JPH0657527A - Polyolefinic tow - Google Patents
Polyolefinic towInfo
- Publication number
- JPH0657527A JPH0657527A JP4214296A JP21429692A JPH0657527A JP H0657527 A JPH0657527 A JP H0657527A JP 4214296 A JP4214296 A JP 4214296A JP 21429692 A JP21429692 A JP 21429692A JP H0657527 A JPH0657527 A JP H0657527A
- Authority
- JP
- Japan
- Prior art keywords
- tow
- plug
- polyolefin
- weight
- tobacco
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、ポリオレフィンからな
るフィラメントトウに関し、さらに詳しくは喫味特性が
良好であり、生産性にも優れたタバコ煙用フィルタ（以
下、タバコフィルタという）の素材として好適なポリオ
レフィントウに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a filament tow made of polyolefin, and more specifically, it is suitable as a material for a cigarette smoke filter (hereinafter, referred to as a cigarette filter) having good taste characteristics and excellent productivity. It relates to a polyolefin tow.
【０００２】[0002]
【従来の技術】一般にタバコフィルタの素材としては、
紙やパルプ等の短繊維を均一に分散させた素材や、セル
ロースアセテートやポリオレフィン等の捲縮繊維からな
るトウを素材としたものが実用化されている。中でも、
セルロースアセテートトウ（以下、アセテートトウとい
う）を素材としたタバコフィルタは、トリアセチン等の
ような取扱い容易な可塑剤が使用可能であることより、
細い繊度の繊維を単位充填重量当たり多く使用して適度
な通気抵抗を維持しながらも、なおかつ適度な硬度を保
持することができるので、該タバコフィルタを手にした
ときおよび口にくわえたときの感触がよく、該タバコフ
ィルタを吸ったときに無理なく吸うことができ、かつ吸
いごこちがよいという優れた喫味特性を有している点で
も最も広く用いられている。2. Description of the Related Art Generally, as a material for a cigarette filter,
A material in which short fibers such as paper and pulp are uniformly dispersed and a tow including crimped fibers such as cellulose acetate and polyolefin have been put into practical use. Above all,
Tobacco filters made from cellulose acetate tow (hereinafter referred to as acetate tow) can be used with easy-to-handle plasticizers such as triacetin.
While maintaining appropriate ventilation resistance by using a large amount of fine fine fibers per unit weight, it is possible to maintain appropriate hardness, so that when the cigarette filter is held in the hand and held in the mouth. It is the most widely used in that it has a good feel, it can be reasonably smoked when the cigarette filter is smoked, and it has excellent taste characteristics that it is comfortable to suck.
【０００３】タバコの喫味特性は、フィルタ硬度とフィ
ルタの通気抵抗とに大きく依存する。喫味特性を良好に
するには、フィルタを指で挟んだときつぶれることな
く、またフィルタを口にくわえたとき、くわえごこちの
よいフィルタ硬度と、フィルタを吸ったとき、無理なく
吸うことができ、かつ吸いごごちがよい通気抵抗とを必
要とし、良好な喫味特性は上述のフィルタ硬度とフィル
タ通気抵抗をバランスよく保つことによって得られる。The taste characteristics of cigarettes largely depend on the filter hardness and the ventilation resistance of the filter. To improve the taste characteristics, the filter does not collapse when pinched with fingers, and when the filter is held in the mouth, the filter hardness is comfortable to hold, and when the filter is sucked, it can be sucked reasonably, In addition, it requires a breathing resistance that is good for sucking, and good taste characteristics can be obtained by keeping the above-described filter hardness and filter ventilation resistance in a well-balanced manner.
【０００４】また、タバコフィルタは、通常プラグマシ
ンを用いて製造される。このプラグマシンはトウを開繊
し、一定の径になるようにトウを集束し、円柱状のトウ
を装置上に走行させ、該トウの円周上に紙を巻いてタバ
コ煙用フィルタプラグ（以下、タバコプラグという）を
製造するものである。このタバコプラグを所定の長さに
カッティングすることによりタバコフィルタが得られる
が、このような製造工程においてもアセテートトウは、
捲縮弾性が小さいのでトウの均一開繊が容易であり、ま
た、アセテートトウを構成する単糸繊維は強度が低いの
で、装置上で多少の単糸繊維の引っ掛かりが起こったと
しても、容易に切断されるので何らプラグ生産工程上の
支障にならないことから、タバコフィルタの生産に適し
ており、プラグ生産速度が４００ｍ／ｍｉｎ以上という
高速生産も可能である。Further, the cigarette filter is usually manufactured by using a plug machine. This plug machine opens the tow, bundles the tows into a certain diameter, runs a columnar tow on the device, wraps paper around the circumference of the tow, and filters the cigarette smoke filter plug ( Hereinafter, referred to as a cigarette plug). A tobacco filter can be obtained by cutting this tobacco plug into a predetermined length.
Since the crimp elasticity is small, uniform opening of the tow is easy, and the strength of the single yarn fibers that make up the acetate tow is low, so even if some single yarn fibers are caught on the device, they can be easily Since it does not hinder the plug production process because it is cut, it is suitable for cigarette filter production, and high-speed production with a plug production speed of 400 m / min or more is also possible.
【０００５】これに対し、ポリオレフィン等の捲縮繊維
からなるトウ（以下、ポリオレフィントウという）につ
いても、略２〜１０デニールの比較的細繊度のポリオレ
フィン繊維を、多数本集束して適度なトウ繊度とし、適
度な捲縮を付与した捲縮ポリオレフィントウとすること
により、経済性の面やアセテートトウを用いたフィルタ
とは異なる喫味特性を狙って、研究が盛んに行われてい
る。On the other hand, regarding a tow made of crimped fibers such as polyolefin (hereinafter referred to as polyolefin tow), a large number of polyolefin fibers having a relatively fineness of about 2 to 10 denier are bundled to obtain an appropriate tow fineness. However, by using a crimped polyolefin tow provided with an appropriate crimp, research has been actively conducted aiming at economic efficiency and taste characteristics different from those of a filter using acetate tow.
【０００６】しかしながら、ポリオレフィントウの場合
には、アセテートトウに対するような有効な可塑剤や接
着剤がないので、喫味特性に優れるフィルタ硬度が得ら
れない。フィルタ硬度を向上させるには、比較的太い単
糸繊維の集束体のポリオレフィントウを用いるか、ある
いは捲縮数を多く付加したポリオレフィントウを使用す
る方法が考えられるが、前者の場合は単位充填重量当た
りの単糸数が減るため、煙の遮り面積が減少して通気抵
抗が不足することになる。また、後者の場合は、捲縮弾
性が大きくなるため、プラグマシンでポリオレフィント
ウを開繊し引き伸ばし、そして巻き上げるのに大きな力
が必要とされる。しかし、大きな力で引き伸ばされた該
トウを用いて得られるタバコプラグは、常に大きな残留
収縮力を持っているため、該タバコプラグをカッティン
グしたとき、タバコプラグのカッティング面（以下、プ
ラグ端面という）でポリオレフィントウがタバコフィル
タ内部に陥入するという不良品が増大し、生産安定性が
悪化する。However, in the case of polyolefin tow, since there is no effective plasticizer or adhesive as for acetate tow, a filter hardness having excellent taste characteristics cannot be obtained. In order to improve the filter hardness, it is conceivable to use a polyolefin tow that is a bundle of relatively thick monofilament fibers, or to use a polyolefin tow with a large number of crimps. Since the number of single yarns per unit is reduced, the smoke blocking area is reduced and the ventilation resistance becomes insufficient. Further, in the latter case, since the crimp elasticity is large, a large force is required to open and stretch the polyolefin tow with a plug machine, and to wind it. However, since a tobacco plug obtained by using the tow stretched with a large force always has a large residual shrinkage force, when the tobacco plug is cut, the cutting surface of the tobacco plug (hereinafter, referred to as plug end surface) As a result, the number of defective products such as polyolefin tow invading the inside of the tobacco filter increases, and the production stability deteriorates.
【０００７】このように、従来公知のポリオレフィント
ウでは、タバコフィルタとしての基本的に必要な特性で
ある喫味特性を良好にするための硬度と通気抵抗、また
フィルタ硬度と生産安定性を同時に維持し難いという欠
点を有する。さらに、タバコプラグを製造する際、上記
の該ポリオレフィントウは、以下のような製造上の欠点
を有しているので、現在のところポリオレフィントウを
用いたときのタバコプラグ生産速度は、２００ｍ／ｍｉ
ｎがせいぜいであり、アセテートトウ並みの４００ｍ／
ｍｉｎという高速生産が安定してできていないのが実情
である。As described above, in the conventionally known polyolefin tow, the hardness and the air flow resistance, the filter hardness and the production stability for improving the taste characteristics which are basically necessary characteristics of the tobacco filter are maintained at the same time. It has the drawback of being difficult. Further, when manufacturing a tobacco plug, the above-mentioned polyolefin tow has the following manufacturing defects. Therefore, at present, the tobacco plug production rate using the polyolefin tow is 200 m / mi.
n is at most 400 m /, which is similar to acetate tow
The reality is that high-speed production of min is not stable.
【０００８】（１）アセテートトウに較べポリオレフィ
ントウは捲縮弾性が高いため、オレフィントウをプラグ
マシンによって巻き上げるとき、ポリオレフィントウの
均一開繊が困難であり、ポリオレフィントウの引き伸ば
しに必要な力も大きくなる。そのためトウの開繊斑や収
縮力も増大し、プラグぶれやプラグ巻紙にしわが発生し
易くなり、タバコプラグのメジャーリング前での直進性
が悪化し、タバコプラグの高速走行性が悪化する。 （２）プラグマシンの生産速度を高速にするほど、ポリ
オレフィントウの均一開繊性は悪化し、ポリオレフィン
トウの引き伸ばしに必要な力も増加させなくてはならな
くなる。そのため生産速度を高速にするほど、タバコフ
ィルタとしての基本的に必要な特性である喫味特性を良
好にするための硬度と通気抵抗のバランスが悪化し、同
時に得られるタバコフィルタの硬度や通気抵抗もバラツ
キの大きいものとなる。 （３）アセテートトウに較べポリオレフィントウは、構
成する単糸繊維が硬いためカッターで切断しにくく、そ
れは生産速度が高速になるほど重大な障害になる。 （４）プラグマシンの生産速度を高速にするほど、急速
なオレフィントウの引き伸ばしによるオレフィントウの
残留収縮力が大きくなり、プラグ端面の陥入が発生し易
くなる。(1) Since polyolefin tow has a higher crimp elasticity than acetate tow, it is difficult to uniformly open the polyolefin tow when the olefin tow is wound by a plug machine, and the force required for stretching the polyolefin tow is also increased. . As a result, the spread and contraction force of the tow are increased, and the blurring of the plug and the wrapping paper easily occur, the straightness of the tobacco plug before the measuring is deteriorated, and the high-speed running property of the tobacco plug is deteriorated. (2) As the production speed of the plug machine is increased, the uniform opening property of the polyolefin tow is deteriorated, and the force required for stretching the polyolefin tow must be increased. Therefore, the higher the production speed, the poorer the balance between hardness and ventilation resistance for improving the taste characteristics, which are basically necessary characteristics of a tobacco filter, and the hardness and ventilation resistance of the tobacco filter obtained at the same time. It will vary greatly. (3) Polyolefin tow is harder to cut with a cutter than the acetate tow because the constituent single-fibers are hard, which becomes a serious obstacle as the production speed increases. (4) The higher the production speed of the plug machine, the greater the residual shrinkage force of the olefin tow due to the rapid stretching of the olefin tow, and the more likely the plug end surface is invaded.
【０００９】[0009]
【発明が解決しようとする課題】本発明の目的は、フィ
ルタ硬度とフィルタ通気抵抗をバランスよく維持した喫
味特性に優れるタバコフィルタが得られ、さらに公知公
用のタバコプラグマシンを使用したとき、アセテートト
ウ並みの高速生産性を有し、しかも生産安定性に優れる
ポリオレフィントウおよび該トウを素材とするタバコフ
ィルタを提供することである。SUMMARY OF THE INVENTION An object of the present invention is to obtain a tobacco filter having excellent taste characteristics while maintaining a well-balanced filter hardness and filter ventilation resistance. Further, when a publicly known tobacco plug machine is used, acetate tow is used. It is an object of the present invention to provide a polyolefin tow having an average high-speed productivity and excellent production stability, and a tobacco filter made of the tow.
【００１０】[0010]
【課題を解決するための手段】本発明者らは鋭意研究し
た結果、特定のポリオレフィン樹脂組成物を溶融紡糸し
て得られるポリオレフィン繊維を集束して得られるトウ
に、特定の捲縮数、特定の伸度および捲縮弾性率を与え
ることにより、上記の目的を達成することに成功し本発
明を完成するに到った。Means for Solving the Problems As a result of intensive studies, the present inventors have found that a tow obtained by bundling a polyolefin fiber obtained by melt spinning a specific polyolefin resin composition has a specific crimp number and a specific crimp number. The present invention has been completed successfully and the present invention has been completed by providing the elongation and the crimping elastic modulus.
【００１１】すなわち、本発明は、ポリオレフィン１０
０重量％に対し、二酸化チタンが０．１〜１．０重量％
配合された組成物を溶融紡糸して得られるポリオレフィ
ン繊維からなるトウであって、該トウは、捲縮数が２０
〜４５山／ｉｎｃｈ、伸度が５０〜２５０％、捲縮弾性
率が８０％以下であることを特徴とするポリオレフィン
トウおよび該トウを素材とするタバコフィルタである。That is, the present invention relates to a polyolefin 10
0.1% to 1.0% by weight of titanium dioxide to 0% by weight
A tow comprising polyolefin fibers obtained by melt spinning a compounded composition, wherein the tow has a crimp number of 20.
It is a polyolefin tow and a tobacco filter made of the tow, characterized by having a pitch of up to 45 peaks / inch, an elongation of 50 to 250%, and a crimp elastic modulus of 80% or less.
【００１２】以下、本発明を詳細に説明する。本発明の
ポリオレフィントウの原料として用いるポリオレフィン
としては、ポリプロピレン、ポリエチレン、エチレン酢
酸ビニール共重合体等が利用でき、該ポリオレフィンの
中でも特に結晶性ポリプロピレンが好ましく用いられ
る。結晶性ポリプロピレンは、プロピレンの単独重合
体、プロピレンを主成分とするプロピレンとエチレンま
たは炭素数４以上のαオレフィンとの二元以上の共重合
体、またはそれらの混合物であり、共重合体の具体例と
してはエチレン・プロピレン共重合体、プロピレン・ブ
テン−１共重合体、プロピレン・ヘキセン−１共重合
体、エチレン・プロピレン・ブテン−１共重合体等の結
晶融点を有するプロピレン系共重合体が挙げられるが、
タバコフィルタの硬度と通気抵抗のバランスをよくする
には、プロピレンの単独重合体を使用するのがより好ま
しい。The present invention will be described in detail below. As the polyolefin used as the raw material of the polyolefin tow of the present invention, polypropylene, polyethylene, ethylene vinyl acetate copolymer and the like can be used, and among these polyolefins, crystalline polypropylene is particularly preferably used. Crystalline polypropylene is a homopolymer of propylene, a binary copolymer of propylene containing propylene as a main component and ethylene or an α-olefin having 4 or more carbon atoms, or a mixture thereof. Examples include ethylene / propylene copolymers, propylene / butene-1 copolymers, propylene / hexene-1 copolymers, ethylene / propylene / butene-1 copolymers, and other propylene-based copolymers having a crystalline melting point. Can be mentioned,
It is more preferable to use a propylene homopolymer in order to improve the balance between the hardness and the ventilation resistance of the tobacco filter.
【００１３】また、結晶性ポリプロピレンとしては、タ
バコフィルタの生産安定性を良好とし、ポリオレフィン
トウに適度な柔軟性を付加させることができるように、
メルトフローレイト（ＪＩＳ Ｋ ７２１０−１９７６
で測定した溶融流動指数。以下、ＭＦＲという）が１０
〜２５ｇ／１０分の範囲のものが好ましい。本発明のポ
リオレフィントウは、ポリオレフィン１００重量％に対
し、二酸化チタンが０．１〜１．０重量％配合された組
成物を溶融紡糸して得られるポリオレフィン繊維からな
るトウである。該組成物の構成成分である二酸化チタン
としては、通常プラスチックの着色剤や艶消し剤等に使
用されているルチル型あるいはアナターゼ型の、平均粒
子サイズ０．１０〜０．５０ミクロンの微細結晶構造の
ものでよいが、ポリオレフィンに対する親和性および均
一分散性や耐熱性および耐候性を配慮する上で、極性基
材で表面処理されたルチル型の平均粒子径が０．１５〜
０．３５ミクロンの範囲で、かつ非毒性で食品等級に適
合したものがより好ましい。As the crystalline polypropylene, the production stability of the tobacco filter can be improved, and the polyolefin tow can have appropriate flexibility.
Melt flow rate (JIS K 7210-1976
Melt flow index measured by. Hereinafter referred to as MFR) is 10
It is preferably in the range of -25 g / 10 minutes. The polyolefin tow of the present invention is a tow composed of a polyolefin fiber obtained by melt spinning a composition containing 0.1 to 1.0% by weight of titanium dioxide based on 100% by weight of polyolefin. Titanium dioxide, which is a constituent of the composition, is a rutile type or anatase type fine crystal structure having an average particle size of 0.10 to 0.50 micron, which is usually used as a coloring agent or a matting agent for plastics. However, in consideration of affinity for polyolefin, uniform dispersibility, heat resistance and weather resistance, the average particle diameter of rutile type particles surface-treated with a polar base material is 0.15 to 0.15.
More preferred is a range of 0.35 micron, non-toxic and food grade compatible.
【００１４】本発明において、ポリオレフィン１００重
量％に対し、二酸化チタンが０．１〜１．０重量％配合
された組成物を溶融紡糸して得られるポリオレフィン繊
維からなるトウは、柔軟性に富み、その柔軟性がトウの
捲縮弾性の低減に寄与し、総じてタバコプラグの生産性
を向上させ、また、タバコフィルタの硬度調節にも貢献
する。In the present invention, a tow comprising polyolefin fibers obtained by melt spinning a composition containing 0.1 to 1.0% by weight of titanium dioxide based on 100% by weight of polyolefin has high flexibility, The flexibility contributes to the reduction of the crimp elasticity of the tow, generally improves the productivity of the tobacco plug, and also contributes to the hardness control of the tobacco filter.
【００１５】該二酸化チタンの添加量が０．１重量％未
満では、ポリオレフィンの単糸繊維の柔軟性が不足する
ので、ポリオレフィントウの捲縮弾性が高く、該トウの
均一な開繊が困難となり、タバコプラグの生産性が悪化
する。一方、該添加量が１重量％を超えると溶融紡糸
時、あるいは紡糸して得られた未延伸糸の延伸時に単糸
繊維の切断が生じて、得られるポリオレフィントウは端
切れ繊維を抱き込むことになるので、該トウを使用して
プラグマシンでタバコプラグを製造する際、端切れ繊維
が装置に引っ掛かったり、また、トウの開繊性が悪化し
たりするので、タバコプラグの生産性が極度に悪化す
る。When the amount of the titanium dioxide added is less than 0.1% by weight, the flexibility of the single filament fiber of polyolefin is insufficient, so that the crimp elasticity of the polyolefin tow is high and it becomes difficult to uniformly open the tow. , The productivity of cigarette plugs deteriorates. On the other hand, if the amount added exceeds 1% by weight, single filament fibers are cut during melt spinning or during drawing of undrawn yarn obtained by spinning, and the obtained polyolefin tow encloses the cut fibers. Therefore, when manufacturing a tobacco plug with a tow machine using the tow, the cut fibers are caught in the device, and the openability of the tow is deteriorated, so the productivity of the tobacco plug is extremely deteriorated. To do.
【００１６】本発明に用いる上記ポリオレフィン組成物
には、酸化防止剤および必要に応じて造核剤、滑剤、顔
料、充填剤、各種ポリマー類等が本発明の効果を損なわ
ない範囲で適宜配合されていてもよい。ポリオレフィン
に二酸化チタンおよびその他添加剤を混合する方法とし
ては、通常の押出機、バンバリーミキサー等を用いて溶
融混合し、ペレット状のポリオレフィン組成物を得る方
法を用いることができる。An antioxidant and, if necessary, a nucleating agent, a lubricant, a pigment, a filler, various polymers and the like are appropriately blended in the above-mentioned polyolefin composition used in the present invention within a range that does not impair the effects of the present invention. May be. As a method of mixing titanium dioxide and other additives with the polyolefin, a method of melt-mixing using a conventional extruder, Banbury mixer or the like to obtain a pellet-shaped polyolefin composition can be used.
【００１７】本発明のポリオレフィントウを得る方法
は、上記ポリオレフィン組成物を公知の溶融紡糸法によ
り未延伸糸となした後、公知の延伸法および技術により
適度に延伸、機械捲縮、乾燥等を施して単糸繊維の集束
体でなるポリオレフィントウを得る方法が採用される。
単糸繊維の断面形状としては、Ｙ型、デルタ型、十字型
あるいは真円等から選ぶことができるが、タバコフィル
タの硬度や通気抵抗をバランスよく得るにはデルタ型が
好ましい。The method for obtaining the polyolefin tow of the present invention is such that the above polyolefin composition is made into an undrawn yarn by a known melt spinning method, and then appropriately stretched, mechanically crimped, dried, etc. by a known stretching method and technique. A method of obtaining a polyolefin tow comprising a bundle of single yarn fibers is adopted.
The cross-sectional shape of the single fiber can be selected from Y-type, delta-type, cross-type, perfect circle and the like, but the delta-type is preferable in order to obtain a well-balanced hardness and ventilation resistance of the tobacco filter.
【００１８】本発明のポリオレフィントウの繊度は、単
糸繊維２〜１０デニールの範囲のものが好ましく用いら
れる。本発明におけるポリオレフィントウは、捲縮数２
０〜４５山／ｉｎｃｈ、好ましくは２３〜３６山／ｉｎ
ｃｈを有する。捲縮は、単糸繊維の集束体であるポリオ
レフィントウを適度に挫屈させることにより、単糸繊維
間を交絡して網目状とするものである。本発明において
捲縮数を限定する理由は、タバコフィルタに望ましい硬
度と通気抵抗を与え、かつ生産安定性を良好に保つため
である。特に、捲縮数は、タバコフィルタの硬度を調節
するのに効果的である。捲縮数が２０山／ｉｎｃｈ未満
では、得られるタバコフィルタの硬度が低く、通気抵抗
も小さいので望ましい喫味特性が得られない。一方、捲
縮数が４５山／ｉｎｃｈ超えると、捲縮過度により硬く
なり過ぎて、良好な喫味特性が得られなくなる。また、
捲縮過度による弾性過度を来してオレフィントウの開繊
性が悪化し、プラグマシン上でのポリオレフィントウの
走行性が低下したり、得られるタバコフィルタがプラグ
端面の陥入が激しく、硬度と通気抵抗のバラツキの大き
いものとなるため、生産安定性が低下する。The fineness of the polyolefin tow of the present invention is preferably in the range of 2 to 10 denier single fiber. The polyolefin tow according to the present invention has a crimp number of 2
0-45 mountains / inch, preferably 23-36 mountains / in
have ch. Crimping is a process in which a polyolefin tow, which is a bundle of single yarn fibers, is appropriately buckled to entangle the single yarn fibers to form a mesh. The reason for limiting the number of crimps in the present invention is to provide the tobacco filter with desired hardness and ventilation resistance, and to maintain good production stability. In particular, the number of crimps is effective in controlling the hardness of the cigarette filter. When the number of crimps is less than 20 threads / inch, the obtained tobacco filter has low hardness and low ventilation resistance, so that desired taste characteristics cannot be obtained. On the other hand, when the number of crimps exceeds 45 ridges / inch, the crimps become excessively hard and the taste characteristics cannot be obtained. Also,
The elasticity of the olefin tow is deteriorated due to excessive crimping, the openability of the polyolefin tow is deteriorated, and the tobacco filter obtained has a severe indentation of the plug end face, resulting in hardness and Since the variation in ventilation resistance is large, the production stability is reduced.
【００１９】本発明におけるポリオレフィントウは、Ｊ
ＩＳ Ｌ １０１３に準じ測定した伸度５０〜２５０％
を有する。本発明において伸度を限定する理由は、ポリ
オレフィントウに柔軟性を付与し、捲縮弾性を低減させ
るためである。ポリオレフィントウの伸度が５０％未満
では、該トウの捲縮弾性が高くなるので、タバコプラグ
の生産性が低下する。一方、該伸度が２５０％を超える
と、逆にポリオレフィントウは柔らかくなり過ぎてヘタ
リ易くなり、良好な喫味特性を得るだけのフィルタ硬度
が得られない。The polyolefin tow used in the present invention is J
Elongation measured according to IS L 1013 50-250%
Have. The reason for limiting the elongation in the present invention is to impart flexibility to the polyolefin tow and reduce crimp elasticity. When the elongation of the polyolefin tow is less than 50%, the crimp elasticity of the tow becomes high, so that the productivity of the tobacco plug decreases. On the other hand, when the elongation exceeds 250%, on the contrary, the polyolefin tow becomes too soft and easily set easily, and the filter hardness sufficient to obtain good taste characteristics cannot be obtained.
【００２０】本発明におけるポリオレフィントウは、Ｊ
ＩＳ Ｌ １０１５に準じ測定した捲縮弾性率８０％以
下、好ましくは７６〜６０％を有する。本発明において
捲縮弾性率を限定する理由は、タバコフィルタの生産性
を向上させるためである。捲縮弾性率が８０％を超える
と、ポリオレフィントウをプラグマシンで巻き上げると
き、該トウの均一開繊性が悪くなり、該トウの引き伸ば
しに必要な力も大きくなるので生産性、特に生産速度が
低下したり、プラグ端面の陥入が激しくなるので生産安
定性も低下する。The polyolefin tow used in the present invention is J
It has a crimp elastic modulus of 80% or less, preferably 76 to 60%, measured according to IS L 1015. The reason why the crimp elastic modulus is limited in the present invention is to improve the productivity of the tobacco filter. When the crimping elastic modulus exceeds 80%, when the polyolefin tow is wound up by a plug machine, the uniform opening property of the tow is deteriorated and the force required for stretching the tow is increased, so that the productivity, particularly the production speed is reduced. Or the indentation of the plug end face becomes more severe, resulting in lower production stability.
【００２１】本発明のポリオレフィントウは、主として
タバコフィルタに好ましく用いられるが、該トウは高速
生産性や生産安定性に優れるので、該トウを適度な幅に
開繊後、熱ロールやサクションドライヤー等を通して効
率よく不織布シートとすることも可能であり、粉塵フィ
ルタ、断熱材、マスク、ワイピングクロス、農業用シー
トおよび植物栽培用シート等の用途にも適している。The polyolefin tow of the present invention is preferably used mainly in a tobacco filter, but since the tow is excellent in high-speed productivity and production stability, after opening the tow into an appropriate width, a hot roll, a suction dryer, etc. It is also possible to efficiently make a non-woven sheet through the sheet, and it is also suitable for applications such as a dust filter, a heat insulating material, a mask, a wiping cloth, an agricultural sheet and a plant cultivation sheet.
【００２２】本発明のタバコフィルタは、上記のポリオ
レフィントウを通常のプラグマシンに供給してプラグを
製造し、これを適当な長さにカットすることにより製造
される。The tobacco filter of the present invention is manufactured by supplying the above-described polyolefin tow to a usual plug machine to manufacture a plug, and cutting the plug into an appropriate length.
【００２３】[0023]
【実施例】以下、実施例１〜９および比較例１〜８によ
り本発明をさらに具体的に説明するが、本発明はこれに
限定されるものではない。なお、実施各例および比較各
例の評価は、次の測定方法に準拠して行った。 ・トウ伸度 ：ＪＩＳ Ｌ １０１３に準拠。 ・トウ捲縮弾性率 ：ＪＩＳ Ｌ １０１５に準拠。 ・プラグ巻き上げ速度：１５分以上安定生産が可能な速
度。The present invention will be described in more detail below with reference to Examples 1 to 9 and Comparative Examples 1 to 8, but the present invention is not limited thereto. The evaluation of each Example and Comparative Example was carried out according to the following measuring method. -Toe elongation: According to JIS L 1013. Tow crimp elastic modulus: conforming to JIS L 1015. -Plug hoisting speed: A speed that enables stable production for 15 minutes or more.
【００２４】・プラグ外観 ：プラグ端面の陥
入、巻紙のシワ、切断不良による単糸繊維の引き出し等
の発生度合いを以下の基準によって評価した。 ○ 発生なし △ 陥入、シワが微発生 × 陥入、シワ、単糸繊維の引き出し等の発生が激しい ・プラグ重量 ：１２０mmのタバコプラグ１本の
重量。 ・プラグの通気抵抗 ：１２０mmのタバコプラグに空気
を１７．５ml／秒通したときの抵抗を水柱（mm）で表示
した。External appearance of the plug: The degree of occurrence of indentation of the plug end surface, wrinkling of the wrapping paper, pulling out of the single yarn fiber due to poor cutting, etc. was evaluated according to the following criteria. ○ No occurrence △ Indentations and wrinkles were slightly generated × Intrusions, wrinkles and single yarn fiber withdrawal were severe ・ Plug weight: The weight of one 120 mm tobacco plug. -Ventilation resistance of plug: The resistance when air was passed through a 120 mm cigarette plug at 17.5 ml / sec was expressed by a water column (mm).
【００２５】・プラグの変動指数 ：プラグ通気抵抗の
均一度を以下で表わし、数値が小さいほど均一度がよい
ことを意味する。 標準偏差／平均値×１００ （ｎ＝５０） ・プラグの硬度 ：水平に置いた１２０mmのタバコ
プラグ上に直径１２mmφの円板を介して３００ｇの荷重
を１０秒間かけた場合に生ずるタバコプラグ変形量を
０．１mm単位で読み取った数値をもって見掛けの硬度と
している。該硬度値は大なるほど柔らかく、小さくなる
ほど硬いことを示している。適度な硬度とは、１１以下
を表わす。-Plug variation index: The uniformity of the plug ventilation resistance is expressed below, and the smaller the value, the better the uniformity. Standard deviation / average value × 100 (n = 50) ・ Hardness of plug: Deformation amount of a tobacco plug when a 300 g load is applied for 10 seconds on a 120 mm horizontal tobacco plug through a 12 mmφ disc. The apparent hardness is determined by reading the value in units of 0.1 mm. The larger the hardness value is, the softer it is, and the smaller the hardness value is, the harder it is. The appropriate hardness means 11 or less.
【００２６】実施例および比較例の諸データを表１に示
す。Table 1 shows various data of Examples and Comparative Examples.
【００２７】[0027]
【表１】 [Table 1]
【００２８】実施例１ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．１０重量％、ステアリン酸カルシウム０．１０重量
％、二酸化チタン（東洋インキ社製のＰＰＭＷ−０２−
Ｘ−ＷＨＩＴＥ−ＦＤ：平均粒径０．１５〜０．３５ミ
クロン、ルチル型）０．１重量％を添加し、ヘンシェル
ミキサーで混合した後、押出機を通してＭＦＲ １６の
ペレット状組成物を得た。そして得られた組成物を溶融
紡糸してデルタ型の繊維断面を有する未延伸糸を得、こ
の未延伸糸を延伸して伸度１４０％のポリオレフィント
ウとした。次にクリンパーにより、ポリオレフィントウ
に捲縮数２３〜２７山／ｉｎｃｈの捲縮を付与させた
後、乾燥して、捲縮弾性率が７７．２％を有するフィラ
メント繊度４．６デニール、トータル繊度４０，２５０
デニールのポリオレフィントウを得た。汎用のプラグマ
シンを使用して、該トウを開繊し、巻き上げ、一定の径
の円柱状のトウとして走行させながら３７ｇ／ｍ2 の巻
紙を巻き付けたタバコプラグを製造した。そのときのタ
バコプラグの生産性を、前述の評価項目に準じて測定
し、その結果をプラグ巻き上げ性（速度と外観）として
表１に示した。また、タバコフィルタの性能を、前述の
評価項目に準じて測定し、その結果をプラグ物性（重
量、硬度、通気抵抗、変動指数）として表１に示した。Example 1 0.10% by weight of phenolic antioxidant, 0.10% by weight of calcium stearate, 100% by weight of crystalline propylene homopolymer having an MFR of 16.0 g / 10 min, titanium dioxide (Toyo Ink Co., Ltd.) Made PPMW-02-
X-WHITE-FD: average particle size 0.15 to 0.35 micron, rutile type) 0.1% by weight was added and mixed with a Henschel mixer, and then a pelletized composition of MFR 16 was obtained through an extruder. . Then, the obtained composition was melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and this undrawn yarn was drawn to obtain a polyolefin tow having an elongation of 140%. Next, a crimper is applied to the polyolefin tow with crimps having a crimp number of 23 to 27 threads / inch, and then dried to obtain a filament fineness having a crimp elastic modulus of 77.2% 4.6 denier, total fineness. 40,250
A denier polyolefin tow was obtained. Using a general-purpose plug machine, the tow was opened, rolled up, and a cigarette plug wound with 37 g / m 2 of wrapping paper was produced while running as a cylindrical tow having a constant diameter. The productivity of the tobacco plug at that time was measured according to the above-mentioned evaluation items, and the result is shown in Table 1 as the plug-up property (speed and appearance). Further, the performance of the cigarette filter was measured according to the above-mentioned evaluation items, and the results are shown in Table 1 as plug physical properties (weight, hardness, ventilation resistance, variation index).
【００２９】実施例２ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．１０重量％、ステアリン酸カルシウム０．１０重量
％、二酸化チタン（東洋インキ社製のＰＰＭＷ−０２−
Ｘ−ＷＨＩＴＥ−ＦＤ：平均粒径０．２０〜０．３５ミ
クロン、ルチル型）０．５重量％を添加し、ヘンシェル
ミキサーで混合した後、押出機を通してＭＦＲ １６．
３のペレット状組成物を得た。そして得られた組成物を
溶融紡糸してデルタ型の繊維断面を有する未延伸糸を
得、この未延伸糸を延伸して伸度１４０％のポリオレフ
ィントウとした。次にクリンパーにより、ポリオレフィ
ントウに捲縮数２３〜２７山／ｉｎｃｈの捲縮を付与さ
せた後、乾燥して、捲縮弾性率が７２．１％を有するフ
ィラメント繊度４．６デニール、トータル繊度４０，２
５０デニールのポリオレフィントウを得た。汎用のプラ
グマシンを使用して、該トウを開繊し、巻き上げ、一定
の径の円柱状のトウとして走行させながら３７ｇ／ｍ2
の巻紙を巻き付けたタバコプラグを製造した。得られた
タバコプラグのプラグ巻き上げ性およびプラグ物性を実
施例１に準拠して測定し、その結果を表１に示した。Example 2 0.10% by weight of phenolic antioxidant, 0.10% by weight of calcium stearate, 100% by weight of crystalline propylene homopolymer of 16.0 g / 10 minutes MFR, 10% by weight of titanium dioxide (Toyo Ink Co., Ltd.) Made PPMW-02-
X-WHITE-FD: average particle size 0.20 to 0.35 micron, rutile type) 0.5 wt% was added and mixed with a Henschel mixer, and then passed through an extruder to obtain MFR 16.
A pelletized composition of 3 was obtained. Then, the obtained composition was melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and this undrawn yarn was drawn to obtain a polyolefin tow having an elongation of 140%. Next, the crimps having a crimp number of 23 to 27 threads / inch are crimped to the polyolefin tow with a crimper, and then dried to have a filament crimp modulus of 72.1%, a filament fineness of 4.6 denier, and a total fineness. 40,2
A 50 denier polyolefin tow was obtained. Using a general-purpose plug machine, open the tow, wind it up, and run it as a cylindrical tow with a constant diameter, 37 g / m 2
A cigarette plug wound with a wrapping paper was manufactured. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００３０】実施例３ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．１０重量％、ステアリン酸カルシウム０．１０重量
％、二酸化チタン（東洋インキ社製のＰＰＭＷ−０２−
Ｘ−ＷＨＩＴＥ−ＦＤ：平均粒径０．２０〜０．３５ミ
クロン、ルチル型）１．０重量％を添加し、ヘンシェル
ミキサーで混合した後、押出機を通してＭＦＲ １８．
０のペレット状組成物を得た。そして得られた組成物を
溶融紡糸してデルタ型の繊維断面を有する未延伸糸を
得、この未延伸糸を延伸して伸度１４０％のポリオレフ
ィントウとした。次にクリンパーにより、ポリオレフィ
ントウに捲縮数２３〜２７山／ｉｎｃｈの捲縮を付与さ
せた後、乾燥して、捲縮弾性率が７１．４％を有するフ
ィラメント繊度４．６デニール、トータル繊度４０，２
５０デニールのポリオレフィントウを得た。汎用のプラ
グマシンを使用して、該トウを開繊し、巻き上げ、一定
の径の円柱状のトウとして走行させながら３７ｇ／ｍ2
の巻紙を巻き付けたタバコプラグを製造した。得られた
タバコプラグのプラグ巻き上げ性およびプラグ物性を実
施例１に準拠して測定し、その結果を表１に示した。Example 3 100% by weight of crystalline propylene homopolymer having an MFR of 16.0 g / 10 min, 0.10% by weight of a phenolic antioxidant, 0.10% by weight of calcium stearate, titanium dioxide (Toyo Ink Co., Ltd.) Made PPMW-02-
X-WHITE-FD: average particle size 0.20 to 0.35 micron, rutile type) 1.0 wt% was added and mixed in a Henschel mixer, and then passed through an extruder to obtain MFR 18.
0 pelletized composition was obtained. Then, the obtained composition was melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and this undrawn yarn was drawn to obtain a polyolefin tow having an elongation of 140%. Next, after crimping the polyolefin tow with crimps having a crimp number of 23 to 27 threads / inch with a crimper, the polyolefin tow is dried and has a crimp elastic modulus of 71.4%, a filament fineness of 4.6 denier, and a total fineness. 40,2
A 50 denier polyolefin tow was obtained. Using a general-purpose plug machine, open the tow, wind it up, and run it as a cylindrical tow with a constant diameter, 37 g / m 2
A cigarette plug wound with a wrapping paper was manufactured. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００３１】実施例４ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．２０重量％、ステアリン酸カルシウム０．１０重量
％、二酸化チタン（東洋インキ社製のＰＰＭＷ−０２−
Ｘ−ＷＨＩＴＥ−ＦＤ：平均粒径０．２０〜０．３５ミ
クロン、ルチル型）０．２重量％を添加し、ヘンシェル
ミキサーで混合した後、押出機を通してＭＦＲ １７．
０のペレット状組成物を得た。そして得られた組成物を
溶融紡糸してデルタ型の繊維断面を有する未延伸糸を
得、この未延伸糸を延伸して伸度２３０％のポリオレフ
ィントウとした。次にクリンパーにより、ポリオレフィ
ントウに捲縮数２３〜２７山／ｉｎｃｈの捲縮を付与さ
せた後、乾燥して、捲縮弾性率が６９．２％を有するフ
ィラメント繊度４．６デニール、トータル繊度４０，２
５０デニールのポリオレフィントウを得た。汎用のプラ
グマシンを使用して、該トウを開繊し、巻き上げ、一定
の径の円柱状のトウとして走行させながら３７ｇ／ｍ2
の巻紙を巻き付けたタバコプラグを製造した。得られた
タバコプラグのプラグ巻き上げ性およびプラグ物性を実
施例１に準拠して測定し、その結果を表１に示した。Example 4 100% by weight of crystalline propylene homopolymer having an MFR of 16.0 g / 10 min, 0.20% by weight of a phenolic antioxidant, 0.10% by weight of calcium stearate, titanium dioxide (Toyo Ink Co., Ltd.) Made PPMW-02-
X-WHITE-FD: average particle size 0.20 to 0.35 micron, rutile type) 0.2% by weight was added and mixed with a Henschel mixer, and then passed through an extruder to obtain MFR 17.
0 pelletized composition was obtained. Then, the obtained composition was melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and this undrawn yarn was drawn to obtain a polyolefin tow having an elongation of 230%. Next, after crimping the polyolefin tow with crimps having a crimp number of 23 to 27 threads / inch with a crimper, it is dried and then the filament fineness having a crimp elastic modulus of 69.2% is 4.6 denier, and the total fineness is 40,2
A 50 denier polyolefin tow was obtained. Using a general-purpose plug machine, open the tow, wind it up, and run it as a cylindrical tow with a constant diameter, 37 g / m 2
A cigarette plug wound with a wrapping paper was manufactured. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００３２】実施例５ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．２０重量％、ステアリン酸カルシウム０．１０重量
％、二酸化チタン（東洋インキ社製のＰＰＭＷ−０２−
Ｘ−ＷＨＩＴＥ−ＦＤ：平均粒径０．２０〜０．３５ミ
クロン、ルチル型）０．２重量％を添加し、ヘンシェル
ミキサーで混合した後、押出機を通してＭＦＲ １７．
０のペレット状組成物を得た。そして得られた組成物を
溶融紡糸してデルタ型の繊維断面を有する未延伸糸を
得、この未延伸糸を延伸して伸度１４０％のポリオレフ
ィントウとした。次にクリンパーにより、ポリオレフィ
ントウに捲縮数２３〜２７山／ｉｎｃｈの捲縮を付与さ
せた後、乾燥して、捲縮弾性率が７４．５％を有するフ
ィラメント繊度４．６デニール、トータル繊度４０，２
５０デニールのポリオレフィントウを得た。汎用のプラ
グマシンを使用して、該トウを開繊し、巻き上げ、一定
の径の円柱状のトウとして走行させながら３７ｇ／ｍ2
の巻紙を巻き付けたタバコプラグを製造した。得られた
タバコプラグのプラグ巻き上げ性およびプラグ物性を実
施例１に準拠して測定し、その結果を表１に示した。Example 5 0.20% by weight of phenolic antioxidant, 0.10% by weight of calcium stearate, 100% by weight of crystalline propylene homopolymer having an MFR of 16.0 g / 10 min, titanium dioxide (Toyo Ink Co., Ltd.) Made PPMW-02-
X-WHITE-FD: average particle size 0.20 to 0.35 micron, rutile type) 0.2% by weight was added and mixed with a Henschel mixer, and then passed through an extruder to obtain MFR 17.
0 pelletized composition was obtained. Then, the obtained composition was melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and this undrawn yarn was drawn to obtain a polyolefin tow having an elongation of 140%. Next, after crimping the polyolefin tow with a crimp having a crimp number of 23 to 27 threads / inch by a crimper, it is dried, and the filament fineness having a crimp elastic modulus of 74.5% is 4.6 denier and the total fineness. 40,2
A 50 denier polyolefin tow was obtained. Using a general-purpose plug machine, open the tow, wind it up, and run it as a cylindrical tow with a constant diameter, 37 g / m 2
A cigarette plug wound with a wrapping paper was manufactured. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００３３】実施例６ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．２０重量％、ステアリン酸カルシウム０．１０重量
％、二酸化チタン（東洋インキ社製のＰＰＭＷ−０２−
Ｘ−ＷＨＩＴＥ−ＦＤ：平均粒径０．２０〜０．３５ミ
クロン、ルチル型）０．２重量％を添加し、ヘンシェル
ミキサーで混合した後、押出機を通してＭＦＲ １７．
０のペレット状組成物を得た。そして得られた組成物を
溶融紡糸してデルタ型の繊維断面を有する未延伸糸を
得、この未延伸糸を延伸して伸度６０％のポリオレフィ
ントウとした。次にクリンパーにより、ポリオレフィン
トウに捲縮数２３〜２７山／ｉｎｃｈの捲縮を付与させ
た後、乾燥して、捲縮弾性率が７８．９％を有するフィ
ラメント繊度４．６デニール、トータル繊度４０，２５
０デニールのポリオレフィントウを得た。汎用のプラグ
マシンを使用して、該トウを開繊し、巻き上げ、一定の
径の円柱状のトウとして走行させながら３７ｇ／ｍ2 の
巻紙を巻き付けたタバコプラグを製造した。得られたタ
バコプラグのプラグ巻き上げ性およびプラグ物性を実施
例１に準拠して測定し、その結果を表１に示した。Example 6 Based on 100% by weight of crystalline propylene homopolymer having an MFR of 16.0 g / 10 min, 0.20% by weight of a phenolic antioxidant, 0.10% by weight of calcium stearate, and titanium dioxide (Toyo Ink Co., Ltd.) Made PPMW-02-
X-WHITE-FD: average particle size 0.20 to 0.35 micron, rutile type) 0.2% by weight was added and mixed with a Henschel mixer, and then passed through an extruder to obtain MFR 17.
0 pelletized composition was obtained. Then, the obtained composition was melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and this undrawn yarn was drawn to obtain a polyolefin tow having an elongation of 60%. Next, after crimping the polyolefin tow with crimps having a crimp number of 23 to 27 threads / inch by a crimper, it is dried and then the filament fineness having a crimp elastic modulus of 78.9% is 4.6 denier, and the total fineness is 40, 25
A 0 denier polyolefin tow was obtained. Using a general-purpose plug machine, the tow was opened, rolled up, and a cigarette plug wound with 37 g / m 2 of wrapping paper was produced while running as a cylindrical tow having a constant diameter. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００３４】実施例７ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．１０重量％、ステアリン酸カルシウム０．１０重量
％、二酸化チタン（東洋インキ社製のＰＰＭＷ−０２−
Ｘ−ＷＨＩＴＥ−ＦＤ：平均粒径０．２０〜０．３５ミ
クロン、ルチル型）０．３重量％を添加し、ヘンシェル
ミキサーで混合した後、押出機を通してＭＦＲ １６．
０のペレット状組成物を得た。そして得られた組成物を
溶融紡糸してデルタ型の繊維断面を有する未延伸糸を
得、この未延伸糸を延伸して伸度１４０％のポリオレフ
ィントウとした。次にクリンパーにより、ポリオレフィ
ントウに捲縮数２３〜２７山／ｉｎｃｈの捲縮を付与さ
せた後、乾燥して、捲縮弾性率が７３．２％を有するフ
ィラメント繊度４．６デニール、トータル繊度４０，２
５０デニールのポリオレフィントウを得た。汎用のプラ
グマシンを使用して、該トウを開繊し、巻き上げ、一定
の径の円柱状のトウとして走行させながら３７ｇ／ｍ2
の巻紙を巻き付けたタバコプラグを製造した。得られた
タバコプラグのプラグ巻き上げ性およびプラグ物性を実
施例１に準拠して測定し、その結果を表１に示した。Example 7 0.10% by weight of a phenolic antioxidant, 0.10% by weight of calcium stearate, 100% by weight of a crystalline propylene homopolymer having an MFR of 16.0 g / 10 minutes, titanium dioxide (Toyo Ink Co., Ltd.) Made PPMW-02-
X-WHITE-FD: average particle size 0.20 to 0.35 micron, rutile type) 0.3 wt% was added and mixed with a Henschel mixer, and then passed through an extruder to obtain MFR 16.
0 pelletized composition was obtained. Then, the obtained composition was melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and this undrawn yarn was drawn to obtain a polyolefin tow having an elongation of 140%. Next, after crimping the polyolefin tow with crimps having a crimp number of 23 to 27 threads / inch with a crimper, the polyolefin tow is dried and has a crimp elastic modulus of 73.2%, a filament fineness of 4.6 denier, and a total fineness. 40,2
A 50 denier polyolefin tow was obtained. Using a general-purpose plug machine, open the tow, wind it up, and run it as a cylindrical tow with a constant diameter, 37 g / m 2
A cigarette plug wound with a wrapping paper was manufactured. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００３５】実施例８ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．１０重量％、ステアリン酸カルシウム０．１０重量
％、二酸化チタン（東洋インキ社製のＰＰＭＷ−０２−
Ｘ−ＷＨＩＴＥ−ＦＤ：平均粒径０．２０〜０．３５ミ
クロン、ルチル型）０．３重量％を添加し、ヘンシェル
ミキサーで混合した後、押出機を通してＭＦＲ １６．
０のペレット状組成物を得た。そして得られた組成物を
溶融紡糸してデルタ型の繊維断面を有する未延伸糸を
得、この未延伸糸を延伸して伸度１４０％のポリオレフ
ィントウとした。次にクリンパーにより、ポリオレフィ
ントウに捲縮数３２〜３６山／ｉｎｃｈの捲縮を付与さ
せた後、乾燥して、捲縮弾性率が７５．５％を有するフ
ィラメント繊度４．６デニール、トータル繊度４０，２
５０デニールのポリオレフィントウを得た。汎用のプラ
グマシンを使用して、該トウを開繊し、巻き上げ、一定
の径の円柱状のトウとして走行させながら３７ｇ／ｍ2
の巻紙を巻き付けたタバコプラグを製造した。得られた
タバコプラグのプラグ巻き上げ性およびプラグ物性を実
施例１に準拠して測定し、その結果を表１に示した。Example 8 0.10% by weight of phenolic antioxidant, 0.10% by weight of calcium stearate, 100% by weight of crystalline propylene homopolymer having an MFR of 16.0 g / 10 min, titanium dioxide (Toyo Ink Co., Ltd.) Made PPMW-02-
X-WHITE-FD: average particle size 0.20 to 0.35 micron, rutile type) 0.3 wt% was added and mixed with a Henschel mixer, and then passed through an extruder to obtain MFR 16.
0 pelletized composition was obtained. Then, the obtained composition was melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and this undrawn yarn was drawn to obtain a polyolefin tow having an elongation of 140%. Then, the polyolefin tow is crimped with a crimp number of 32 to 36 ridges / inch by a crimper, and then dried to obtain a filament fineness having a crimp elastic modulus of 75.5% 4.6 denier, total fineness. 40,2
A 50 denier polyolefin tow was obtained. Using a general-purpose plug machine, open the tow, wind it up, and run it as a cylindrical tow with a constant diameter, 37 g / m 2
A cigarette plug wound with a wrapping paper was manufactured. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００３６】実施例９ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．１０重量％、ステアリン酸カルシウム０．１０重量
％、二酸化チタン（東洋インキ社製のＰＰＭＷ−０２−
Ｘ−ＷＨＩＴＥ−ＦＤ：平均粒径０．２０〜０．３５ミ
クロン、ルチル型）０．３重量％を添加し、ヘンシェル
ミキサーで混合した後、押出機を通してＭＦＲ １６．
０のペレット状組成物を得た。そして得られた組成物を
溶融紡糸してデルタ型の繊維断面を有する未延伸糸を
得、この未延伸糸を延伸して伸度１４０％のポリオレフ
ィントウとした。次にクリンパーにより、ポリオレフィ
ントウに捲縮数４０〜４４山／ｉｎｃｈの捲縮を付与さ
せた後、乾燥して、捲縮弾性率が７８．６％を有するフ
ィラメント繊度４．６デニール、トータル繊度４０，２
５０デニールのポリオレフィントウを得た。汎用のプラ
グマシンを使用して、該トウを開繊し、巻き上げ、一定
の径の円柱状のトウとして走行させながら３７ｇ／ｍ2
の巻紙を巻き付けたタバコプラグを製造した。得られた
タバコプラグのプラグ巻き上げ性およびプラグ物性を実
施例１に準拠して測定し、その結果を表１に示した。Example 9 0.10% by weight of phenolic antioxidant, 0.10% by weight of calcium stearate, 100% by weight of crystalline propylene homopolymer having an MFR of 16.0 g / 10 min, titanium dioxide (Toyo Ink Co., Ltd.) Made PPMW-02-
X-WHITE-FD: average particle size 0.20 to 0.35 micron, rutile type) 0.3 wt% was added and mixed with a Henschel mixer, and then passed through an extruder to obtain MFR 16.
0 pelletized composition was obtained. Then, the obtained composition was melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and this undrawn yarn was drawn to obtain a polyolefin tow having an elongation of 140%. Next, the crimps having a crimp number of 40 to 44 threads / inch are crimped to the polyolefin tow with a crimper, and then dried to obtain a filament fineness having a crimp elastic modulus of 78.6% 4.6 denier and a total fineness. 40,2
A 50 denier polyolefin tow was obtained. Using a general-purpose plug machine, open the tow, wind it up, and run it as a cylindrical tow with a constant diameter, 37 g / m 2
A cigarette plug wound with a wrapping paper was manufactured. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００３７】比較例１ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．１０重量％、ステアリン酸カルシウム０．１０重量
％を添加し、ヘンシェルミキサーで混合した後、押出機
を通してＭＦＲ１６．０のペレット状組成物を得た。そ
して得られた組成物を溶融紡糸してデルタ型の繊維断面
を有する未延伸糸を得、この未延伸糸を延伸して伸度１
４０％のポリオレフィントウとした。次にクリンパーに
より、ポリオレフィントウに捲縮数２３〜２７山／ｉｎ
ｃｈの捲縮を付与させた後、乾燥して、捲縮弾性率が８
５．２％を有するフィラメント繊度４．６デニール、ト
ータル繊度４０，２５０デニールのポリオレフィントウ
を得た。汎用のプラグマシンを使用して、該トウを開繊
し、巻き上げ、一定の径の円柱状のトウとして走行させ
ながら３７ｇ／ｍ2の巻紙を巻き付けたタバコプラグを
製造した。得られたタバコプラグのプラグ巻き上げ性お
よびプラグ物性を実施例１に準拠して測定し、その結果
を表１に示した。Comparative Example 1 0.10% by weight of a phenolic antioxidant and 0.10% by weight of calcium stearate were added to 100% by weight of a crystalline propylene homopolymer having an MFR of 16.0 g / 10 minutes, and the mixture was mixed with a Henschel mixer. After mixing, a pelletized composition with MFR 16.0 was obtained through the extruder. Then, the obtained composition is melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and the undrawn yarn is drawn to have an elongation of 1
40% polyolefin tow. Next, crimp 23 to 27 threads / in on the polyolefin tow with a crimper.
After the crimp of ch is applied, the crimp elastic modulus is 8 after drying.
A polyolefin tow having a filament fineness of 5.2% and a total fineness of 40,250 denier was obtained. Using a general-purpose plug machine, the tow was opened, rolled up, and a cigarette plug wound with 37 g / m 2 of wrapping paper was produced while running as a cylindrical tow having a constant diameter. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００３８】比較例２ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．１０重量％、ステアリン酸カルシウム０．１０重量
％を添加し、ヘンシェルミキサーで混合した後、押出機
を通してＭＦＲ１６．０のペレット状組成物を得た。そ
して得られた組成物を溶融紡糸してデルタ型の繊維断面
を有する未延伸糸を得、この未延伸糸を延伸して伸度２
３０％のポリオレフィントウとした。次にクリンパーに
より、ポリオレフィントウに捲縮数２３〜２７山／ｉｎ
ｃｈの捲縮を付与させた後、乾燥して、捲縮弾性率が８
２．２％を有するフィラメント繊度４．６デニール、ト
ータル繊度４０，２５０デニールのポリオレフィントウ
を得た。汎用のプラグマシンを使用して、該トウを開繊
し、巻き上げ、一定の径の円柱状のトウとして走行させ
ながら３７ｇ／ｍ2の巻紙を巻き付けたタバコプラグを
製造した。得られたタバコプラグのプラグ巻き上げ性お
よびプラグ物性を実施例１に準拠して測定し、その結果
を表１に示した。Comparative Example 2 0.10% by weight of a phenolic antioxidant and 0.10% by weight of calcium stearate were added to 100% by weight of a crystalline propylene homopolymer having an MFR of 16.0 g / 10 minutes, and the mixture was mixed with a Henschel mixer. After mixing, a pelletized composition with MFR 16.0 was obtained through the extruder. Then, the obtained composition is melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and the undrawn yarn is drawn to have an elongation of 2
30% polyolefin tow. Next, crimp 23 to 27 threads / in on the polyolefin tow with a crimper.
After the crimp of ch is applied, the crimp elastic modulus is 8 after drying.
A polyolefin tow having a filament fineness of 2.2% and a total fineness of 40,250 denier was obtained. Using a general-purpose plug machine, the tow was opened, rolled up, and a cigarette plug wound with 37 g / m 2 of wrapping paper was produced while running as a cylindrical tow having a constant diameter. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００３９】比較例３ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．１０重量％、ステアリン酸カルシウム０．１０重量
％、二酸化チタン（東洋インキ社製のＰＰＭＷ−０２−
Ｘ−ＷＨＩＴＥ−ＦＤ：平均粒径０．２０〜０．３５ミ
クロン、ルチル型）１．２重量％を添加し、ヘンシェル
ミキサーで混合した後、押出機を通してＭＦＲ ２０．
０のペレット状組成物を得た。そして得られた組成物を
溶融紡糸してデルタ型の繊維断面を有する未延伸糸を
得、この未延伸糸を延伸して伸度１４０％のポリオレフ
ィントウとした。次にクリンパーにより、ポリオレフィ
ントウに捲縮数２３〜２７山／ｉｎｃｈの捲縮を付与さ
せた後、乾燥して、捲縮弾性率が７０．１％を有するフ
ィラメント繊度４．６デニール、トータル繊度４０，２
５０デニールのポリオレフィントウを得た。汎用のプラ
グマシンを使用して、該トウを開繊し、巻き上げ、一定
の径の円柱状のトウとして走行させながら３７ｇ／ｍ2
の巻紙を巻き付けたタバコプラグを製造した。得られた
タバコプラグのプラグ巻き上げ性およびプラグ物性を実
施例１に準拠して測定し、その結果を表１に示した。Comparative Example 3 0.10% by weight of phenolic antioxidant, 0.10% by weight of calcium stearate, titanium dioxide (Toyo Ink Co., Ltd.) per 100% by weight of crystalline propylene homopolymer having an MFR of 16.0 g / 10 min. Made PPMW-02-
X-WHITE-FD: average particle size 0.20 to 0.35 micron, rutile type) 1.2 wt% was added and mixed with a Henschel mixer, and then passed through an extruder to obtain MFR 20.
0 pelletized composition was obtained. Then, the obtained composition was melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and this undrawn yarn was drawn to obtain a polyolefin tow having an elongation of 140%. Next, after crimping the polyolefin tow with crimps having a crimp number of 23 to 27 threads / inch by a crimper, it is dried and then the filament fineness having a crimp elastic modulus of 70.1% 4.6 denier, total fineness 40,2
A 50 denier polyolefin tow was obtained. Using a general-purpose plug machine, open the tow, wind it up, and run it as a cylindrical tow with a constant diameter, 37 g / m 2
A cigarette plug wound with a wrapping paper was manufactured. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００４０】比較例４ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．１０重量％、ステアリン酸カルシウム０．１０重量
％、二酸化チタン（東洋インキ社製のＰＰＭＷ−０２−
Ｘ−ＷＨＩＴＥ−ＦＤ：平均粒径０．２０〜０．３５ミ
クロン、ルチル型）１．２重量％を添加し、ヘンシェル
ミキサーで混合した後、押出機を通してＭＦＲ ２０．
０のペレット状組成物を得た。そして得られた組成物を
溶融紡糸してデルタ型の繊維断面を有する未延伸糸を
得、この未延伸糸を延伸して伸度１４０％のポリオレフ
ィントウとした。次にクリンパーにより、ポリオレフィ
ントウに捲縮数３２〜３６山／ｉｎｃｈの捲縮を付与さ
せた後、乾燥して、捲縮弾性率が７３．３％を有するフ
ィラメント繊度４．６デニール、トータル繊度４０，２
５０デニールのポリオレフィントウを得た。汎用のプラ
グマシンを使用して、該トウを開繊し、巻き上げ、一定
の径の円柱状のトウとして走行させながら３７ｇ／ｍ2
の巻紙を巻き付けたタバコプラグを製造した。得られた
タバコプラグのプラグ巻き上げ性およびプラグ物性を実
施例１に準拠して測定し、その結果を表１に示した。Comparative Example 4 0.10% by weight of phenolic antioxidant, 0.10% by weight of calcium stearate, 100% by weight of crystalline propylene homopolymer having an MFR of 16.0 g / 10 min, titanium dioxide (Toyo Ink Co., Ltd.) Made PPMW-02-
X-WHITE-FD: average particle size 0.20 to 0.35 micron, rutile type) 1.2 wt% was added and mixed with a Henschel mixer, and then passed through an extruder to obtain MFR 20.
0 pelletized composition was obtained. Then, the obtained composition was melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and this undrawn yarn was drawn to obtain a polyolefin tow having an elongation of 140%. Next, after crimping the polyolefin tow with a crimp having a crimp number of 32 to 36 peaks / inch by a crimper, it is dried and then the filament fineness having a crimp elastic modulus of 73.3% is 4.6 denier, and the total fineness is 40,2
A 50 denier polyolefin tow was obtained. Using a general-purpose plug machine, open the tow, wind it up, and run it as a cylindrical tow with a constant diameter, 37 g / m 2
A cigarette plug wound with a wrapping paper was manufactured. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００４１】比較例５ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．２０重量％、ステアリン酸カルシウム０．１０重量
％、二酸化チタン（東洋インキ社製のＰＰＭＷ−０２−
Ｘ−ＷＨＩＴＥ−ＦＤ：平均粒径０．２０〜０．３５ミ
クロン、ルチル型）０．２重量％を添加し、ヘンシェル
ミキサーで混合した後、押出機を通してＭＦＲ １７．
０のペレット状組成物を得た。そして得られた組成物を
溶融紡糸してデルタ型の繊維断面を有する未延伸糸を
得、この未延伸糸を延伸して伸度３０％のポリオレフィ
ントウとした。次にクリンパーにより、ポリオレフィン
トウに捲縮数２３〜２７山／ｉｎｃｈの捲縮を付与させ
た後、乾燥して、捲縮弾性率が８８．１％を有するフィ
ラメント繊度４．６デニール、トータル繊度４０，２５
０デニールのポリオレフィントウを得た。汎用のプラグ
マシンを使用して、該トウを開繊し、巻き上げ、一定の
径の円柱状のトウとして走行させながら３７ｇ／ｍ2 の
巻紙を巻き付けたタバコプラグを製造した。得られたタ
バコプラグのプラグ巻き上げ性およびプラグ物性を実施
例１に準拠して測定し、その結果を表１に示した。Comparative Example 5 0.20% by weight of a phenolic antioxidant, 0.10% by weight of calcium stearate, 100% by weight of a crystalline propylene homopolymer having an MFR of 16.0 g / 10 min, titanium dioxide (Toyo Ink Co., Ltd.) Made PPMW-02-
X-WHITE-FD: average particle size 0.20 to 0.35 micron, rutile type) 0.2% by weight was added and mixed with a Henschel mixer, and then passed through an extruder to obtain MFR 17.
0 pelletized composition was obtained. Then, the obtained composition was melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and this undrawn yarn was drawn to obtain a polyolefin tow having an elongation of 30%. Then, the polyolefin tow is crimped with a crimp having a crimp number of 23 to 27 threads / inch by a crimper, and then dried to obtain a filament fineness having a crimp elastic modulus of 88.1% 4.6 denier and a total fineness. 40, 25
A 0 denier polyolefin tow was obtained. Using a general-purpose plug machine, the tow was opened, rolled up, and a cigarette plug wound with 37 g / m 2 of wrapping paper was produced while running as a cylindrical tow having a constant diameter. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００４２】比較例６ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．２０重量％、ステアリン酸カルシウム０．１０重量
％、二酸化チタン（東洋インキ社製のＰＰＭＷ−０２−
Ｘ−ＷＨＩＴＥ−ＦＤ：平均粒径０．２０〜０．３５ミ
クロン、ルチル型）０．２重量％を添加し、ヘンシェル
ミキサーで混合した後、押出機を通してＭＦＲ １７．
０のペレット状組成物を得た。そして得られた組成物を
溶融紡糸してデルタ型の繊維断面を有する未延伸糸を
得、この未延伸糸を延伸して伸度３００％のポリオレフ
ィントウとした。次にクリンパーにより、ポリオレフィ
ントウに捲縮数２３〜２７山／ｉｎｃｈの捲縮を付与さ
せた後、乾燥して、捲縮弾性率が６８．０％を有するフ
ィラメント繊度４．６デニール、トータル繊度４０，２
５０デニールのポリオレフィントウを得た。汎用のプラ
グマシンを使用して、該トウを開繊し、巻き上げ、一定
の径の円柱状のトウとして走行させながら３７ｇ／ｍ2
の巻紙を巻き付けたタバコプラグを製造した。得られた
タバコプラグのプラグ巻き上げ性およびプラグ物性を実
施例１に準拠して測定し、その結果を表１に示した。Comparative Example 6 Based on 100% by weight of crystalline propylene homopolymer having an MFR of 16.0 g / 10 min, 0.20% by weight of a phenolic antioxidant, 0.10% by weight of calcium stearate, and titanium dioxide (Toyo Ink Co., Ltd.) Made PPMW-02-
X-WHITE-FD: average particle size 0.20 to 0.35 micron, rutile type) 0.2% by weight was added and mixed with a Henschel mixer, and then passed through an extruder to obtain MFR 17.
0 pelletized composition was obtained. Then, the obtained composition was melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and this undrawn yarn was drawn to obtain a polyolefin tow having an elongation of 300%. Next, after crimping the polyolefin tow with crimps having a crimp number of 23 to 27 threads / inch by a crimper, it is dried and then the filament fineness having a crimp elastic modulus of 68.0% is 4.6 denier, and the total fineness is 40,2
A 50 denier polyolefin tow was obtained. Using a general-purpose plug machine, open the tow, wind it up, and run it as a cylindrical tow with a constant diameter, 37 g / m 2
A cigarette plug wound with a wrapping paper was manufactured. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００４３】比較例７ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．１０重量％、ステアリン酸カルシウム０．１０重量
％、二酸化チタン（東洋インキ社製のＰＰＭＷ−０２−
Ｘ−ＷＨＩＴＥ−ＦＤ：平均粒径０．２０〜０．３５ミ
クロン、ルチル型）０．３重量％を添加し、ヘンシェル
ミキサーで混合した後、押出機を通してＭＦＲ １６．
０のペレット状組成物を得た。そして得られた組成物を
溶融紡糸してデルタ型の繊維断面を有する未延伸糸を
得、この未延伸糸を延伸して伸度１４０％のポリオレフ
ィントウとした。次にクリンパーにより、ポリオレフィ
ントウに捲縮数１４〜１８山／ｉｎｃｈの捲縮を付与さ
せた後、乾燥して、捲縮弾性率が７２．２％を有するフ
ィラメント繊度４．６デニール、トータル繊度４０，２
５０デニールのポリオレフィントウを得た。汎用のプラ
グマシンを使用して、該トウを開繊し、巻き上げ、一定
の径の円柱状のトウとして走行させながら３７ｇ／ｍ2
の巻紙を巻き付けたタバコプラグを製造した。得られた
タバコプラグのプラグ巻き上げ性およびプラグ物性を実
施例１に準拠して測定し、その結果を表１に示した。Comparative Example 7 0.10% by weight of phenolic antioxidant, 0.10% by weight of calcium stearate, 100% by weight of crystalline propylene homopolymer having an MFR of 16.0 g / 10 min, titanium dioxide (Toyo Ink Co., Ltd.) Made PPMW-02-
X-WHITE-FD: average particle size 0.20 to 0.35 micron, rutile type) 0.3 wt% was added and mixed with a Henschel mixer, and then passed through an extruder to obtain MFR 16.
0 pelletized composition was obtained. Then, the obtained composition was melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and this undrawn yarn was drawn to obtain a polyolefin tow having an elongation of 140%. Next, after crimping the polyolefin tow with crimps having a crimp number of 14 to 18 peaks / inch with a crimper, it is dried and then the filament fineness having a crimp elastic modulus of 72.2% is 4.6 denier and the total fineness. 40,2
A 50 denier polyolefin tow was obtained. Using a general-purpose plug machine, open the tow, wind it up, and run it as a cylindrical tow with a constant diameter, 37 g / m 2
A cigarette plug wound with a wrapping paper was manufactured. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００４４】比較例８ ＭＦＲ １６．０ｇ／１０分の結晶性プロピレンホモポ
リマー１００重量％に対し、フェノール系酸化防止剤
０．１０重量％、ステアリン酸カルシウム０．１０重量
％、二酸化チタン（東洋インキ社製のＰＰＭＷ−０２−
Ｘ−ＷＨＩＴＥ−ＦＤ：平均粒径０．２０〜０．３５ミ
クロン、ルチル型）０．３重量％を添加し、ヘンシェル
ミキサーで混合した後、押出機を通してＭＦＲ １６．
０のペレット状組成物を得た。そして得られた組成物を
溶融紡糸してデルタ型の繊維断面を有する未延伸糸を
得、この未延伸糸を延伸して伸度１４０％のポリオレフ
ィントウとした。次にクリンパーにより、ポリオレフィ
ントウに捲縮数４８〜５２山／ｉｎｃｈの捲縮を付与さ
せた後、乾燥して、捲縮弾性率が８６．０％を有するフ
ィラメント繊度４．６デニール、トータル繊度４０，２
５０デニールのポリオレフィントウを得た。汎用のプラ
グマシンを使用して、該トウを開繊し、巻き上げ、一定
の径の円柱状のトウとして走行させながら３７ｇ／ｍ2
の巻紙を巻き付けたタバコプラグを製造した。得られた
タバコプラグのプラグ巻き上げ性およびプラグ物性を実
施例１に準拠して測定し、その結果を表１に示した。Comparative Example 8 0.10% by weight of a phenolic antioxidant, 0.10% by weight of calcium stearate, 100% by weight of a crystalline propylene homopolymer having an MFR of 16.0 g / 10 min, titanium dioxide (Toyo Ink Co., Ltd.) Made PPMW-02-
X-WHITE-FD: average particle size 0.20 to 0.35 micron, rutile type) 0.3 wt% was added and mixed with a Henschel mixer, and then passed through an extruder to obtain MFR 16.
0 pelletized composition was obtained. Then, the obtained composition was melt-spun to obtain an undrawn yarn having a delta type fiber cross section, and this undrawn yarn was drawn to obtain a polyolefin tow having an elongation of 140%. Next, after crimping the polyolefin tow with a crimp having a crimp number of 48 to 52 threads / inch by a crimper, it is dried and then the filament fineness having a crimp elastic modulus of 86.0% is 4.6 denier, and the total fineness is 40,2
A 50 denier polyolefin tow was obtained. Using a general-purpose plug machine, open the tow, wind it up, and run it as a cylindrical tow with a constant diameter, 37 g / m 2
A cigarette plug wound with a wrapping paper was manufactured. The plug-up property and plug physical properties of the obtained tobacco plug were measured according to Example 1, and the results are shown in Table 1.
【００４５】上記実施例の結果からわかるように、特定
のポリオレフィン組成物を用いて溶融紡糸したポリオレ
フィン繊維を集束し、特定の捲縮数、特定の伸度および
捲縮弾性率を与えることにより得られるポリオレフィン
トウは、該トウを使用してタバコプラグを製造する際、
高速生産が可能となる。また、該トウを用いることによ
り、喫味特性がきわめて良好である適度な硬度と通気抵
抗を有するタバコフィルタが得られる。As can be seen from the results of the above-mentioned examples, melt-spun polyolefin fibers were bundled with a specific polyolefin composition to obtain a specific crimp number, specific elongation and crimp elastic modulus. The polyolefin tow to be used, when manufacturing a tobacco plug using the tow,
High-speed production is possible. Further, by using the tow, a tobacco filter having an appropriate hardness and a ventilation resistance with extremely good taste characteristics can be obtained.
【００４６】一方比較例に示すごとく、本発明の請求範
囲外のポリオレフィントウを用いると、タバコプラグの
高速生産性が低下し、さらにはタバコフィルタとしての
適度な硬度と通気抵抗も得られなくなる。On the other hand, as shown in the comparative example, when the polyolefin tow outside the scope of the present invention is used, the high-speed productivity of the tobacco plug is lowered, and further, suitable hardness and ventilation resistance as a tobacco filter cannot be obtained.
【００４７】[0047]
【発明の効果】本発明のポリオレフィントウは、例えば
汎用のプラグマシンを使用して、タバコプラグを製造す
る際、アセテートトウ並みの高速生産が可能になり、経
済的にきわめて有利である。また、該トウを用いたタバ
コフィルタは、適度な硬度と通気抵抗を有しているの
で、アセテートトウとは異なる良好な喫味特性を楽しむ
ことができる。INDUSTRIAL APPLICABILITY The polyolefin tow of the present invention is economically advantageous because it enables high-speed production comparable to acetate tow when producing a tobacco plug using a general-purpose plug machine. Further, since the tobacco filter using the tow has appropriate hardness and ventilation resistance, it is possible to enjoy good taste characteristics different from those of the acetate tow.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 伊東 秀実 滋賀県守山市立入町251 淡海寮 (72)発明者 森川 義雄 福岡県田川市大字夏吉字竹見エズ467番地 の１ 九州フィルター工業株式会社内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Hidemi Ito, 251 Irumicho, Moriyama City, Shiga Prefecture Tamami Dormitory (72) Yoshio Morikawa, No. 4 Takemi Ez, Natsumiji, Tagawa City, Fukuoka Prefecture Kyushu Filter Industry Co., Ltd.
Claims (2)
酸化チタンが０．１〜１．０重量％配合された組成物を
溶融紡糸して得られるポリオレフィン繊維からなるトウ
であって、該トウは、捲縮数が２０〜４５山／ｉｎｃ
ｈ、伸度が５０〜２５０％、捲縮弾性率が８０％以下で
あることを特徴とするポリオレフィントウ。1. A tow comprising polyolefin fibers obtained by melt-spinning a composition containing 0.1 to 1.0% by weight of titanium dioxide with respect to 100% by weight of polyolefin, the tow comprising: Reduced number is 20 to 45 mountains / inc
h, an elongation of 50 to 250%, and a crimp elastic modulus of 80% or less, a polyolefin tow.
素材とするタバコフィルタ。2. A tobacco filter made of the polyolefin tow according to claim 1.