and collected by suction filtration. When recrystallization was performed with methanol, 13 g of a white solid of O11Br, which was the target product of Step 1, was obtained (yield 89%). The synthesis scheme of Step 1 described above is shown in the following scheme (E-1).

<Step 2; Synthesis of 4- (9H-carbazol-9-yl) diphenylamine (abbreviation: YGA)>
In Step 2, YGA was synthesized according to the following procedures (i) to (ii).

(I) Synthesis of 9- (4-bromophenyl) carbazole First, 56 g (240 mmol) of p-dibromobenzene, 31 g (180 mmol) of carbazole, 4.6 g (24 mmol) of copper iodide, 66 g (480 mmol) of potassium carbonate, 18- 2.1 g (8 mmol) of crown-6-ether was placed in a 300 mL three-necked flask, purged with nitrogen, 8 mL of N, N′-dimethylpropylene urea (abbreviation: DMPU) was added, and the mixture was stirred at 180 ° C. for 6 hours. The reaction mixture was cooled to room temperature, and the precipitate was removed by suction filtration. The filtrate was washed with diluted hydrochloric acid, saturated aqueous sodium hydrogen carbonate solution and saturated brine in that order, and then dried over magnesium sulfate. After drying, the solution is naturally filtered and concentrated. The resulting oily substance is purified by silica gel column chromatography (hexane: ethyl acetate = 9: 1) and recrystallized from chloroform and hexane to obtain the desired product. 21 g of a light brown plate crystal of 9- (4-bromophenyl) carbazole was obtained (yield 35%).

(Ii) Synthesis of YGA Next, 5.4 g (17 mmol) of 9- (4-bromophenyl) carbazole obtained in (i) above, 1.8 mL (20 mmol) of aniline, bis (dibenzylideneacetone) palladium (0) 0.1 g (0.2 mmol) and 3.9 g (40 mmol) of sodium tert-butoxide were placed in a 200 mL three-necked flask and replaced with nitrogen, and 0.1 mL of 10% hexane solution of tri (tert-butyl) phosphine and 50 mL of toluene were added. , And stirred at 80 ° C. for 6 hours. The reaction mixture was filtered through Florisil, Celite, and alumina, and the filtrate was washed with water and saturated brine, and then dried over magnesium sulfate. After drying, the solution was naturally filtered and then concentrated, and the resulting oil was purified by silica gel column chromatography (hexane: ethyl acetate = 9: 1). 1 g was obtained (yield 73%). The synthesis scheme of Step 2 described above is shown in the following scheme (E-2).

<Step 3; Synthesis of 4- (9H-carbazol-9-yl) -4 ′-(5-phenyl-1,3,4-oxadiazol-2-yl) triphenylamine) (abbreviation: YGAO11)>
O11Br (3.0 g, 10.0 mmol) obtained in Step 1, YGA (3.4 g, 10.0 mmol) obtained in Step 2, and sodium tert-butoxide (1.9 g, 19.9 mmol) were placed in a 100 mL three-necked flask and purged with nitrogen. , 45 mL of toluene, 0.3 mL of 10% hexane solution of tri (tert-butyl) phosphine, and 0.3 g (0.6 mmol) of bis (dibenzylideneacetone) palladium (0) were added, and the mixture was heated and stirred at 120 ° C. for 5 hours. After the reaction, the mixture was filtered through celite, and the filtrate was washed with water and dried over magnesium sulfate. After drying, the solution was filtered and the filtrate was concentrated. The obtained solid was dissolved in toluene and purified by silica column chromatography. Column purification was performed by first using toluene as a developing solvent and then using a mixed solvent of toluene: ethyl acetate = 1: 1 as a developing solvent. When recrystallization was performed with chloroform and hexane, 4.7 g of a light yellow solid of YGAO11, which was the target product of Synthesis Example 1, was obtained (yield 85%). The synthesis scheme of Step 3 described above is shown in the following scheme (E-3).

In addition, the analysis result by the nuclear magnetic resonance spectroscopy (< ¹ > H-NMR) of obtained YGAO11 is shown below. A ¹ H-NMR chart is shown in FIG. 37 (a), and an enlarged view thereof is shown in FIG. 37 (b). From this, it was found that YGAO11 represented by the above structural formula (202) was obtained in this synthesis example.

¹ H-NMR (CDCl ₃ , 300 MHz): δ = 7.14-7.53 (m, 19H), δ = 8.03 (d, J = 8.7, 2H), δ = 8.11-8 .15 (m, 4H)

Further, sublimation purification of the obtained YGAO11 was performed by a train sublimation method. The sublimation purification was performed at 265 ° C. for 12 hours under a reduced pressure of 7 Pa with an argon flow rate of 3 mL / min. When sublimation purification was performed on 4.5 g of YGAO11, the yield was 3.4 g and the yield was 76%.

  The optimum molecular structure of YGA011 in the ground state was calculated by B3LYP / 6-311 (d, p) of density functional theory (DFT). The DFT has better calculation accuracy than the Hartree-Fock (HF) method that does not consider electron correlation, and the calculation cost is lower than the perturbation method (MP) method, which is the same level of calculation accuracy. Adopted. The calculation was performed using a high performance computer (HPC) (manufactured by SGI, Altix 3700 DX). By applying the time-dependent density functional theory (TDDFT) B3LYP / 6-311 (d, p) in the molecular structure optimized by DFT, the singlet excitation energy (energy gap) of YGA011 was calculated. Singlet excitation energy was calculated to be 3.18 eV. The triplet excitation energy of YGAO11 was calculated to be 2.53 eV. From the above results, it can be seen that the oxadiazole derivative of the present invention is a substance having a large excitation energy. In particular, it can be seen that the substance has a large triplet excitation energy.

<< Synthesis Example 7 >>
In this synthesis example 7, in the organometallic complex represented by the general formula (G12) of the embodiment, R ⁴ and R ⁹ are methyl groups, and R ³ and R ^{5 to} R ⁸ and R ^{10 to} R1 ¹ are hydrogen. An organometallic complex of the present invention represented by the structural formula (45), wherein Ar ¹ is a 3-fluorophenyl group, and L is a ligand represented by the structural formula (L1), (acetylacetonato ) Illustrative examples of the synthesis of bis [5- (3-fluorophenyl) -2,3-di-p-tolylpyrazinato] iridium (III) (abbreviation: [Ir (Mdppr-3FP) ₂ (acac)]) To do.

<Step 1; Synthesis of 5- (3-fluorophenyl) -2,3-di-p-tolylpyrazine (abbreviation: HMdppr-3FP)>
First, 11 mL of n-butyllithium hexane solution (1.58 mol / L) was added dropwise to a mixed solution of 2.86 g of 3-bromofluorobenzene and 16 mL of tetrahydrofuran in a nitrogen atmosphere at −78 ° C. The mixture was stirred at −78 ° C. for 2 hours. The obtained solution was added dropwise to an ice-cooled mixed solution of 3.53 g of 2,3-di-p-tolylpyrazine, which is an intermediate obtained in Step 1 of Synthesis Example 4, and 25 mL of tetrahydrofuran, and brought to room temperature. And stirred for 12 hours. Water was added to this mixture, and the organic layer was extracted with dichloromethane. The obtained organic layer was washed with water and dried over anhydrous magnesium sulfate. To the solution after drying, an excess of active manganese dioxide was added and filtered. After the solvent of this solution was distilled off, the residue obtained by distillation was purified by silica gel column chromatography using dichloromethane as a developing solvent to obtain the target pyrazine derivative HMdppr-3FP (orange powder, 8%). The synthesis scheme of Step 1 is shown in (a-6) below.

<Step 2; Di-μ-chloro-bis {bis [5- (3-fluorophenyl) -2,3-di-p-tolylpyrazinato] iridium (III)} (abbreviation: [Ir (Mdppr-3FP) ₂ Cl ] ₂ ) Synthesis>
Next, 12 mL of 2-ethoxyethanol and 4 mL of water, 0.14 g of the pyrazine derivative HMdppr-3FP obtained in Step 1 above, 0.06 g of iridium chloride hydrate (IrCl ₃ · H ₂ O) (manufactured by Sigma-Aldrich) The flask was placed in a recovery flask equipped with a reflux tube, and the atmosphere in the flask was replaced with argon. Then, the microwave (2.45 GHz 100W) was irradiated for 30 minutes, and it was made to react. The red powder precipitated from the reaction solution was filtered and washed with ethanol to obtain a binuclear complex [Ir (Mdppr-3FP) ₂ Cl] ₂ (yield 16%). Note that a microwave synthesizer (Discovery manufactured by CEM) was used for microwave irradiation. Moreover, the synthesis scheme of Step 2 is shown in (b-6) below.

<Step 3; (acetylacetonato) bis [5- (3-fluorophenyl) -2,3-di-p-tolylpyrazinato] iridium (III) (abbreviation: [Ir (Mdppr-3FP) ₂ (acac)] Synthesis>
Further, 3 mL of 2-ethoxyethanol, 0.03 g of the binuclear complex [Ir (Mdppr-3FP) ₂ Cl] ₂ obtained in Step 2 above, 0.005 mL of acetylacetone and 0.02 g of sodium carbonate were added to an eggplant flask equipped with a reflux tube. The flask was purged with argon. Thereafter, microwaves (2.45 GHz 100 W) were irradiated for 15 minutes to react. The reaction solution was filtered, and the solvent of the obtained filtrate was distilled off. The residue obtained by evaporation was purified by silica gel column chromatography using dichloromethane as a developing solvent to obtain the organometallic complex [Ir (Mdppr-3FP) ₂ (acac)] of the present invention (red powder, Yield 50%). The synthesis scheme of Step 3 is shown in (c-6) below.

In addition, the analysis result by the nuclear magnetic resonance spectroscopy (< ¹ > H-NMR) of the red powder obtained at the said step 3 is shown below. A ¹ H-NMR chart is shown in FIG. From this, it was found that, in Synthesis Example 7, the organometallic complex [Ir (Mdppr-3FP) ₂ (acac)] of the present invention represented by the above structural formula (45) was obtained.

¹ H-NMR. δ (CDCl ₃ ): 1.92 (s, 6H), 2.03 (s, 6H), 2.49 (s, 6H), 5.36 (s, 1H), 6.27 (s, 2H) 6.37 (dd, 2H), 6.90 (d, 2H), 7.15 (m, 2H), 7.34 (d, 4H), 7.46 (m, 2H), 7.71 ( d, 4H), 7.82 (m, 4H), 8.87 (s, 2H).

Next, the absorption spectrum of [Ir (Mdppr-3FP) ₂ (acac)] was measured. The absorption spectrum was measured at room temperature using a UV-visible spectrophotometer (model V550 manufactured by JASCO Corporation) and a dichloromethane solution (0.010 mmol / L). In addition, an emission spectrum of [Ir (Mdppr-3FP) ₂ (acac)] was measured. The emission spectrum was measured at room temperature using a fluorometer (FS920, manufactured by Hamamatsu Photonics) using a degassed dichloromethane solution (0.35 mmol / L). The measurement results are shown in FIG. The horizontal axis represents wavelength, and the vertical axis represents molar extinction coefficient and emission intensity. The excitation wavelength was 468 nm.

As shown in FIG. 39, the organometallic complex [Ir (Mdppr-3FP) ₂ (acac)] of the present invention has an emission peak at 627 nm, and red light emission was observed from the solution.

4A and 4B illustrate a light-emitting element of the present invention. 4A and 4B illustrate a light-emitting element of the present invention. 4A and 4B illustrate a light-emitting element of the present invention. 4A and 4B illustrate a light-emitting device of the present invention. 4A and 4B illustrate a light-emitting device of the present invention. 8A and 8B each illustrate an electronic device of the invention. 8A and 8B each illustrate an electronic device of the invention. The figure explaining the illuminating device of this invention. The figure explaining the illuminating device of this invention. Shows a ¹ H-NMR chart of (acetylacetonato) bis (2,3,5-triphenylpyrazinato) iridium (III). The figure which shows the absorption spectrum and emission spectrum of (acetylacetonato) bis (2,3,5-triphenyl pyrazinato) iridium (III). 3A and 3B illustrate a light-emitting element of an example. FIG. 6 shows current density-luminance characteristics of the light-emitting element manufactured in Example 2. FIG. 11 shows voltage-luminance characteristics of the light-emitting element manufactured in Example 2. FIG. 11 shows luminance-current efficiency characteristics of the light-emitting element manufactured in Example 2. FIG. 11 shows luminance vs. external quantum efficiency characteristics of the light-emitting element manufactured in Example 2. FIG. 6 shows an emission spectrum of the light-emitting element manufactured in Example 2. FIG. 11 shows current density-luminance characteristics of the light-emitting element manufactured in Example 3. FIG. 11 shows voltage-luminance characteristics of the light-emitting element manufactured in Example 3. FIG. 11 shows luminance-current efficiency characteristics of the light-emitting element manufactured in Example 3. FIG. 11 shows luminance vs. external quantum efficiency characteristics of the light-emitting element manufactured in Example 3. FIG. 6 shows an emission spectrum of the light-emitting element manufactured in Example 3. 2,3-bis {4- [N- (4- biphenylyl) -N- phenylamino] phenyl} shows a ¹ H-NMR chart of quinoxaline. Shows a ¹ H-NMR chart of (acetylacetonato) bis (2,3-diphenyl -5-p-Torirupirajinato) iridium (III). The figure which shows the absorption spectrum and emission spectrum of (acetylacetonato) bis (2,3-diphenyl-5-p-tolylpyrazinato) iridium (III). Shows a ¹ H-NMR chart of (acetylacetonato) bis (5-phenyl-2,3--p- Torirupirajinato) iridium (III). The figure which shows the absorption spectrum and emission spectrum of (acetylacetonato) bis (5-phenyl-2,3-di-p-tolylpyrazinato) iridium (III). Shows a ¹ H-NMR chart of bis (2,3,5-triphenylpyrazinato) (Pikorinato) iridium (III). The figure which shows the absorption spectrum and emission spectrum of bis (2,3,5- triphenyl pyrazinato) (picolinato) iridium (III). Shows a ¹ H-NMR chart of (acetylacetonato) bis (3-methyl-2,5-diphenylpyrazoline) iridium (III). The figure which shows the absorption spectrum and emission spectrum of (acetylacetonato) bis (3-methyl-2,5-diphenylpyrazinato) iridium (III). FIG. 11 shows current density-luminance characteristics of the light-emitting element manufactured in Example 8. FIG. 11 shows voltage-luminance characteristics of the light-emitting element manufactured in Example 8. FIG. 11 shows luminance-current efficiency characteristics of the light-emitting element manufactured in Example 8. FIG. 11 shows luminance vs. external quantum efficiency characteristics of the light-emitting element manufactured in Example 8. FIG. 10 shows an emission spectrum of the light-emitting element manufactured in Example 8. 4-(9H-carbazol-9-yl) -4 '- shows a ¹ H-NMR chart of (5-phenyl-1,3,4-oxadiazol-2-yl) triphenylamine). Shows a ¹ H-NMR chart of (acetylacetonato) bis [5- (3-fluorophenyl) -2,3-di -p- Torirupirajinato] iridium (III). The figure which shows the absorption spectrum and emission spectrum of (acetylacetonato) bis [5- (3-fluorophenyl) -2,3-di-p-tolylpyrazinato] iridium (III).

Explanation of symbols

101 first electrode 102 second electrode 111 hole injection layer 112 hole transport layer 113 light emitting layer 114 electron transport layer 115 electron injection layer 201 first electrode 202 second electrode 211 hole injection layer 212 hole transport Layer 213 Light emitting layer 214 Separation layer 215 Light emitting layer 216 Electron transport layer 217 Electron injection layer 301 First electrode 302 Second electrode 311 Hole injection layer 312 Hole transport layer 313 Light emission layer 314 Electron transport layer 315 N layer 321 P Layer 323 Light emitting layer 325 Electron injection layer 601 Source side driving circuit 602 Pixel portion 603 Gate side driving circuit 604 Sealing substrate 605 Sealing material 607 Space 608 Wiring 609 FPC (flexible printed circuit)
610 Element substrate 611 TFT for switching
612 Current control TFT
613 First electrode 614 Insulator 616 Layer containing light emitting substance 617 Second electrode 618 Light emitting element 623 n-channel TFT
624 p-channel TFT
901 Case 902 Liquid crystal layer 903 Backlight 904 Case 905 Driver IC
906 Terminal 951 Substrate 952 Electrode 953 Insulating layer 954 Partition layer 955 Layer containing light emitting material 956 Electrode 2001 Housing 2002 Light source 2101 Glass substrate 2102 First electrode 2103 Layer containing composite material 2104 Hole transport layer 2105 Light emitting layer 2106 Electron transport Layer 2107 Electron injection layer 2108 Second electrode 3001 Lighting device 3002 Television apparatus 9101 Housing 9102 Support base 9103 Display unit 9104 Speaker unit 9105 Video input terminal 9201 Body 9202 Housing 9203 Display unit 9204 Keyboard 9205 External connection port 9206 Pointing device 9401 Main body 9402 Housing 9403 Display unit 9404 Audio input unit 9405 Audio output unit 9406 Operation key 9407 External connection port 9408 Antenna 9501 Main unit 9502 Display unit 950 3 Housing 9504 External connection port 9505 Remote control receiving unit 9506 Image receiving unit 9507 Battery 9508 Audio input unit 9509 Operation key 9510 Eyepiece unit

Claims (32)

An organometallic complex having a structure represented by General Formula (G1).

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms. Z represents hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, or 6 carbon atoms. and an aryl group 25. _{Further, a} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. also, ^{R 1} represents hydrogen or an alkyl group having 1 to 4 carbon atoms, or from 1 to carbon atoms, 4 represents an alkoxy group of 4. M is a central metal and represents a Group 9 element or a Group 10 element.) An organometallic complex having a structure represented by General Formula (G2).

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms, A _r ¹ and A _r ² represent an aryl group having 6 to 25 carbon atoms, and R ¹ represents hydrogen or carbon. It represents either an alkyl group having 1 to 4 or an alkoxy group having 1 to 4 carbon atoms, and M is a central metal and represents a Group 9 element or a Group 10 element. An organometallic complex having a structure represented by General Formula (G3).

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} represents hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms R ^{3 to} R ¹¹ are each hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, an aryl group having 6 to 12 carbon atoms, a halogen group, or trifluoro (M represents a methyl group, and M represents a central metal and represents a Group 9 element or a Group 10 element.) An organometallic complex having a structure represented by General Formula (G4).

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} represents hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms M is a central metal and represents a Group 9 element or a Group 10 element.) An organometallic complex having a structure represented by General Formula (G5).

(In the formula, R ¹ represents either hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms. Also, R ^{12 to} R ¹⁶ are each hydrogen or 1 carbon atom. Represents an alkyl group of ˜4, an alkoxy group of 1 to 4 carbon atoms, an aryl group of 6 to 12 carbon atoms, a halogen group, or a trifluoromethyl group, and M is a central metal, (Represents a Group 9 element or a Group 10 element.) 6. The organometallic complex according to claim 5, wherein R ^{12 to} R ¹⁶ are hydrogen, a fluoro group, or a trifluoromethyl group. An organometallic complex having a structure represented by General Formula (G6).

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms. _{Further, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} and ^{R 2} are hydrogen or, It represents either an alkyl group having 1 to 4 carbon atoms or an alkoxy group having 1 to 4 carbon atoms, and M is a central metal and represents a Group 9 element or a Group 10 element. An organometallic complex having a structure represented by General Formula (G7).

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} and ^{R 2} is hydrogen or an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, R ^{3 to} R ⁶ each represent hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, an aryl group having 6 to 12 carbon atoms, or a halogen atom Represents either a group or a trifluoromethyl group, and M is a central metal and represents a Group 9 element or a Group 10 element.) An organometallic complex having a structure represented by General Formula (G8).

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} and ^{R 2} is hydrogen or an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, M is a central metal and represents a Group 9 element or a Group 10 element.) An organometallic complex having a structure represented by General Formula (G9).

(Wherein R ¹ and R ² each represent hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms. Also, R ^{12 to} R ¹⁶ are each hydrogen. Or an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, an aryl group having 6 to 12 carbon atoms, a halogen group, or a trifluoromethyl group, and M represents (It is a central metal and represents a Group 9 element or a Group 10 element.) The organometallic complex according to claim 10, wherein R ^{12 to} R ¹⁶ are hydrogen, a fluoro group, or a trifluoromethyl group. In any one of Claims 1 to 11,
The organometallic complex, wherein R ¹ is hydrogen or a methyl group. An organometallic complex having a structure represented by the general formula (G10).

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms. Z represents hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, or 6 carbon atoms. and an aryl group 25. _{Further, a} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. also, ^{R 1} represents hydrogen or an alkyl group having 1 to 4 carbon atoms, or from 1 to carbon atoms, And M represents a central metal, a Group 9 element or a Group 10 element, L represents a monoanionic ligand, and the center. (When the metal is a Group 9 element, n = 2, and when the metal is a Group 10 element, n = 1.) An organometallic complex having a structure represented by the general formula (G11).

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms. A _r ¹ and A _r ² each represents an aryl group having 6 to 25 carbon atoms. R ¹ represents hydrogen, Or an alkyl group having 1 to 4 carbon atoms or an alkoxy group having 1 to 4 carbon atoms, M is a central metal, and represents a Group 9 element or a Group 10 element. Represents a monoanionic ligand, and n = 2 when the central metal is a Group 9 element and n = 1 when the central metal is a Group 10 element.) An organometallic complex having a structure represented by General Formula (G12).

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} represents hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms R ^{3 to} R ¹¹ are each hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, an aryl group having 6 to 12 carbon atoms, a halogen group, or trifluoro M represents a methyl group, M represents a central metal, a Group 9 element or a Group 10 element, L represents a monoanionic ligand, and the central metal represents (In the case of a Group 9 element, n = 2, and in the case of a Group 10 element, n = 1.) An organometallic complex having a structure represented by the general formula (G13).

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} represents hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms M is a central metal and represents a group 9 element or a group 10 element, L represents a monoanionic ligand, and when the central metal is a group 9 element, (n = 2 and n = 1 when a Group 10 element) An organometallic complex having a structure represented by the general formula (G14).

(In the formula, R ¹ represents either hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms. Also, R ^{12 to} R ¹⁶ are each hydrogen or 1 carbon atom. Represents an alkyl group of ˜4, an alkoxy group of 1 to 4 carbon atoms, an aryl group of 6 to 12 carbon atoms, a halogen group, or a trifluoromethyl group, and M is a central metal, Represents a Group 9 element or a Group 10 element, L represents a monoanionic ligand, and when the central metal is a Group 9 element, n = 2; In this case, n = 1.) The organometallic complex according to claim 17, wherein R ^{12 to} R ¹⁶ are hydrogen, a fluoro group, or a trifluoromethyl group. An organometallic complex having a structure represented by the general formula (G15).

(In the formula, A represents an aromatic hydrocarbon group having 6 to 25 carbon atoms. _{Further, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} and ^{R 2} are hydrogen or carbon atoms, Represents an alkyl group having 1 to 4 or an alkoxy group having 1 to 4 carbon atoms, M represents a central metal, and represents a Group 9 element or a Group 10 element, and L represents a monoanion. In addition, when the central metal is a Group 9 element, n = 2, and when the central metal is a Group 10 element, n = 1.) An organometallic complex having a structure represented by the general formula (G16).

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} and ^{R 2} is hydrogen or an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, R ^{3 to} R ⁶ each represent hydrogen, an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, an aryl group having 6 to 12 carbon atoms, or a halogen atom Represents a group or a trifluoromethyl group, M represents a central metal, represents a Group 9 element or a Group 10 element, and L represents a monoanionic ligand. When the central metal is a Group 9 element, n = 2, and when the central metal is a Group 10 element, n = 1.) An organometallic complex having a structure represented by the general formula (G17).

_{(Wherein, A} ^{r 1} represents an aryl group having 6 to 25 carbon atoms. Also, ^{R 1} and ^{R 2} is hydrogen or an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, M represents a central metal and represents a Group 9 element or a Group 10 element, L represents a monoanionic ligand, and the central metal represents a 9th element. (When a group element, n = 2, and when a group 10 element, n = 1.) An organometallic complex having a structure represented by the general formula (G18).

(Wherein R ¹ and R ² each represent hydrogen, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms. Also, R ^{12 to} R ¹⁶ are each hydrogen. Or an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, an aryl group having 6 to 12 carbon atoms, a halogen group, or a trifluoromethyl group, and M represents It is a central metal and represents a Group 9 element or a Group 10 element, L represents a monoanionic ligand, and n = 2 when the central metal is a Group 9 element. In the case of a Group 10 element, n = 1.) 23. The organometallic complex according to claim 22, wherein R ^{12 to} R ¹⁶ are hydrogen, a fluoro group, or a trifluoromethyl group. 24. In any one of claims 13 to 23,
The organometallic complex, wherein R ¹ is hydrogen or a methyl group. 25. In any one of claims 13 to 24,
The monoanionic ligand is a monoanionic bidentate chelate ligand having a beta diketone structure, a monoanionic bidentate chelate ligand having a carboxyl group, or a monoanion having a phenolic hydroxyl group An organometallic complex, which is either a monodentate bidentate chelate ligand or a monoanionic bidentate chelate ligand in which two coordination elements are both nitrogen. 25. In any one of claims 13 to 24,
The organic metal complex, wherein the monoanionic ligand is a monoanionic ligand represented by the following structural formulas (L1) to (L8).

In any one of Claims 1 to 26,
An organometallic complex, wherein the central metal is iridium or platinum.   A light emitting material containing the organometallic complex according to any one of claims 1 to 27.   A light-emitting element including the organometallic complex according to any one of claims 1 to 27.   A light-emitting element containing the organometallic complex according to any one of claims 1 to 27 as a light-emitting substance. A light emitting device comprising: the light emitting element according to claim 29 or 30; and a control unit that controls light emission of the light emitting element. Having a display,